In order to improve the mechanical properties of the wood surface and explore the mechanical effect of wood veneer surface metallization, the 31-year-old Pinus sylvestris is taken as the research object and Cu is deposited on the wood surface by magnetron sputtering to achieve wood veneer metallization. Based on X-ray diffraction (XRD) and nanoindentation, a research on the gradual process of the structures and mechanical properties of wood veneer metallization was carried out. The results indicate that wood veneer metallization does not affect the crystallization zone of wood, there are still wood cellulose characteristic peaks and the crystalline structure of the wood cellulose is not damaged; the thickness of the copper thin film increases with the increase of the deposition time, the cellulose characteristic peak strength gradually decrease, and the relative crystallinity also decreases; the characteristic diffraction peaks of Cu (111), Cu (200), and Cu (220) appear near the diffraction angle 2θ which is equal to 43.3°, 50.4°, and 74.1°, and the diffraction peak intensity increases with increase of deposition time, the copper film of the metal wood veneer crystallizes well; the load–displacement of wood veneer decreases significantly with the increase of deposition time, while the moduli of elasticity and hardness increase rapidly. The load–displacement of the samples which were coated for 15 min decreased by 80%, while the moduli of elasticity and hardness of these samples increased by 24.1 times and 17.3 times, respectively. From the results of Scanning Electron Microscope (SEM) measurement of the metallization of wood veneer, it can be seen that the uniform and continuous copper film can be formed on the wood veneer surface by using the magnetron sputtering method. This paper provides a basis for wood veneer surface metallization, which is of great significance for the functional improvement of wood, the expansion of wood application fields, and the enhancement of added value.

A superhydrophobic coating on wood can effectively improve the hydrophobicity and service life of wood. In this study, an Al superhydrophobic nano-coating was constructed on the transversal section of poplar wood by magnetron sputtering based on glow-discharge plasma. The structure, microscopic morphology, surface elements, and hydrophobic properties were characterized and tested. When coated for 20 s, the water contact angle on the sample surface can reach 148.9°. When coated for 30 min, the Al-coated wood had a contact angle of 157.3°, which could maintain excellent superhydrophobic properties for 300 s. The sputtered Al nanoparticles were uniformly distributed on the wood surface and formed nanoclusters. Plenty of voids between the clusters can trap air and block contact between water droplets and the coating, making the coating obtain superhydrophobic properties. When the coating time was 60 min, the characteristic peak of the Al (111) crystal plane appeared at 38.4°, while the intensities of (101), (002), and (040) peaks of cellulose were reduced. In conclusion, magnetron sputtering was used to deposit a superhydrophobic coating on wood without low surface free energy agents. Furthermore, this research provides new inspirations for the physical modification of wood and the construction of superhydrophobic coatings on wood.

To solve the problem of dye contamination caused by methylene blue (MB), a one-step synthesised nanocellulose (CNF) and polyacrylamide (PAM) gel network was modified by using NaOH in this study, and the prepared samples were analysed for their micromorphology, chemical structure, and adsorption-release properties. The findings demonstrated that the maximum adsorption capacity of the CNF-PAM5% was 172.08 mg/g, which followed the quasi-second-order kinetic model and the Freundlich adsorption model. The adsorption of the gel increased with the increase of the NaOH-modified concentration. However, the adsorption efficiency of the CNF-PAM5% could still reach 85% after four cycles, and the CNF-PAM5% remained intact without signs of fragmentation after 4 h of stirring and water impact, which was attributed to the introduction of CNF into the PAM network to effectively improve the mechanical properties of the gel. Moreover, toxicity tests showed no significant difference in the amount of cellular activity, even when the volume of the CNF-PAM5% sample was increased up to 10-fold. This gel, which exhibits low toxicity and excellent recycling properties, serves to reduce environmental impact during the adsorption process. Furthermore, the potential exists for utilising the gel’s methylene blue-releasing (MB) properties as a fungicide for fish.

The combination of nano-metal and wood to prepare copper-coated wood-based composite materials has important research value and practical significance for improving the function of wood, expanding the application field of wood, and adding added value. In this paper, 31-year-old wood (Pinus sylvestris L. var. mongholica Litv) veneer was taken as the research object. The wood veneer was pretreated by ultrasonic wave, and copper film was deposited on the surface of the wood veneer by magnetron sputtering to prepare “environmentally friendly” copper-plated wood-based composite materials. The microstructure and hydrophobic properties of Cu-coated wood-based composites were characterized and studied. With the increase in coating time, the diffraction peak intensity of wood cellulose gradually decreased, and the diffraction peaks of Cu (111), Cu (200), and Cu (220) of metallic copper appeared. Under the sputtering condition of a substrate temperature of 200 °C, the copper film deposit on the surface of the wood was uniform and densely arranged. The surface water contact angle reached 149.9°. Ultrasonic treatment increases the porous structure of wood, and the rough metal copper film interface was constructed on the surface of wood by magnetron sputtering to transform the surface wettability of the wood from hydrophilic to super-hydrophobic. The lotus leaf effect was realized on the wood surface.

Optical oxygen sensors have attracted considerable attention owing to their high sensitivity, rapid response, and broad applicability. However, their test results may be affected by fluctuations in the pump light source and instability of the detection equipment. In this study, the intrinsic luminescence of pine wood was utilized as the reference signal, and the luminescence of platinum(II) octaethylporphyrin (PtOEP) was employed as the oxygen indication signal, to fabricate a dual-signal ratiometric oxygen sensor PtOEP/PDMS@Pine. The ratio of the luminescence of pine wood to that of PtOEP was defined as the optical parameter (OP). OP increased linearly with oxygen concentration ([O₂]) in the range of 10–100 kPa, and a calibration curve was obtained. The sensor exhibits excellent anti-interference capabilities, effectively resisting fluctuations from laser sources and detection equipment. It also displays stable hydrophobicity with a contact angle of 118.3° and maintains excellent photostability under continuous illumination. The sensor exhibited long-term stability within 90 days and robust recovery performance during cyclic tests, wherein the response time and recovery time were determined to be 1.4 s and 1.7 s, respectively. Finally, the effects of temperature fluctuations and photobleaching on the sensor’s performance have been effectively corrected, enabling accurate oxygen concentration measurements in complex environments.

The magnetron sputtering method was used to deposit nano-Al film on the wood surface of Pinus sylvestris L. var. mongholica Litv., and the material structure, electrical conductivity, mechanical properties and wetting properties were tested and characterized. When the sputtering time was 60 min, the average cross-grain sheet resistance of metallized wood was 695.9 mΩ, and the average along-grain sheet resistance was 227.2 mΩ. Load displacement decreased by more than 88%,elastic modulus increased by 49.2 times, hardness increased by 46 times andsurface hydrophobic angle was close to 130°. The grain size of the Al film on the wood surface was presented as nanoparticles, and the arrangement was uniform and dense. The results indicate that without any burden on the environment, the use of magnetron sputtering can quickly and efficiently achieve Al metallization on wood surfaces, so that the wood surface can obtain conductivity and hydrophobic properties. The elastic modulus and hardness of the wood surface were improved, the mechanical properties of the wood were effectively improved and the functional improvement of the wood was realized. This study provides a feasible method and basis for the study of the simple, efficient and pollution-free modification of wood.