Ammonia has emerged as a promising fuel for solid oxide fuel cells (SOFCs) owing to its high energy density, high hydrogen content, and carbon-free nature. Herein, the electrocatalytic potential of a novel Ni-doped SFM double-perovskite (Sr_1.9Fe_0.4Ni_0.1Mo_0.5O_6-δ) is studied, for the first time, as an alternative anode material for symmetrical direct-ammonia SOFCs. Scanning and transmission electron microscopy characterization has revealed the exsolution of Ni-Fe nanoparticles (NPs) from the parent Sr₂Fe_1.5Mo_0.5O₆ under anode conditions, and X-ray diffraction has identified the FeNi₃ phase after exposure to ammonia at 800 °C. The active-exsolved NPs contribute to achieving a maximal ammonia conversion rate of 97.9% within the cell's operating temperatures (550-800 °C). Utilizing 3D-printed symmetrical cells with SFNM-GDC electrodes, the study demonstrates comparable polarization resistances and peak power densities of 430 and 416 mW cm^-2 for H₂ and NH₃ fuels, respectively, with long-term stability and a negligible voltage loss of 0.48% per 100 h during ammonia-fed extended galvanostatic operation. Finally, the ammonia consumption mechanism is elucidated as a multistep process involving ammonia decomposition, followed by hydrogen oxidation. This study provides a promising avenue for improving the performance and stability of ammonia-based SOFCs for potential applications in clean energy conversion technologies.

This study investigates the synthesis and characterization of boron-modified nanotubular titania (NTO) arrays fabricated via a single-step anodizing process with varying concentrations of boric acid (BA). Following anodization, a reductive heat treatment was applied to facilitate the crystallization of the anatase phase in the boron-modified NTO. The effect of the BA concentration on the structural, morphological, and photoelectrochemical (PEC) properties of the NTOs was systematically explored through scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), luminescence, and UV-Vis spectrometry. The introduction of boron during anodization facilitated the formation of sub-bandgap states, thereby enhancing the light absorption and electron mobility. This study revealed the optimal BA concentration that yielded a 3.3-fold enhancement of the PEC performance, attributed to a reduction in the bandgap energy. Notably, the highest incident photon-to-current conversion efficiency (IPCE) was observed for NTO samples anodized at a 0.10 M BA concentration. These findings underscore the promise of boron-modified NTOs for advanced photocatalytic applications, particularly in solar-driven water-splitting processes.