To alleviate resource shortage, reduce the cost of materials consumption and the pollution of agricultural and forestry waste, walnut shell composites (WSPC) consisting of walnut shell as additive and copolyester hot melt adhesive (Co-PES) as binder was developed as the feedstock of selective laser sintering (SLS). WSPC parts with different ingredient proportions were fabricated by SLS and processed through after-treatment technology. The density, mechanical properties and surface quality of WSPC parts before and after post processing were analyzed via formula method, mechanical test and scanning electron microscopy (SEM), respectively. Results show that, when the volume fraction of the walnut shell powder in the WSPC reaches the maximum (40%), sintered WSPC parts have the smallest warping deformation and the highest dimension precision, although the surface quality, density, and mechanical properties are low. However, performing permeating resin as the after-treatment technology could considerably increase the tensile, bending and impact strength by 496%, 464%, and 516%, respectively.

Agricultural and forestry wastes are used as materials for selective laser sintering (SLS) to alleviate resource shortage, reduce the pollution of the environment, lower the cost of materials, and improve the accuracy of parts produced by SLS. However, the mechanical properties of wood–plastic parts are poor, and thus they cannot be applied widely. In order to improve the mechanical properties of wood–plastic parts, a new type of walnut shell polymer composite (WSPC) was prepared by a polymer mixing method and was used to produce parts via SLS. Additionally, the dimensional accuracy, morphologies, density, and mechanical properties of the WSPC parts were studied. The results showed that the addition of a small amount of copolyamide (Co-PA) powder could effectively improve the mechanical properties and decrease the density of the WSPC parts. By increasing the amount of Co-PA powder and decreasing that of copolyester (Co-PES) powder, the mechanical properties first increased, then decreased, and finally increased again; in addition, the density first decreased then increased. By increasing the preheating temperature, the mechanical properties and density of the WSPC parts were enhanced.

Purpose: A new kind of polymer mixture (co-PA-PES) was prepared in different mass ratios, by mixing polyether sulfone hot-melt adhesive (PES-HmA) and copolyamide B249 (PA-B249). This study aims to investigate its characteristics of laser sintering and get the optimal process parameters. Design/methodology/approach: The effect of mass ratio of co-PA-PES on thermal behavior was analyzed using a simultaneous thermal analyzer, and the density and mechanical properties of sintered parts were tested to evaluate the performance of the polymeric system. Scanning electron microscopy and Fourier transform infrared spectroscopy were performed to characterize the microstructure and binding mechanism of sintered co-PA-PES parts. Specifically, mechanical properties of the mixture with 20 Wt.% PA-B249 were optimized based on a design of experiment methodology, along with the restriction of maximum absorbable laser energy density. Findings: Liquid phase fusion was considered as the main sintering mechanism for co-PA-PES, and mechanical interlocking was the dominant binding mechanism. The effects of mass ratios of this material on the thermal properties, density and mechanical properties were obtained via data results. Additionally, compared to neat PES-HmA, co-20 Wt.% PA-PES showed a 71.7 per cent increase in tensile strength, 24.4 per cent increase in flexural strength and 102.1per cent increase in impact strength. Originality/value: This paper proposed a new kind of polymer mixture as the feedstock for laser sintering with the advantages of low price and easy processing. The filler of PA-B249 effectively improved the performance of the polymer mixture, including but not limited to mechanical properties.