Coal fly ash zeolites with Sodalite structure were synthesized by ultrasound-assisted double stage fusion-hydrothermal synthesis. Monometallic Ni and bimetallic Ni–Cu supported catalysts with 5 wt.% Ni and different copper contents of 1.5, 2.5 and 5.0 wt.% Cu were prepared by post-synthesis incipient wetness impregnation. The catalysts were characterized by X-ray powder diffraction, N₂ physisorption, transmission electron microscopy (TEM), Mössbauer spectroscopy and H₂ temperature programmed reduction analysis. It was found that crystalline Cu⁰ and Ni_xCu_y intermetallic nanoparticles were formed in the reduced powder and 3D printed catalysts and that they affected the reducibility of the catalytically active nickel phase. Three-dimensionally printed 5Ni2.5Cu/Sodalite catalysts were prepared via modification with metals before and after 3D printing for comparative studies. The powder and 3D printed catalysts were studied in the lignocellulosic biomass-derived levulinic acid (LA) to γ-valerolactone (GVL). The formation of NiCu alloy, which is found on the powder and 3D printed catalysts, favors their catalytic performance in the studied reaction. In contrast with powder catalysts, the preservation of the Sodalite structure was detected for all 3D printed samples and was found to have a positive influence on the metal dispersion registered in the 3D spent catalysts. The powder 5Ni2.5Cu/Sodalite catalyst showed the highest LA conversion and high GVL yield at 150 °C reaction temperature. Three-dimensionally printed catalysts show more stable catalytic activity than powder catalysts due to the preservation of the zeolite structure and metal dispersion.

One of the approaches to limit the negative impact on the environment from the burning of coal in the production of heat and electricity is to limit their use by blending them with biomass. Blended fuel combustion leads to the generation of a solid ash residue differing in composition from coal ash, and opportunities for its utilization have not yet been studied. The present paper provides results on the carbon capture potential of adsorbents developed through the alkaline conversion of ash mixtures from the combustion of lignite and biomass from agricultural plants and wood. The raw materials and the obtained adsorbents were studied with respect to the following: their chemical and phase composition based on Atomic Absorption Spectroscopy with Inductively Coupled Plasma (AAS-ICP) and X-ray powder diffraction (XRD), respectively, morphology based on scanning electron spectroscopy (SEM), thermal properties based on thermal analysis (TG and DTG), surface parameters based on N₂ physisorption, and the type of metal oxides within the adsorbents based on temperature-programmed reduction (TPR) and UV-VIS spectroscopy. The adsorption capacity toward CO₂ was studied in dynamic conditions and the obtained results were compared to those of zeolite-like CO₂ adsorbents developed through the utilization of the raw coal ash. It was observed that the adsorbents based on ash of blended fuel have a comparable carbon capture potential with coal fly ash zeolites despite their lower specific surface areas due to their compositional specifics and that they could be successfully applied as adsorbents in post-combustion carbon capture systems.

The present study aims to develop 3D-structured adsorbents for carbon capture with the utilization of coal ash after its conversion into zeolites. For this purpose, printing paste mixtures with a viscosity of 800 Pa·s were developed based on an environmentally friendly and safe polymer binder filled with coal ash zeolite with the addition of bentonite as a filler. The optimal consistency of the printing mixtures for preserving the shape and dimensions of the 3D-printed structures was established. Various model configurations of the macrostructure of 3D adsorbents were developed, and the optimal settings of the extruding system for their printing were established. After calcination, the resulting 3D structures were studied using instrumental analysis techniques, investigating the influence of 3D structuring on the phase composition, surface characteristics, and adsorption capacity for CO₂ capture in comparison with the initial powder coal ash zeolite adsorbents. The role of compensating cations in terms of the adsorption ability of powders in 3D-printed adsorbents was investigated. The current study offers an innovative and previously unexplored approach to a more expedient and practically significant utilization of aluminosilicate solid waste and, in particular, coal ash, through their 3D structuring and outlines a new research and technological direction in the development of economically advantageous, technologically feasible, and environmentally friendly 3D adsorbents.