Studies were conducted on the effects of filler loading and 3-aminopropyltriethoxysilane (SCA) on the physical characteristics of epoxidized natural rubber (ENR)-alumina nanoparticles composites (ENRAN). The filler loading varied from 10, 20, 30, 40, 50, and 60 phr in the absence and presence of 2 phr SCA in every formulation. The alumina nanoparticles have a positive interaction with the ENR matrix since they increase the glass transition temperature of the composites [Mohamad, N., Muchtar, A., Ghazali, M.J., Dahlan, H.M. and Azhari, C.H. (2008). The Effect of Filler on Epoxidized Natural Rubber-Alumina Nanoparticles Composites, Eur. J. Sci. Res., 24: 538—547]. The addition of SCA decreased the maximum torque (MH) and the torque difference (MH-ML) of ENRANs compound as well as causing the curing process to occur at a very fast rate. The spherical alumina particles were dispersed in ENR matrix and a uniform particle distribution was observed under scanning electron microscope enabling the increase of the torque values in the composites.

This research explores the potential of using recycled polypropylene (PP) incorporated with shrimp shell waste to produce a sustainable polymer composite. In this study, the mechanical and physical properties of recycled polypropylene/shrimp shell (rPP/SS) composites prepared by melt compounding and compression molding techniques were evaluated. The effects of SS loading were investigated by using various compositions of rPP/SS composites, ranging from 0 to 8 wt.% SS that consists of two different sizes, i.e., fine and coarse SS. The composites were tested for their mechanical and physical properties using impact, tensile and water absorption tests. Furthermore, the morphology of the composites was examined by using a scanning electron microscope (SEM). Incorporation of SS was found to increase the Young's modulus of the rPP, but the impact and tensile strength showed a decrease. However, we observed that both the impact and tensile strength improve with the further increase of the SS content. In other words, composites with high shrimp shell loading were observed to exhibit better tensile and impact properties compared to composites with low shrimp shell loading. Moreover, at 8 wt.% of SS, the value of tensile strength is comparable to that of neat rPP.