In this work, the degradation process of natural ester-based insulating fluids was evaluated through laboratory aging tests. Two distinct aging methodologies were used: natural ester-based insulating fluids were placed in sealed flasks at 120°C in the presence of Kraft insulating paper containing about 1.5 and 5 wt% moisture; and natural ester-based insulating fluids were aged with and without Kraft insulating paper containing 1.5 wt% moisture in an open system, adding oxygen at different temperatures. The results indicate that viscosity, acid number and dissipation factor are important markers to consider in monitoring service-aged natural ester fluids.

Minor-destructive (MDT) and non-destructive (NDT) techniques are not commonly used for masonry as they are complex and difficult to perform. This paper describes validation of the following methods: semi-non-destructive, non-destructive, and ultrasonic technique for autoclaved aerated concrete (AAC). The subject of this study covers the compressive strength of AAC test elements with declared various density classes of: 400, 500, 600, and 700 (kg/m³), at various moisture levels. Empirical data including the shape and size of specimens, were established from tests on 494 cylindrical and cuboid specimens, and standard cube specimens 100 mm × 100 mm × 100 mm using the general relationship for ordinary concrete (Neville’s curve). The effect of moisture on AAC was taken into account while determining the strength f_Bw for 127 standard specimens tested at different levels of water content (w = 100%, 67%, 33%, 23%, and 10%). Defined empirical relations were suitable to correct the compressive strength of dry specimens. For 91 specimens 100 mm × 100 mm × 100 mm, the P-wave velocity c_p was tested with the transmission method using the ultrasonic pulse velocity method with exponential transducers. The curve (f_Bw–c_p) for determining the compressive strength of AAC elements with any moisture level (f_Bw) was established. The developed methods turned out to be statistically significant and can be successfully applied during in-situ tests. Semi-non-destructive testing can be used independently, whereas the non-destructive technique can be only applied when the developed curve f_bw–c_p is scaled.

This article presents results from non-destructive testing (NDT) that referred to the location and diameter or rebars in beam and slab members. The aim of paper was to demonstrate that the accuracy and deviations of the NDT methods could be higher than the allowable execution or standard deviations. Tests were conducted on autoclaved aerated concrete beam and nine specimens that were specially prepared from lightweight concrete. The most advanced instruments that were available on the market were used to perform tests. They included two electromagnetic scanners and one ground penetrating radar (GPR). The testing equipment was used to analyse how the rebar (cover) location affected the detection of their diameters and how their mutual spacing influenced the detected quantity of rebars. The considerations included the impact of rebar depth on cover measurements and the spread of obtained results. Tests indicated that the measurement error was clearly greater when the rebars were located at very low or high depths. It could lead to the improper interpretation of test results, and consequently to the incorrect estimation of the structure safety based on the design resistance analysis. Electromagnetic and radar devices were unreliable while detecting the reinforcement of small (8 and 10 mm) diameters at close spacing (up to 20 mm) and of large (20 mm) diameters at a close spacing and greater depths. Recommendations for practical applications were developed to facilitate the evaluation of a structure.

In the article research of the influence of bed joint reinforcement on the compressive and shear strength of Autoclaved Aerated Concrete (AAC, 600kg/m3 type) masonry were described. 18 reinforced models under compression and 18 specimens under diagonal compression were tested according to guidelines of EN 1052-1:2000 [4] and ASTM E519-81 [1] code. The tests of compressive walls showed that the reinforcement influenced on the compressive strength and deformability of wall. Research of shear walls has shown, that the most beneficial effect on shear strength obtained using steel structural truss type reinforcement when mortar applying on the upper and down bed surfaces of units (double joints)

The areas of Central and Eastern Europe and, thus, Poland are not exposed to the effects of seismic actions. Any possible tremors can be caused by coal or copper mining. Wind, rheological effects, the impact of other objects, or a nonuniform substrate are the predominant types of loading included in the calculations for stiffening walls. The majority of buildings in Poland, as in most other European countries, are low, medium-high brick buildings. Some traditional materials, like solid brick (>10% of construction materials market) are still used, but autoclaved aerated concrete (AAC) and cement-sand calcium-silicate (Ca-Si) elements with thin joints are prevailing (>70% of the market) on the Polish market. Adding reinforcement only to bed joints in a wall is a satisfactory solution (in addition to confining) for seismic actions occurring in Poland that improves ULS (ultimate limit state) and SLS (serviceability limit state). This paper presents results from our own tests on testing horizontal shear walls without reinforcement and with different types of reinforcement. This discussion includes 51 walls made of solid brick (CB) reinforced with steel bars and steel trusses and results from tests on 15 walls made of calcium-silicate (Ca-Si) and AAC masonry units reinforced with steel trusses and plastic meshes. Taking into account our own tests and those conducted by other authors, empirical relationships were determined on the basis of more than 90 walls. They are applicable to the design and construction phases to determine the likely effect of reinforcements on cracking stress that damage shear deformation and wall stiffness.

The structure safety can be assessed, but only indirectly, by identifying material properties, geometry of structures, and values of loads. The complete and comprehensive assessment can be done only after determining internal forces acting inside structures. Ultrasonic extensometry using an acoustoelastic effect (AE) is among the most common non-destructive techniques (NDT) of determining true stresses in structures. Theoretical bases of the method were described in the mid 20th century. They were founded on the correlation between ultrasonic waves and the value and direction of stresses. This method is commonly used to determine stresses mainly in homogeneous materials without any inherent internal defects. This method is rarely applied to porous or composite materials, such as concrete or rock due to a high dispersion of results. Autoclaved aerated concrete (AAC), characterized by high homogeneity and porosity, is the popular material in the construction sector, used to produce masonry units. The discussed tests involved the acoustoelastic effect to determine stresses in the masonry wall made of AAC. This paper presents a widely theoretical background for the AE method, and then describes the author’s own research on AAC divided into two stages. At first, the empirical relationships between compressive stress and velocity of longitudinal ultrasonic wave, including humidity, were determined. In stage II, nine masonry walls were tested in axial compression. Mean compressive stresses in the masonry wall determined with the proposed method were found to produce a satisfactory confidence level up to ca. 50% of failure stresses. Results were significantly understated for stresses of the order of 75% of failure stresses.