This study investigated sawdust-derived activated carbon (SAC) as a sustainable reinforcing filler for vulcanized rubber bushings (VRBs). Two types SAC200 (75 µm, carbonized at 200 °C) and SAC400 (38 µm, carbonized at 400 °C) were chemically activated and incorporated into natural rubber (NR) at 25–55 phr loadings, while SAC free VRBs served as controls. Fourier transform infrared (FTIR) analysis revealed that SAC400 exhibited stronger hydroxyl and carbonyl functional groups, indicating higher surface reactivity compared with SAC200. The incorporation of SAC increased cross-linking density, thereby enhancing both curing behavior and mechanical performance. VRBs reinforced with SAC400 demonstrated higher maximum torque (up to 38.07 kg·cm), shorter scorch time (5 min 58 s), and reduced cure time (11 min 05 s) relative to SAC200 and the control. Mechanical properties improved markedly, with hardness and tensile strength rising from 45 Shore A and 5.52 MPa in the control to 70 Shore A and 13.40 MPa in SAC400. Although elongation at break decreased slightly, it remained within the acceptable range for dynamic applications. Swelling resistance also increased, reaching 101.76% at 25 °C and 106.61% at 100 °C. Overall, SAC400 consistently outperformed SAC200 and the control, highlighting its potential as a renewable, biomass-derived filler for high-performance rubber bushings and promising a sustainable alternative to conventional fillers in industrial applications.