The biggest problem with most lakes that have no contact with other water sources and are being charged by precipitation is the massive eutrophication. The aim of this work was to determine the sedimentation rate in order to evaluate the progress of eutrophication for St. Ana Lake (Ciomad Mountain near the Băile Tuşnad in Harghita County (Romania)). The concentration of ²¹⁰Pb was determined by means of high resolution gamma spectrometry as well as derived from ²¹⁰Po activity which was measured through alpha spectrometry; values obtained are in good agreement. For the excess ²¹⁰Pb activity values between 4.0±0.5 Bq/kg and 218±20 Bq/kg have been found. As an alternative method, the ¹³⁷Cs dating method was applied as well. Calculated mass sedimentation rates are in the range of 0.06±0.01 to 0.32±0.05 g/cm² year with a mean of value of 0.15±0.02 g/cm² year. Linear sedimentation rates yielded much higher sedimentation values (between 0.5±0.1 and 7.9±0.7 cm/year with a mean of 2.4±0.6 cm/year), due to the predominant organic matter composition and the long suspension time of the sediment. This is an indication for the process of eutrophication which will probably lead to the transformation of the lake into a peat bog.

Radon (Rn) is a hazardous radioactive gas that poses significant health risks in enclosed indoor environments. This study investigates the potential of silver-exchanged clinoptilolite-rich natural zeolite (NZ-Ag⁺) for the removal of Rn from air. Natural zeolite (NZ) was thermally treated and further modified to enhance its adsorption characteristics. The thermally treated NZ (200 °C) was first exchanged in Na⁺ form, since Na⁺ is more easily exchanged in clinoptilolite with hydrated Ag⁺ ions than the other exchangeable cations. The modification with Ag⁺ was carried out at room temperature using ultrasonic processing to obtain (NZ-Ag⁺). The materials were characterized in terms of chemical composition, cation exchange capacity, mineralogy, total surface area, pore volume, and thermal behavior. Rn adsorption experiments were performed using a closed-circuit system, and the efficiency of NZ-Ag⁺ was compared with that of NZ. The results indicate that NZ-Ag⁺ exhibits superior Rn adsorption capacity, achieving up to 50% higher retention efficiency compared to NZ. The improved performance is attributed to enhanced adsorption facilitated by silver ion clusters interacting with radon atoms. These results suggest that silver-exchanged zeolite represents a promising material for radon mitigation in air filtration systems, with potential applications in residential and occupational settings.