In this work, we elucidate polymer-layered hollow Prussian blue-coated magnetic nanocomposites as an adsorbent to remove radioactive cesium from environmentally contaminated water. To do this, Fe₃O₄ nanoparticles prepared using a coprecipitation method were thickly covered with a layer of cationic polymer to attach hollow Prussian blue through a self-assembly process. The as-synthesized adsorbent was confirmed through various analytical techniques. The adsorbent showed a high surface area (166.16 m²/g) with an excellent cesium adsorbent capacity and removal efficiency of 32.8 mg/g and 99.69%, respectively. Moreover, the superparamagnetism allows effective recovery of the adsorbent using an external magnetic field after the adsorption process. Therefore, the magnetic adsorbent with a high adsorption efficiency and convenient recovery is expected to be effectively used for rapid remediation of radioactive contamination.

The Korea Atomic Energy Research Institute (KAERI) obtains UO₂ powder using the ammonium uranyl carbonate (AUC) wet process. Hydrated lime (Ca(OH)₂) is used to neutralize liquid wastes produced from the AUC process, and the resulting byproduct is known as lime waste. The purpose of this study is to determine optimum operating conditions for cementation of radioactive lime waste produced from the AUC process, and to evaluate the structural stability and leaching stability of cement waste form. The waste acceptance criteria (WAC) of a waste disposal facility in Korea were used to evaluate the cement waste form samples. The maximum lime waste content guaranteeing the shape stability of cement waste form was found to be 80 wt.% or less. Considering the economic feasibility and error of the cementation process, the optimum operating conditions were achieved at a lime waste content of 75 wt.% and a water-to-cement (w/c) ratio of 2.0. The compressive strength of cement waste form samples prepared under optimal operating conditions was 61.4, 76.3, and 61.0 kgf/cm² after the thermal cycling test, water immersion test, and irradiation, respectively, satisfying the compressive strength of 35.2 kgf/cm² specified in WAC. A leaching test was performed on the samples, and the leachability indexes (LX) of Cs, Sr, and Co nuclides were 7.63, 8.02, and 10.89, respectively, which are all higher than the acceptance criterion of 6. The results showed that the cement waste forms prepared under optimal operating conditions satisfied the WAC in terms of structural stability and leaching stability. As such, the proposed cement solidification method for lime waste disposal can be effective in solidifying lime waste powder produced during the neutralization of liquid wastes in the AUC process.

Polydimethyl-siloxane (PDMS) is often applied to fabricate cell chips. In this study, we fabricated an adipocyte microcell pattern chips using PDMS to analyze the inhibition activity of lipid droplets in mouse embryo fibroblast cells (3T3-L1) with anti-obesity agents. To form the PDMS based micropattern, we applied the micro-contact printing technique using PDMS micro-stamps that had been fabricated by conventional soft lithography. This PDMS micro-pattern enabled the selective growth of 3T3-L1 cells onto the specific region by preventing cell adhesion on the PDMS region. It then allowed growth of the 3T3-L1 cells in the chip for 10 days and confirmed that lipid droplets were formed in the 3T3-L1 cells. After treatment of orlistat and quercetin were treated in an adipocyte micro-cell pattern chip with 3T3-L1 cells for six days, we found that orlistat and quercetin exhibited fat inhibition capacities of 19.3% and 24.4% from 0.2 μM of lipid droplets in 3T3-L1 cells. In addition, we conducted a direct quantitative analysis of 3T3-L1 cell differentiation using Oil Red O staining. In conclusion, PDMS-based adipocyte micro-cell pattern chips may contribute to the development of novel bioactive compounds.