High temperature operation of molten sodium batteries impacts cost, reliability, and lifetime, and has limited the widespread adoption of these grid-scale energy storage technologies. Poor charge transfer and high interfacial resistance between molten sodium and solid-state electrolytes, however, prevents the operation of molten sodium batteries at low temperatures. Here, in situ formation of tin-based chaperone phases on solid state NaSICON ion conductor surfaces is shown in this work to greatly improve charge transfer and lower interfacial resistance in sodium symmetric cells operated at 110 °C at current densities up to an aggressive 50 mA cm⁻². It is shown that static wetting testing, as measured by the contact angle of molten sodium on NaSICON, does not accurately predict battery performance due to the dynamic formation of a chaperone NaSn phase during cycling. This work demonstrates the promise of sodium intermetallic-forming coatings for the advancement of low temperature molten sodium batteries by improved mating of sodium–NaSICON surfaces and reduced interfacial resistance.

Solar thermochemical hydrogen (STCH) production is a promising method to generate carbon neutral fuels by splitting water utilizing metal oxide materials and concentrated solar energy. The discovery of materials with enhanced water-splitting performance is critical for STCH to play a major role in the emerging renewable energy portfolio. While perovskite materials have been the focus of many recent efforts, materials screening can be time consuming due to the myriad chemical compositions possible. This can be greatly accelerated through computationally screening materials parameters including oxygen vacancy formation energy, phase stability, and electron effective mass. In this work, the perovskite Gd_0.5La_0.5Co_0.5Fe_0.5O₃ (GLCF), was computationally determined to be a potential water splitter, and its activity was experimentally demonstrated. During water splitting tests with a thermal reduction temperature of 1,350°C, hydrogen yields of 101 μmol/g and 141 μmol/g were obtained at re-oxidation temperatures of 850 and 1,000°C, respectively, with increasing production observed during subsequent cycles. This is a significant improvement from similar compounds studied before (La_0.6Sr_0.4Co_0.2Fe_0.8O₃ and LaFe_0.75Co_0.25O₃) that suffer from performance degradation with subsequent cycles. Confirmed with high temperature x-ray diffraction (HT-XRD) patterns under inert and oxidizing atmosphere, the GLCF mainly maintained its phase while some decomposition to Gd_2-xLa_xO₃ was observed.

Germanium–antimony–telluride has emerged as a nonvolatile phase change memory material due to the large resistivity contrast between amorphous and crystalline states, rapid crystallization, and cyclic endurance. Improving thermal phase stability, however, has necessitated further alloying with optional addition of a quaternary species (e.g., C). Here, the thermal transport implications of this additional species are investigated using frequency-domain thermoreflectance in combination with structural characterization derived from x-ray diffraction and Raman spectroscopy. Specifically, the room temperature thermal conductivity and heat capacity of ${({\mathrm{Ge}}_2{\mathrm{Sb}}_2{\mathrm{Te}}_5)}_{1-x}{\mathrm{C}}_x$ are reported as a function of carbon concentration ($x\le 0.12$ ) and anneal temperature ($\mathrm{T}\le 350{}^{°}\mathrm{C}$ ) with results assessed in reference to the measured phase, structure, and electronic resistivity. Phase stability imparted by the carbon comes with comparatively low thermal penalty as materials exhibiting similar levels of crystallinity have comparable thermal conductivity despite the addition of carbon. The additional thermal stability provided by the carbon does, however, necessitate higher anneal temperatures to achieve similar levels of structural order.

Sputter-deposited Pt-Au thin films have been reported to develop a hard, stable, nanocrystalline structure, yet little is known about how these characteristics vary with PtxAu1−x composition and process conditions. Toward this end, this document describes an extensive, combinatorial Pt-Au thin film library including characterized film compositions, structure, and properties. Complemented by kinematic Monte Carlo simulations of codeposition, a broad range of PtxAu1−x compositions (from x ∼ 0.02 to 0.93) was first established by sputtering with varied magnetron powers and gun tilt angles. The produced films were subsequently interrogated using automated nanoindentation, x-ray reflectivity, x-ray diffraction, atomic force microscopy, surface profilometry, four-point probe sheet resistance techniques, and wavelength dispersive spectroscopy in order to determine how hardness, modulus, density, surface roughness, structure, and resistivity vary with film stoichiometry and process parameters. Combinatorial films displayed an assortment of properties with the hardness of some films exceeding values reported previously for this material system. High hardness, high modulus, and low resistivity were generally attained when using increased deposition energy and reduced angle-of-incidence processes. Overall, the research identified promising, new PtxAu1−x compositions for future study and pinpointed strategies for improved deposition.