The results of the modification of austenitic matrix in cast high-manganese steel containing 11÷19% Mn with additions of Cr, Ni and Ti were discussed. The introduction of carbide-forming alloying elements to this cast steel leads to the formation in matrix of stable complex carbide phases, which effectively increase the abrasive wear resistance in a mixture of SiC and water. The starting material used in tests was a cast Hadfield steel containing 11% Mn and 1.34% C. The results presented in the article show significant improvement in abrasive wear resistance and hardness owing to the structure modification with additions of Cr and Ti

Changes in the microstructure and selected mechanical properties of two-phase ferritic-austenitic cast steel containing 24% Cr-5% Ni-2.5% Mo-2.5% Cu after isothermal holding at 750 °C and 900 °C are presented. The choice of the two temperatures of isothermal holding was dictated by the precipitation of brittle phases within a range of 600 °C–950 °C, while the holding time depended on the casting cooling time in the mould. Changes in the microstructure were studied by the SEM-EDS and XRD techniques. As a result of the decomposition of the eutectoid ferrite, a σ phase that was rich in Cr, Mo, and Ni and a secondary γ₂ austenite with Widmannstätten morphology were formed. Compared to the austenite, the chemical composition of the secondary γ₂ austenite showed depletion of Cr and Mo. In the ferrite, the presence of Cr₂N nitrides was also detected. After a holding time of 3 h at 900 °C, these phases increased the hardness of the tested cast steel to approximately 275 HV₁₀. At the same time, the UTS value was recorded to decrease with the increasing temperature based on the tensile test results. At 750 °C, the value of UTS was 250 MPa for 1 h of holding and 345 MPa for 3 h of holding. These values decreased after increasing the temperature to 900 °C and amounted to 139 for 1 h holding and 127 MPa for 3 h holding. It was also found that the elongation values at 750 °C ranged from 7–10%, while they amounted to 35–37% at 900 °C. A fracture analysis of the tested cast steel showed that in the prevailing part, the fractures were made of ductile nature with an arrangement of dimples that is typical for this type of fracture. Non-metallic inclusions that are typical for cast steel (i.e., oxides and nitrides) were also found in the area of the fractures.

Three variants of high-entropy alloys (HEAs) from the AlCoCuFeNi group, containing different amounts of Al and Cu, were developed and produced via induction melting and casting into ceramic moulds. The ingots were homogenized at 1000 °C for 10 h. Analyses revealed that variations in Al and Cu concentrations led to significant changes in the material’s microstructure, hardness, strength, and impact strength. In the equiatomic variant, differential scanning calorimetry revealed a peak associated with the phase transformation, indicating that this alloy’s microstructure consists of two distinct phases. In contrast, when the concentrations of Al and Cu are reduced, a single-phase microstructure is observed. The equiatomic variant (used as a reference) is characterized by its hardness and brittleness, exhibiting slight ductility, with a tensile strength of 80 MPa, a hardness of 400 HV5, and an impact strength of 1.9 J/cm². However, with adjusted Al contents of 1/2 and Cu contents of 1/4, the alloy displays exceptional strength combined with good plasticity, achieving a tensile strength of up to 450 MPa with 60% elongation, and an impact strength of 215 J/cm². The non-equiatomic variants exhibit a comparatively more straightforward microstructure and enhanced ductility, which may facilitate easier processing of these alloys. Fractography investigation revealed a ductile mode of fracture in the samples.

An influence of a decreased Cr content on the microstructure of the highly alloyed Cr-Ni cast steel, duplex type, melted under laboratory conditions, was characterized in the paper. The microstructure investigations were performed in the initial state and after the heat treatment (solution annealing) at 1060°C as well as the phase transformation kinetics at continuous cooling was measured. The wear resistance of the investigated cast steel was tested and compared with the 24%Cr-5%Ni-2.5%Mo cast steel. The Cr content decrease, in ferritic-austenitic cast steels (duplex), from 24-26%Cr to 18% leads to the changes of the castings microstructure and eliminating of a brittle σ phase. In dependence of the casting cooling rate, apart from ferrite and austenite, also fine martensite precipitates occur in the casting structure. It was shown that the investigated cast steel is characterised by a slightly lower wear resistance than the typical cast steel duplex grades.

This article is a description of the progress of research and development in the area of massive large-scale castings - slag ladles implemented in cooperation with the Faculty of Foundry Engineering of UST in Krakow. Slag ladles are the one of the major castings that has been developed by the Krakodlew (massive castings foundry) for many years. Quality requirements are constantly increasing in relation to the slag ladles. Slag ladles are an integral tool in the logistics of enterprises in the metallurgical industry in the process of well-organized slag management and other by-products and input materials. The need to increase the volume of slag ladles is still growing. Metallurgical production is expected to be achieved in Poland by 2022 at the level of 9.4 million Mg/year for the baseline scenario - 2016 - 9 million Mg/year. This article describes the research work carried out to date in the field of technology for the production of massive slag ladles of ductile cast iron and cast steel.