Crumb rubber (CR) is one of the materials most widely used in the road infrastructure industry due to its mechanical and environmental benefits as an asphalt binder modifier. Nonetheless, CR decreases the workability of mixes by increasing the viscosity of the binder, leading to an increase in the production temperatures of asphalt mixes. However, warm mix technologies can reduce the temperature demand associated with these processes. The preceding explains the growing interest in producing rubberised asphalt binders incorporating warm mix asphalt (WMA) additives. In this research, the mechanical and rheological properties of a 60/70 penetration grade asphalt binder modified with CR (at a dosage of 15, 18 and 21% by the wet process) and WMA chemical additives (Evotherm M1 and Iterlow T) were investigated. Laboratory tests included penetration, softening point, rotational viscosity, frequency sweep through dynamic shear rheometer (DSR), and multiple stress creep recovery (MSCR) tests. The results indicate that CR increases the stiffness of the asphalt binder, which is reflected in a lower penetration grade and improved softening point. It also improves its rutting resistance but decreases fatigue performance. Furthermore, it has been shown that under the conditions studied, the higher the CR content, the more elevated the degree of stiffness and performance of the asphalt binder. On the other hand, WMA technology decreases asphalt stiffness and performance at high temperatures.

Graphene is a carbon-based nanomaterial used in various industries to improve the performance of hundreds of materials. For instance, graphene-like materials have been employed as asphalt binder modifying agents in pavement engineering. In the literature, it has been reported that (in comparison to an unmodified binder) the Graphene Modified Asphalt Binders (GMABs) exhibit an enhanced performance grade, a lower thermal susceptibility, a higher fatigue life, and a decreased accumulation of permanent deformations. Nonetheless, although GMABs stand out significantly from traditional alternatives, there is still no consensus on their behavior regarding chemical, rheological, microstructural, morphological, thermogravimetric, and surface topography properties. Therefore, this research conducted a literature review on the properties and advanced characterization techniques of GMABs. Thus, the laboratory protocols covered by this manuscript are atomic force microscopy, differential scanning calorimetry, dynamic shear rheometer, elemental analysis, Fourier transform infrared spectroscopy, Raman spectroscopy, scanning electron microscopy, thermogravimetric analysis, X-ray diffraction, and X-ray photoelectron spectroscopy. Consequently, the main contribution of this investigation to the state-of-the-art is the identification of the prominent trends and gaps in the current state of knowledge.

Unlike conventional pavements with a service life of 20~30 years, perpetual pavements (PPs) are designed to have a 50-year service life without requiring major maintenance and rehabilitation (M&R) activities. In this way, PPs are more cost-effective than conventional rigid pavements (CRPs) and conventional flexible pavements (CFPs). Nonetheless, even though the economic and mechanical aspects of PPs have been widely studied and well documented, the literature is limited regarding the environmental assessment of PPs. Consequently, this research estimated the environmental burden associated with five pavement structures (one CRP, one CFP, and three PP structures) through the life-cycle assessment (LCA) methodology. Notably, the PaLATE computational tool was used to carry out the LCAs. The results indicated that for CFP, most of the environmental impacts are generated by the M&R activities. Otherwise, for CRP and PP structures, the most impact occurred during the initial construction stage. The study results also revealed that materials production is the sub-stage that most contributed to the generation of environmental detriments. Overall, this comparative case study concluded that the pavement alternative with the slightest environmental damage is the PP structure.

Portland cement concrete (PCC) has been the most widely used concrete in the construction industry. However, PCC has a short service life under some aggressive environments, leading to the need of costly repairs. The purpose of this research was to implement local materials to produce a modified sulfur concrete (MSC) with better performance in industrial applications. Several modified sulfur concrete mixtures were prepared using natural aggregates from the northern region of Colombia, and sulfur cement by combination of sulfur with a modifier, with the objective of achieving the best performance based on mechanical strength and chemical resistance. To achieve this purpose, an experimental program based on a k-factorial design was used to determine the optimal mix design based on the results of the compressive strength. The mixture presenting the best results was then examined further with standardized tests to determine its physical, mechanical, and chemical properties (compressive strength, abrasion resistance, bulk density, absorption, and chemical resistance). Final results showed that the sulfur concrete mixture is very resistant to chemical attack and an outstanding substitute for PCC. The results indicated that there is no significant loss in weight and no relevant variation in compressive strength after the specimens were immersed in sulfuric acid and sulfate solutions. In addition, similar results were obtained for the slabs located in chemicals plants whose conditions were assessed during a 60-day period of exposure.