The hardfacing process aims to increase the life span of structural components in the petrochemical, mining, nuclear and automotive industries. During operation, these components are subject to demands of abrasion wear, cavitation erosion and corrosion. Duplex stainless steels are characterized by high mechanical characteristics and corrosion resistance, but poor behavior to abrasive wear and cavitation erosion. The improvement in wear resistance is possible by selecting and depositing a special alloy on the surface using a joining technique that ensures a metallurgical bonding between the layer and the substrate. The experimental investigations carried out in this work demonstrate the ability of the TIG pulsed welding process to produce layers with good functional properties for engineering surfaces. The “Corodur 65” alloy was deposited on a duplex-stainless-steel substrate, X2CrNiMoN22-5-3, using a series of process parameters that allowed for the control of the cooling rate and heat input. The properties of the deposited layers are influenced not only by the chemical composition, but also by the dilution degree value. Since the deposition of layers through the welding operation can be considered as a process with several inputs and outputs, the control of the input parameters in the process aims at finishing the granulation and the structure in the fusion zone as well as limiting the segregation phenomena. The aim of this work is to investigate the microstructural characteristics of the iron-based alloy layer, Corodur 65, deposited via pulsed current TIG welding on duplex X2CrNiMoN22-5-3 stainless-steel substrates.

Duplex stainless steels are materials with high performance under mechanical stress and stress corrosion in chloride ion environments. Despite being used in many new applications such as components for offshore drilling platforms as well as in the chemical and petrochemical industry, the automotive industry, etc., they face issues of wear and hardness that limit current applications and prevent the creation of new use opportunities. To address these shortcomings, it is proposed to develop a hardfacing process by a special welding technique using a universal TIG source adapted for manual welding with a pulsed current, and a manganese austenitic alloy electrode as filler material. The opportunity to deposit layers of manganese austenitic steel through welding creates advantages related to the possibility of achieving high mechanical characteristics of this steel exclusively in the working area of the part, while the substrate material will not undergo significant changes in chemical composition. As a result of the high strain hardening rate, assisted mainly by mechanical twinning, manganese austenitic alloys having a face-centered cubic crystal lattice (f.c.c) and low stacking fault energy (SFE = 20–40 mJ/m²) at room temperature, exhibit high wear resistance and exceptional toughness. Following cold deformation, the hardness of the deposited metal increases to 465 HV5–490 HV5. The microstructural characteristics were investigated through optical microscopy (OM), scanning electron microscopy (SEM), energy-dispersive X-ray analysis (EDX), X-ray diffraction (XRD), and Vickers hardness measurements (HV). The obtained results highlighted the feasibility of forming hard coatings on duplex stainless steel substrates.

Cavitation-induced degradation of metallic materials presents a significant challenge for engineers and users of equipment operating with high-velocity fluids. For any metallic material, the mechanical strength and ductility characteristics are controlled by the mobility of dislocations and their interaction with other defects in the crystal lattice (such as dissolved foreign atoms, grain boundaries, phase separation surfaces, etc.). The increase in mechanical properties, and consequently the resistance to cavitation erosion, is possible through the application of heat treatments and cold plastic deformation processes. These factors induce a series of hardening mechanisms that create structural barriers limiting the mobility of dislocations. Cavitation tests involve exposing a specimen to repeated short-duration erosion cycles, followed by mass loss measurements and surface morphology examinations using optical microscopy and scanning electron microscopy (SEM). The results obtained allow for a detailed study of the actual wear processes affecting the tested material and provide a solid foundation for understanding the degradation mechanism. The tested material is the Ni-based alloy INCONEL 625, subjected to stress-relief annealing heat treatment. Experiments were conducted using an ultrasonic vibratory device operating at a frequency of 20 kHz and an amplitude of 50 µm. Microstructural analyses showed that slip bands formed due to shock wave impacts serve as preferential sites for fatigue failure of the material. Material removal occurs along these slip bands, and microjets result in pits with sizes of several micrometers.

The present work aims to investigate the microstructure and mechanical properties of laser beam spot welds in the superalloy Nimonic 80 A. Considering the importance of this innovative process in the manufacturing of engineering components for high-security industries, it is necessary to study the influence of the welding thermal cycle on the microstructure and mechanical properties of welded joints. The rapid heating/cooling, melting, and re-solidification phenomena that occur during welding modify the metallurgical characteristics of the weld compared with the microstructure of the base metal. Because the energy density is high and the process duration is very short, the microstructure obtained after solidification is fine dendritic in the central area of the joint and columnar in the weld–base metal transition zone. For the same reasons, the heat-affected zone (HAZ) is slightly extended. The increase in the size of the crystalline grains in the HAZ is negligible due to the low diffusivity of the nickel-based γ solid solution matrix, which inhibits the rapid migration of grain boundaries during the welding process. Metallographic analyses were performed using optical microscopy and scanning electron microscopy. The microhardness values, 152–168 HV0.05 in the weld and 180–190 HV0.05 in the base metal, together with the tensile–shear strength values (760–780 N/mm²) obtained at room temperature, demonstrate that the proposed welding process is appropriate and feasible for engineering applications involving Nimonic 80A superalloys.