Coating systems used for anticorrosion protection usually consist of a primer, intermediate layers, and topcoats. Zinc-rich primers, which serve as cathodic and barrier protection, are widely used for the corrosion protection of steel structures. Due to the fact that the functioning of the above-mentioned coatings is related to the conduction of galvanic current, these types of coatings are highly pigmented with zinc (up to 80 wt% in the dry coating). This may result not only in a deterioration of the performance of the coating system but also have a negative impact on the environment. Taking the above into account, solvent-based and water-based organic epoxy primers with zinc content reduced to approximately 50% have been developed. Zinc pigments of different shapes and with different surface treatments were used in the primers, as well as pigments without chemical treatment but with the addition of nanoparticles. It was found that, depending on the type of zinc pigment, both the developed solvent-based and water-based primers demonstrate good protective properties comparable to traditional zinc-rich coatings. Water-based paints tend to absorb more moisture compared to solvent-based systems, but their water uptake reversibility is limited. Moreover, the organic treatment of zinc flakes helps to improve this water uptake reversibility, improving the mechanical properties of coatings.

The effect of pigments and additives on the resistance of organic binders to cyclic changes in temperature, humidity, and UV radiation intensity was investigated. The study involved paints based on two binders used in polyurethane paints, pigmented in various shades of yellow, red, and blue. Both the binders and pigments differed in their weather resistance. The color stability, gloss, water contact angle, and surface energy of the coatings were assessed. Changes in color and gloss depended primarily on UV radiation, while decorative properties depended on the type of pigments in each color group. Smaller changes in color and gloss were caused by changes in humidity and temperature, without the contribution of UV radiation. The more weather-resistant pigmentation protected the binder from degradation, as confirmed by FT-IR.

This study presents an eco-friendly approach to antibacterial polyester powder coatings by incorporating hybrid additives composed of biopolymers immobilized on halloysite nanotubes. Polylysine (PLY) and quaternized chitosan (CH-Q) were used as natural antimicrobial agents, while halloysite (HAL) acted as a carrier to improve dispersion and reduce leaching. HAL/PLY and HAL/CH-Q hybrids were incorporated into polyester coatings and evaluated for morphology, mechanical properties, water resistance, and antibacterial performance (ISO 22196). The HAL/PLY coating demonstrated a strong bactericidal effect, reducing Escherichia coli and Staphylococcus aureus by 99.9989% and 99.9993%, respectively. HAL/CH-Q showed moderate activity against E. coli (50.2323%) but high activity against S. aureus (98.6500%). Immobilization of biopolymers on the halloysite surface improved dispersion and barrier properties while enabling a silver-free antibacterial effect. The results demonstrate a sustainable strategy for multifunctional powder coatings based on naturally derived antimicrobial components.