Chemically crosslinked hydrogels based on poly(N-vinylcaprolactam) (PNVCL) were synthetized by a photoinitiated chemical method. A galactose-based monomer, 2-lactobionamidoethyl methacrylate (LAMA), and N-vinylpyrrolidone (NVP) were added with the aim to improve the physical and chemical properties of hydrogels. The effects of both comonomers on the swelling ratio (Q), volume phase transition temperature (VPTT), glass transition temperature (T_g), and Young’s moduli by mechanical compression below and above the VPTT were studied. Gold nanorods (GNRDs) and 5-fluorouracil (5FU) were embedded into the hydrogels, to study the drug release profiles with and without the excitation of GNRDs by irradiation in the near-infrared region (NIR). Results showed that the addition of LAMA and NVP increased the hydrogels’ hydrophilicity, elasticity, and VPTT. The loading of GNRDs in the hydrogels changed the release rate of 5FU when irradiated intermittently with an NIR laser. The present study reports on the preparation of a hydrogel-based platform of PNVCL-GNRDs−5FU as a potential hybrid anticancer hydrogel for chemo/photothermal therapy that could be applied against skin cancer for topical 5FU delivery.

Currently, wound dressing technology is of significant interest in order to avoid undesired effects when burns or skin wounds are treated, especially their risk for microbial contamination and subsequent infection. Silver nanoparticles (AgNPs) have claimed importance as antimicrobial agents. For these reasons, a comparative study of different methods to synthesize electrospun polymeric fibers loaded with AgNPs (Ag⁺/PCLPVP) such as direct blending, ultraviolet irradiation, thermal treatment, and silver mirror reaction methods were done. The morphology and size of the fibers were investigated using the SEM, where the loading of the AgNPs in the fibers was measured with EDS analysis. FTIR, Raman spectroscopy, XRD, and TGA analysis were applied to measure the physicochemical properties of the fibers. DLS study allowed us to measure the size and surface charge of the obtained materials. The antimicrobial efficiency was carried out against Staphylococcus aureus and Escherichia coli bacteria for 24 h. Cytotoxicity was evaluated with the MTT assay using HFF1 cells. The results showed that the method with the best antimicrobial effect in both bacteria is the UV irradiation conducted before the electrospinning process. The UV radiation method also promotes good distribution efficiency, the physicochemical properties obtained were desirable for wound dressings, and the particle size within nanoparticle interval (~17 nm). Therefore, the most promising method for the preparation of Ag+/PCLPVPbased wound dressings was UV irradiation.

In this work, five new chelating resins (MRnBz) functionalized with N -benzyl bis(carbamoyl)carboxylic acid molecules (Bz bCCA ) on their surface were prepared to study the metal ion (M ^{n +} ) adsorption properties in water.

The limited mechanical properties of composite materials, including stiffness, strength, and biocompatibility, restrict their effectiveness in biomedical applications. This research enhanced the mechanical properties and biocompatibility of polylactic acid and carbon fiber-reinforced composites (PLA/CFRCs) by incorporating multi-walled carbon nanotube (MWCNT) fillers. The methodology involved synthesizing MWCNTs and integrating them into PLA/CFRC laminates using fusion-blending, dispersion, and interlaminar spray-coating. Raman spectroscopy confirmed the presence of MWCNTs, with characteristic D and G band peaks and an I_D/I_G of 1.44 ± 0.089. SEM revealed MWCNTs in the PLA/CFRC matrix and allowed size determination, with an outer diameter range of 125–150 nm and a length of 14,407 ± 2869 nm. FTIR identified interactions between the matrix and the MWCNTs, evidenced by band shifts. TGA/DSC analysis showed thermal stability above 338 °C for all composites. The tensile tests revealed that all composites had values greater than 19 GPa for the elastic modulus and 232 MPa for the ultimate strength. Cytotoxicity assays confirmed biocompatibility, and all samples maintained a cell growth rate greater than 80%. This study highlighted the potential of nanotechnology to optimize the mechanical behavior of polymer-based composites, expanding their applicability in biomedical fields.

In recent years, the composite nanomaterials area has had a great development impact in health sciences. Biomaterials depict as one of the most promising since they are compatible with additive manufacturing (AM) techniques. It is also possible to use them to mold specific medical parts. Composite nanomaterials have shown good biocompatibility and low toxicity to have benefits equal to or greater than metals (i.e., Co-Cr alloy). The purpose of this study is to develop a nanocomposite biomaterial (PLA/MWCNTf) from Polylactic Acid (PLA) and functionalized Multi Walled Carbon Nanotubes (MWCNTf) to evidence its potential application in 3D printing of orthopedic fixation devices. PLA/MWCNTf nanocomposite was prepared by solution blending technique, incorporating a proportion of 0.5 wt% of MWCNTf to the PLA matrix. TGA analysis of the PLA/MWCNTf was used to determine the thermal stability, a slight increase was found compared to the PLA. FTIR spectroscopy confirmed the presence of carboxylic acid groups in the MWCNTf which improves good incorporation of the nanotubes in the PLA matrix. Additionally, Raman spectroscopy, SEM, and AFM micrographs were used to verify MWCNTf reached the PLA surface homogeneously. Additive manufacturing preparation was done by extrusion molding of PLA/MWCNTf as well as its 3D printing.

In this work, the preparation of dense blended membranes, from blends of poly(vinylidene fluoride) (PVDF), poly(ether sulfone) (PES) and polyethyleneimine (PEI) or Fumion^®, with possible applications in alkaline fuel cell (AEMFC) is reported. The blended PEI/Fumion^® membranes were prepared under a controlled air atmosphere by a solvent evaporation method, and were characterized regarding water uptake, swelling ratio, thermogravimetric analysis (TGA), infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), ion exchange capacity (IEC), OH⁻ conductivity and novel hydroxide ion exchange rate (HIER), which is related to the mass transport capacity of the OH⁻ ions through the membrane. The effect of the chemical composition on its morphological and anion exchange properties was evaluated. It was expected that the usage of a commercial ionomer Fumion^®, in the blended membranes would result in better features in the electrical/ionic conductivity behaviour. However, two of the membranes containing PEI exhibited a higher HIER and OH⁻ conductivity than Fumion^® membranes, and were excellent option for potential applications in AEMFC, considering their performance and the cost of Fumion^®-based membranes.