Zinc chromite (ZnCr₂O₄) has been synthesized by the thermolysis of a new Zn(II)-Cr(III) oxalate coordination compound, namely [Cr₂Zn(C₂O₄)₄(OH₂)₆]·4H₂O. The coordination compound has been characterized by chemical analysis, infrared spectroscopy (IR), and thermal analysis. The zinc chromite obtained after a heating treatment of the coordination compound at 450 °C for 1 h has been investigated by XRD, FE-SEM, TEM/HR-TEM coupled with selected area electron diffraction (SAED) measurements. The photocatalytic performance of nanosized zinc chromite was assessed for the degradation and mineralization of humic acid (HA) from a drinking water source, envisaging the development of the advanced oxidation process for drinking water treatment technology. A mineralization efficiency of 60% was achieved after 180 min of 50 mg L⁻¹ HA photocatalysis using zinc chromite under UV irradiation, in comparison with 7% efficiency reached by photolysis.

The concept of academic spin-off (AS) has witnessed an increase in attention due to its effectiveness in solving industry problems using core technology and knowledge from academia. Most studies based on US and western Europe experiences have presented the main key factors for academic spin-offs. The present study aims to address a literature gap regarding AS survival factor identification for central and eastern European countries, to relate resource groups with these key factors from a literature perspective, and to statistically investigate the long-term performance of academic spin-offs in Romania, an eastern European country that has only recently understood the opportunity academic spin-offs offer for national and regional development. Since EU programs are setting the scene for AS development, this research brings new insights for university strategic management to achieve sustainable regional growth by proposing a novelty spin-off key factor specific to central and eastern European countries: team competency in accessing government funds. Since these emerging economies face similar challenges regarding AS formation and development, statistical evidence from Romania is insightful and valuable. Data were collected on Romanian AS companies founded from 2006–2010, and eleven survival factors were investigated within a quantitative survey to understand which had a significant impact on AS performance. By using Pearson’s correlation matrix and a Cobb–Douglas nonlinear regression model, this study validated two research hypotheses that, in Romania, the quality of scientific support received from a university or research center during the development of a product and the competency of a team in accessing government funds were the most important factors having nonlinear influences on AS performance. Their positive and negative influences were furthermore discussed, and managerial implications were outlined.

As water is essential to life and is an indispensable resource for ecosystems and their services and for nearly all human activities, the goal of this research was to evaluate the surface water quality of the Danube as it passes through the Romania–Serbia border in the nature reservations Djerdap and Iron Gate. The study aimed to assess the oxygen regime, nutrients and heavy metals contamination of the surface waters of the Danube on a length of about 240 km, between Bazias and Iron Gate II. Reference sampling and analytical methods (UV-VIS and AAS) were deployed to reach this goal. In addition, sediments were analyzed through back scattered SEM-EDAX for the elemental analysis of the sediment surface. Results obtained show a low environmental impact of heavy metals, while the Danube’s oxygen regime is under stress due to nutrients’ (nitrites and orthophosphates) significant concentration in the Danube surface water in the analyzed sector. Our approach can be applied to other water bodies in the area, to increase available scientific data together with societal awareness of the Danube’s environmental risks.

3D-printed materials are present in numerous applications, from medicine to engineering. The aim of this study is to assess their suitability for an application of interest today, that of testing of 3D-printed polylactic acid (PLA)-based reactors for biogas production using anaerobic digestion. The impact of temperature, pH, and aqueous phase on the tested bioreactor is investigated, together with the effect of the gaseous phase (i.e., produced biogas). Two batches of materials used separately, one after another inside the bioreactor were considered, in a realistic situation. Two essential parameters inside the reactor (i.e., pH and temperature) were continuously monitored during a time interval of 25 to 30 days for each of the two biogas-generating processes. To understand the impact of these processes on the walls of the bioreactor, samples of 3D-printed material were placed at three levels: at the top (i.e., outside the substrate), in the middle, and at the bottom of the bioreactor. The samples were analyzed using a non-destructive imaging method, Optical Coherence Tomography (OCT). An in-house developed swept-source (SS) OCT system, master–slave (MS) enhanced, operating at a central wavelength of 1310 nm was utilized. The 3D OCT images related to the degradation level of the material of the PLA samples were validated using Scanning Electron Microscopy (SEM). The differences between the impact of the substrate on samples situated at the three considered levels inside the reactor were determined and analyzed using their OCT B-scans (optical cross-section images). Thus, the impact of the biogas-generating process on the interior of the bioreactor was demonstrated and quantified, as well as the capability of OCT to perform such assessments. Therefore, future work may target OCT for in situ investigations of such bioreactors.

The alumina, in the form of α-Al₂O₃ tabular balls, considered in this study is a high-purity form of aluminum oxide that has been fired at high temperatures (well above 1900 °C), virtually removing porosity. However, the purity and inertness of the surface of the Al₂O₃ tabular balls minimize the catalytic activity, which is why lithium doping was tried. Thus, the target of this study was the effect of doping with lithium ions in some tabular balls of Al₂O₃ (the crystalline structure is corundum) on the improvement of the catalytic properties of alumina. This study examined the impact of a lithium catalyst on the combustion of various fuels within a porous inert medium (PIM) burner. This study specifically compared low calorific gaseous fuel (e.g., biogas) combustion in a PIM burner with and without the lithium catalyst. The experimental setup comprised a gas preparation unit for mixing CNG and CO₂ to simulate biogas and a PIM burner. The PIM burner comprised Al₂O₃ spheres (13 mm diameter, 45% porosity) in a random packing configuration. Three fuels, varying in composition and lower heating value (LHV ranging from 20.771 to 27.695 MJ/m³), were combusted at air ratios ranging from 1.67 to 1.79. The results indicated that the catalyst increased peak combustion temperatures by 23.2 °C to 51.4 °C, depending on the fuel type and air ratio. Significantly higher carbon monoxide (CO) concentrations were observed without the catalyst, particularly with fuel type F1, while nitrous oxide (NOx) levels remained consistently low. Upstream flame propagation was observed in the presence of the catalyst. These findings demonstrate the potential of lithium catalysts to enhance combustion stability and reduce emissions in porous media combustion burners. Following these studies, it can be stated that Li(I) has the role of promoter of the catalytic process.