Water pollution caused by increasing industrial and human activity remains a serious environmental challenge, especially due to the persistence of organic contaminants in aquatic systems. Photocatalysis offers a promising and eco-friendly solution, but in the case of bismuth oxide (Bi₂O₃) there is still a limited understanding of how structural and morphological features influence photocatalytic performance. In this work, a straightforward hydrothermal synthesis method followed by controlled calcination was developed to produce phase-pure α- and β-Bi₂O₃ with tunable morphologies. By varying the hydrothermal temperature and reaction time, distinct structures were successfully obtained, including flower-like, broccoli-like, and fused morphologies. XRD analyses showed that the final crystal phase depends solely on the calcination temperature, with β-Bi₂O₃ forming at 350 °C and α-Bi₂O₃ at 500 °C. SEM and BET analyses confirmed that morphology and surface area are strongly influenced by the hydrothermal conditions, with the flower-like β-Bi₂O₃ exhibiting the highest surface area. UV–Vis spectroscopy revealed that β-Bi₂O₃ also has a lower bandgap than its α counterpart, making it more responsive to visible light. Photocatalytic tests using Rhodamine B showed that the flower-like β-Bi₂O₃ achieved the highest degradation efficiency (81% in 4 h). Kinetic analysis followed pseudo-first-order behavior, and radical scavenging experiments identified hydroxyl radicals, superoxide radicals, and holes as key active species. The catalyst also demonstrated excellent stability and reusability. Additionally, Methyl Orange (MO), a more stable and persistent azo dye, was selected as a second model pollutant. The flower-like β-Bi₂O₃ catalyst achieved 73% degradation of MO at pH = 7 and complete removal under acidic conditions (pH = 2) in less than 3 h. These findings underscore the importance of both phase and morphology in designing high-performance Bi₂O₃ photocatalysts for environmental remediation.

Contamination of water bodies caused by increasing human and industrial activities poses a serious threat to human health and environmental sustainability, highlighting the need for green and efficient remediation strategies. In this study, a facile hydrothermal synthesis followed by controlled calcination was developed to fabricate phase-pure α- and β-Bi₂O₃ with a unique coral-like hierarchical morphology as visible-light-active photocatalysts. Phase selectivity was achieved by tuning the calcination temperature, yielding pure β-Bi₂O₃ while preserving the hierarchical structure. Optical characterization revealed a narrower bandgap for β-Bi₂O₃ (2.24 eV) compared to α-Bi₂O₃ (2.75 eV), favoring visible-light absorption. Photocatalytic performance was evaluated using Rhodamine B as a model pollutant, where β-Bi₂O₃ achieved complete degradation within 240 min, significantly outperforming α-Bi₂O₃. The degradation followed pseudo-first-order kinetics, and the catalyst exhibited excellent robustness and reusability. To further demonstrate applicability toward persistent contaminants, Methyl Orange (MO) and the antibiotic ciprofloxacin (CIP) were employed as additional model pollutants. The coral-like β-Bi₂O₃ showed high visible-light activity toward MO, including complete removal under acidic conditions. Moreover, efficient degradation of CIP was achieved at neutral pH, with 90% removal within 150 min and complete degradation after 240 min. Overall, these results highlight coral-like β-Bi₂O₃ as an efficient standalone photocatalyst for visible-light-driven degradation of dye and pharmaceutical pollutants.