The aim of this study is to investigate the influence of cross-linking and reinforcements in gelatin on the physico-mechanical properties of obtained composites. The gelatin-based composites cross-linked with citric acid (CA) were prepared: gelatin type B (GB) and β-tricalcium phosphate (β-TCP) and novel hybrid composite GB with β-TCP and hydroxyapatite (HAp) particles, and their structure, thermal, and mechanical properties were compared with pure gelatin B samples. FTIR analysis revealed that no chemical interaction between the reinforcements and gelatin matrix was established during the processing of hybrid composites by the solution casting method, proving the particles had no influence on GB cross-linking. The morphological investigation of hybrid composites revealed that cross-linking with CA improved the dispersion of particles, which further led to an increase in mechanical performance. The microindentation test showed that the hardness value was increased by up to 449%, which shows the high potential of β-TCP and HAp particle reinforcement combined with CA as a cross-linking agent. Furthermore, the reduced modulus of elasticity was increased by up to 288%. Results of the MTT assay on L929 cells have revealed that the hybrid composite GB-TCP-HA-CA was not cytotoxic. These results showed that GB cross-linked with CA and reinforced with different calcium phosphates presents a valuable novel material with potential applications in dentistry.

While dental poly methyl methacrylate(PMMA) possesses distinctive qualities such as ease of fabrication, cost-effectiveness, and favorable physical and mechanical properties, these attributes alone are inadequate to impart the necessary impact strength and hardness. Consequently, pure PMMA is less suitable for dental applications. This research focused on the incorporation of Strontium titanate (SrTiO₃-STO) and hybrid filler STO/Manganese oxide (MnO₂) to improve impact resistance and hardness. The potential of STO in reinforcing PMMA is poorly investigated, while hybrid filler STO/MnO₂ has not been presented yet. Differential scanning calorimetry is conducted in order to investigate the agglomeration influence on the PMMA glass transition temperature (T_g), as well as the leaching of residual monomer and volatile additives that could pose a threat to human health. It has been determined that agglomeration with 1 wt% loading had no influence on T_g, while the first scan revealed differences in evaporation of small molecules, in favor of composite PMMA-STO/MnO₂, which showed the trapping potential of volatiles. Investigations of mechanical properties have revealed the significant influence of hybrid STO/MnO₂ filler on microhardness and total absorbed impact energy, which were increased by 89.9% and 145.4%, respectively. Results presented in this study revealed the reinforcing potential of hybrid nanoparticles that could find application in other polymers as well.

Flexible, wearable biomedical sensors based on laser-induced graphene (LIG) have garnered significant attention due to a straightforward fabrication process and exceptional electrical and mechanical properties. However, most relevant studies rely on commercial polyimide precursors, which suffer from inadequate biocompatibility and weak adhesion between the precursor material and the LIG layer. To address these challenges, we synthesized cross-linked polyurethanes (PUs) with good biocompatibility and used them as substrates for LIG-based wearable pulse sensors. During fabrication, we employed two methods of LIG transfer to achieve optimal transfer yield. We adjusted the thickness of PU films and tailored their mechanical and physicochemical properties by varying the soft segment content to achieve optimal sensor performance. Our findings demonstrate that the success of LIG transfer is strongly influenced by the structure and composition of the polymeric substrate. Tensile testing revealed that increasing the soft segment content in PU films significantly improved their tensile strength, elongation at break, and flexibility, with PU based on 50 wt.% soft segment content (PU-50) showing the best mechanical properties. LIG exhibited minimal sensitivity to humidity, while PU films maintained high transparency (>80% at 500 nm), and PU-50 was non-toxic, with less than 5% lactate dehydrogenase (LDH) release in endothelial cell cultures, confirming its biocompatibility. Adhesion tests demonstrated that LIG transferred onto PU-50 exhibited significantly stronger adhesion compared to other tested substrates, with only a 30% increase in electrical resistance after the Scotch tape test, ensuring stability for wearable sensors. The optimal substrate, a semicrystalline PU-50, yielded superior transfer efficiency. Among all tested sensors, the LIG/PU-50, featuring a 77 μm thick substrate with good mechanical properties and improved adhesion, exhibited the highest signal-to-noise ratio (SNR). This study showcases a skin-safe LIG/PU-based pulse sensor that has significant potential for applications as a wearable patch in medical and sports monitoring.