Industrial effluents and wastewater treatment have been a mainstay of environmental preservation and remediation for the last decade. Silica nanoparticles (SiO₂) obtained from rice husk (RH) are an alternative to producing low-cost adsorbent and agriculture waste recovery. One adsorption challenge is facilitating the adsorbate separation and reuse cycle from aqueous medium. Thus, the present work employs SiO₂ supported on polylactic acid (PLA) nanofibers obtained by the electrospinning method for Rhodamine B (RhB) dye adsorption. The silica surface was modified with trimethylsilyl chloride (TMCS) to increase affinity towards organic compounds. As a result, the silanized surface of the silica from rice husk (RHSil) promoted an increase in dye adsorption attributed to the hydrophobic properties. The PLA fibers containing 40% SiO₂ (w w⁻¹) showed about 85–95% capacity adsorption. The pseudo-first-order kinetic model was demonstrated to be the best model for PLA:SiO₂ RHSil nanocomposites, exhibiting a 1.2956 mg g⁻¹ adsorption capacity and 0.01404 min⁻¹ kinetic constant (k₁) value. In the reuse assay, PLA:SiO₂ membranes preserved their adsorption activity after three consecutive adsorption cycles, with a value superior to 60%. Therefore, PLA:SiO₂ nanocomposites from agricultural waste are an alternative to “low-cost/low-end” treatments and can be used in traditional treatment systems to improve dye removal from contaminated waters.

A novel black, direct band gap (E_g = 1.32 eV), water and temperature stable hybrid lead halide perovskite was synthesized and characterized.

The elusive hydroxylammonium lead iodide NH ₃ OHPbI ₃ has been successfully synthesized and characterized for the first time.

This work focuses on the possible application of gold nanoparticles on flexible cotton fabric as acetone- and ethanol-sensitive substrates by means of impedance measurements. Specifically, citrate- and polyvinylpyrrolidone (PVP)-functionalized gold nanoparticles (Au NPs) were synthesized using green and well-established procedures and deposited on cotton fabric. A complete structural and morphological characterization was conducted using UV–VIS and Fourier transform infrared (FT–IR) spectroscopy, atomic force microscopy (AFM), and scanning electron microscopy (SEM). A detailed dielectric characterization of the blank substrate revealed interfacial polarization effects related to both Au NPs and their specific surface functionalization. For instance, by entirely coating the cotton fabric (i.e., by creating a more insulating matrix), PVP was found to increase the sample resistance, i.e., to decrease the electrical interconnection of Au NPs with respect to citrate functionalized sample. However, it was observed that citrate functionalization provided a uniform distribution of Au NPs, which reduced their spacing and, therefore, facilitated electron transport. Regarding the detection of volatile organic compounds (VOCs), electrochemical impedance spectroscopy (EIS) measurements showed that hydrogen bonding and the resulting proton migration impedance are instrumental in distinguishing ethanol and acetone. Such findings can pave the way for the development of VOC sensors integrated into personal protective equipment and wearable telemedicine devices. This approach may be crucial for early disease diagnosis based on nanomaterials to attain low-cost/low-end and easy-to-use detectors of breath volatiles as disease markers.

A new and simple procedure for the deposition of lead (II, IV) oxide films by screen printing was developed. In contrast to conventional electrochemical methods, films can be also deposited on non-conductive substrates without any specific dimensional restriction, being the only requirement the thermal stability of the substrate in air up to 500 °C to allow for the calcination of the screen printing paste and sintering of the film. In this study, films were exploited for the preparation of both photoresponsive devices and photoelectrochemical cell photoanodes. In both cases, screen printing was performed on FTO (Fluorine-Tin Oxide glass) substrates. The photoresponsive devices were tested with I-V curves in dark and under simulated solar light with different irradiation levels. Responses were evaluated at different voltage biases and under light pulses of different durations. Photoelectrochemical cells were tested by current density–voltage (J-V) curves under air mass (AM) 1.5 G illumination, incident photon-to-current efficiency (IPCE) measurements, and electrochemical impedance spectroscopy.