Optical oxygen sensors have attracted considerable attention owing to their high sensitivity, rapid response, and broad applicability. However, their test results may be affected by fluctuations in the pump light source and instability of the detection equipment. In this study, the intrinsic luminescence of pine wood was utilized as the reference signal, and the luminescence of platinum(II) octaethylporphyrin (PtOEP) was employed as the oxygen indication signal, to fabricate a dual-signal ratiometric oxygen sensor PtOEP/PDMS@Pine. The ratio of the luminescence of pine wood to that of PtOEP was defined as the optical parameter (OP). OP increased linearly with oxygen concentration ([O₂]) in the range of 10–100 kPa, and a calibration curve was obtained. The sensor exhibits excellent anti-interference capabilities, effectively resisting fluctuations from laser sources and detection equipment. It also displays stable hydrophobicity with a contact angle of 118.3° and maintains excellent photostability under continuous illumination. The sensor exhibited long-term stability within 90 days and robust recovery performance during cyclic tests, wherein the response time and recovery time were determined to be 1.4 s and 1.7 s, respectively. Finally, the effects of temperature fluctuations and photobleaching on the sensor’s performance have been effectively corrected, enabling accurate oxygen concentration measurements in complex environments.

Gaseous oxygen detection is essential in numerous production and manufacturing sectors. To meet the varying oxygen detection requirements across different fields, techniques that offer a wide oxygen detection range should be developed. In this study, a wood-based oxygen sensing material was designed using balsa wood as the supporting matrix and gadolinium hemoporphyrin monomethyl ether (Gd-HMME) as the oxygen-sensitive indicator. The wood-based Gd-HMME exhibits a cellular porous structure, which not only facilitates the loading of a substantial number of indicator molecules but also enables the rapid interaction between indicators and oxygen molecules. OP is defined as the ratio of the phosphorescence intensity of the oxygen-sensing material in the anaerobic and aerobic environment. A linear relationship between OP and oxygen partial pressure ([O₂]) was obtained within the whole range of [O₂] (0–100 kPa). The wood-based Gd-HMME exhibited excellent resistance to photobleaching, along with a rapid response time (3.9 s) and recovery time (4.4 s). It was demonstrated that the measurement results obtained using wood-based Gd-HMME were not influenced by other gaseous components present in the air. An automatic oxygen detection system was developed using LabVIEW for practical use, and the limit of detection was determined to be 0.01 kPa.