Additive manufacturing (AM) stands out for its variable applications in terms of material, quality, and geometry. Wire Arc Additive Manufacturing (WAAM) is remarkable for producing large parts in reduced times when compared to other AM methods. The possibility of producing a part with a near-net shape not only enhances productivity but also reduces resources usage. However, parts produced by WAAM may need post-processing by machining to achieve functional surface requirements. Therefore, it is important that machining, even if minimized, does not lead to a significant environmental impact. In this sense, this work evaluates the effect of using compressed air, dry cut, and synthetic biodegradable cutting fluid at varying nozzle positions and flow rates on the surface quality of ER70S-6 steel produced by WAAM, after milling with TiAlN-coated carbide tools. To analyze the surface roughness, parameters Ra, Rq, and Rz were measured and microscopy was used to further evaluate the surfaces. The surface hardness was also evaluated. The results showed that a flow rate of 10 L/min promotes better surface quality, which can be further improved using compressed air, leading to a surface quality 50% better when compared to dry cutting. Dry cut was not suitable for machining ER70S-6 WAAM material as it resulted in rough surface texture with an Rz = 4.02 µm. Compressed air was the best overall condition evaluated, achieving a 36% Ra reduction compared to dry cutting, the second-lowest hardness deviation at 6.51%, and improved sustainability by eliminating the need for cutting fluid.

Laser-Directed Energy Deposition (L-DED) is an additive manufacturing technique used for producing and repairing components, mainly for coating applications, depositing metal matrix composites such as cemented carbides, composed of hard metal carbides and a metallic binder. In this sense, this study evaluated the preparation of a ready-to-press WC-25Co powder as a reliable feedstock for L-DED process. This powder required pre-heat treatment studies to prevent fragmentation during powder feeding, due to the absence of metallurgical bonding between WC and Co particles. In the current study, the Taguchi methodology was used, varying laser power, powder feed rate, and scanning speed to reach an optimised deposition window. The best bead morphology resulted from 2400 W laser power, 11 mm/s scanning speed, and 9 g/min feed rate. Moreover, defects such as porosity and cracking were mitigated by applying a remelting strategy of 2400 W and 9 mm/s. Therefore, a perfect deposition is obtained using the optimised processing parameters. Microstructural analysis of the optimised deposited line revealed a fine structure, comprising columnar and equiaxed dendrites of complex carbides. The average hardness of the deposited WC-25Co powder on a AISI 1045 steel was 854 ± 37 HV0.2. These results demonstrate the potential of L-DED for processing high-performance cemented carbide coatings.