Ultra-high performance concrete (UHPC) is a kind of cement-based material with ultra-high strength, high toughness and excellent durability. However, the tensile strain capacity of UHPC is often below 0.5%, and the mode of single crack failure is the main failure pattern, which limits the development of UHPC. In order to overcome the weakness of the relatively low strain capacity of UHPC, five types of polyethylene (PE) fibers with different geometrical and mechanical parameters (length, diameter and elastic modulus) were added into the matrix, and the corresponding mechanical behavior was investigated. The experimental results showed that the high fiber length and fiber diameter of PE fibers are a benefit for the compressive strength and tensile strength of UHPC. The increase of the fiber diameter and elastic modulus remarkably attributed to the increase in the tensile strain capacity of UHPC. With the increase of the fiber diameter and elastic modulus, the overall energy absorption capacity G and the energy absorption capacity of the substrate prior to the softening section g_a of UHPC were both enhanced. The diameter of PE fiber was the main factor affecting the energy consumption of UHPC. Among the five types of PE fiber, PF fiber (PF fiber is PF type polyethylene fiber; Fiber length: 15 mm; Fiber diameter: 27 μm; Elastic Modulus: 117 GPa) is the optimal fiber to increase the tensile mechanical behavior of UHPC.

Multi-walled carbon nanotubes (MWCNTs) have great potential to improve the strength and microstructure of traditional cement-based materials. In this research, different aspect ratios of MWCNTs (F-type and L-type) were dispersed into water using surfactants, and then incorporated into reactive powder concrete (RPC) for improving mechanical and microstructure properties. With the addition of 0.025 wt.% F-MWCNTs, the 28 days compressive strength and initial-cracking flexural strength increased by 7.2% and 36%, respectively. Moreover, the first-cracking tensile strengths of the composites containing L-MWCNTs were improved by 16%. Energy absorption capability indices were formulated based on tensile load–displacement curves, and results showed that the energy absorption capabilities of RPC at initial cracking improved as a result of the incorporation of MWCNTs. Furthermore, microscopic analysis indicated that MWCNTs decelerate crack development at the nanoscale and improve the initial-cracking tensile strength of RPC.

This work experimentally studies the mechanical properties and microstructure of cementitious composites reinforced with a three-dimensional graphene–carbon nanotube (CNT) hybrid. Firstly, the graphene–CNT (GC) hybrid is dispersed in cement pastes using ultrasonication and surfactant, and then, the effect of the GC hybrid on the early hydration of the cement pastes is investigated. The experimental results show that adding the GC hybrid shortens the setting stage of cement hydration and accelerates the early hydration process. Moreover, the macro- and micro-mechanical properties of each group are evaluated. The 7- and 28-day strength of the cement pastes improves with addition of the GC hybrid. Finally, the microstructural analysis demonstrates that the GC hybrid is reasonably well distributed in cement and forms a spatial network, which could bridge the cracks and compact the cementitious matrix.

High strength and high ductility concrete (HSHDC) exhibit exceptional compressive strength (up to 90 MPa) and remarkable tensile ductility (ultimate tensile strain reaching 6%), making them highly resilient under impact loading. To elucidate the influence of strain rate and wet–dry cycling of salt spray on the dynamic compressive response of HSHDC, a series of tests was conducted using a 75 mm split Hopkinson pressure bar (SHPB) system on specimens exposed to cyclic corrosion for periods ranging from 0 to 180 days. The alternating seasonal corrosion environment was reproduced by using a programmable walk-in environmental chamber. Subsequently, both uniaxial compression and SHPB tests were employed to evaluate the post-corrosion dynamic compressive properties of HSHDC. Experimental findings reveal that corrosive exposure significantly alters both the static and dynamic compressive mechanical behavior and constitutive characteristics of HSHDC, warranting careful consideration in long-term structural integrity assessments. As corrosion duration increases, the quasi-static and dynamic compressive strengths of HSHDC exhibit an initial enhancement followed by a gradual decline, with stress reaching its peak at 120 days of corrosion under all strain rates. All specimens demonstrated pronounced strain-rate sensitivity, with the dynamic increase factor (DIF) being minimally influenced by the extent of corrosion under dynamic strain rates (112.6–272.0 s⁻¹). Furthermore, the peak energy-consumption capacity of HSHDC was modulated by both the duration of corrosion and the applied strain rate.