In high-voltage insulation systems, the most commonly used material is polymeric material because of its high dielectric strength, high resistivity, and low dielectric loss in addition to good chemical and mechanical properties. In this work, various polymer compounds were prepared, consisting of low-density polyethylene (LDPE), high-density polyethylene (HDPE), polypropylene (PP), HDPE/PP, and LDPE/PP polymer blends. The relative permittivity and breakdown strength of each sample types were evaluated. In order to determine the physical properties of the prepared samples, the samples were also characterized using differential scanning calorimetry (DSC). The results showed that the dielectric constant of PP increased with the increase of HDPE and LDPE content. The breakdown measurement data for all samples were analyzed using the cumulative probability plot of Weibull distribution. From the acquired results, it was found that the dielectric strengths of LDPE and HDPE were higher than that of PP. Consequently, the addition of LDPE and HDPE to PP increased the breakdown strength of PP, but a variation in the weight ratio (30%, 50% and 70%) did not change significantly the breakdown strength. The DSC measurements showed two exothermic crystallization peaks representing two crystalline phases. In addition, the DSC results showed that the blended samples were physically bonded, and no co-crystallization occurred in the produced blends.

In zinc oxide (ZnO) surge arresters, leakage current usually flows across the arrester under normal operating condition. Leakage current is one of the factors which contribute towards degradation of surge arresters and therefore, it is very important to monitor the condition of surge arrester. In this work, the behaviour of leakage current in a ZnO surge arrester during normal operation, under different voltage amplitudes, wetness and pollution conditions was analysed. An 11 kV surge arrester model in three-dimensional space was subjected to finite element analysis (FEA) to determine the leakage current under different conditions. The results from the FEA model were compared with the measurement results to validate the model that has been developed. From comparison between the measurement and simulation results, physical parameters of a surge arrester that influence the leakage current under different conditions of the surge arrester were identified from the model. Through this work, a better understanding of leakage current behaviour can be attained, which may help in condition monitoring analysis on surge arrester in electrical utilities.

This study provides a thorough investigation of partial discharge (PD) activities in nanofluid insulation material consisting of different types of nanoparticles, which are conductive and semiconductive when subjected to high voltage stress is presented. Nanofluids have become a topic of interest because they can be an alternative to liquid insulation in electrical apparatus due to their promising dielectric strength and cooling ability. However, during in-service operation, PDs can occur between conductors in the insulation system. Therefore, this study presents the behavior of PDs within nanofluid dielectric materials consisting of conductive and semiconductive nanoparticles. The results show that there is an improvement in the PD resistance and a reduction in the tan delta of nanofluids at power frequency after the incorporation of conductive or semiconductive nanoparticles in the nanofluid oil. However, the most suitable concentration of conductive and semiconductive nanoparticles in the base fluid was found to be, respectively, 0.01 g/L and 1.0 g/L at PD inception and PD steady-state conditions. The clustering of nanoparticles in a nanofluid suspension due to PD activities is also discussed in this study.