A ZnPc(COOH) ₄ /Fe ₃ O ₄ /Ch photosensitizer was synthesized by immobilization of ZnPc(COOH) ₄ onto Fe ₃ O ₄ /chitosan nanoparticles by a simple immersion method.

In this study, we report the synthesis and characterization of Fe₃O₄ nanoparticles coated with dextran. The structural and optical properties of the Dx:Fe₃O₄ synthesized composites were investigated by Fourier Transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD) and UV–Vis absorption spectroscopy. For the first time in this paper, the photophysics of Dx:Fe₃O₄ composites in water is studied using fluorescence and phosphorescence molecular spectrometry. An analysis of the absorption spectra of the Dx:Fe₃O₄ composite reveals the broad absorption bands with maxima at wavelengths of 227 nm, 264 nm, and 340 nm. Dx:Fe₃O₄ composite nanoparticles in water exhibit strong fluorescence with a quantum yield of 0.24% in contrast to 0.07% for dextran. Phosphorescence spectra confirm the formation of new emission bands within the Dx:Fe₃O₄ solution evidenced by the maxima shift for both dextran and Dx:Fe₃O₄ composites.

This paper describes the electrical and dielectric behavior of the nCdS/pZnTe HJ by current–voltage, capacitance–voltage characteristics, and impedance spectroscopy in a temperature interval 220–350 K. A microcrystalline p-ZnTe layer and n-CdS were grown on glass/ZnO substrate by closed space sublimation method. As frontal contact to CdS, the transparent ZnO and as a back contact to ZnTe, silver conductive paste (Ag) treated at 50 °C in vacuum were used. The current–voltage results of nCdS/pZnTe HJ show a rectifying behavior. The junction ideality factor, barrier height, and series resistance values were extracted from the rectifying curves at different temperatures. The built-in voltage, carrier concentration and depletion width were obtained from the capacitance–voltage measurements. Analysis of the J–V–T and C–V–T characteristics shows that the thermionic emission and recombination current flow mechanisms dominate in the nCdS/pZnTe HJ. The dielectric study reveals that the experimental values of the AC conductivity, dielectric constant, dielectric loss, the imaginary part of the electric modulus are found to be very sensitive to frequency and temperature. The dielectric constant and dielectric loss are observed to be high at the low frequency region. The increase in the values of electric modulus with the frequency implies an increase in the interfacial polarization at the interface of nCdS/pZnTe HJ. Jonscher’s universal power law shows that with increasing frequency, AC conductivity increased. The results conductivity show that the ionic conductivity and interfacial polarization are the main parameters affecting the dielectric properties of the device when the temperature changes.

This paper focuses on the linking of zinc phthalocyanine (ZnPc) to N-vinylpyrrolidone (N-VP): acryloyl chloride (ClAC) copolymer. The synthesis of binary N-VP:ClAC copolymer was performed by the radical polymerization method and then grafted to ZnPc by the Friedel Crafts acylation reaction. We have developed a water-soluble ZnPc:ClAC:N-VP photosensitizer with a narrow absorption band at 970 nm, fluorescence at λ_em = 825 nm and the decay fluorescence profile with 3-decay relatively longer times of 1.2 µs, 4.6 µs, and 37 µs. The concentration-dependent dark cytotoxicity investigated in normal fibroblasts (NHDF), malignant melanoma (MeWo), adenocarcinoma (HeLa), and hepatocellular carcinoma (HepG2) cell lines incubated to increased concentrations of ZnPc:ClAC:N-VP (up to 40 μM) for 24 h in the dark show low cytotoxicity. Maximum cell viability in HeLa and HepG2 tumor cell lines was observed.

In this study, zinc phthalocyanine (ZnPc) and copper phthalocyanine (CuPc) thin films fabricated by drop casting (DC) and close space sublimation (CSS) have been investigated and compared with ZnPc and CuPc solutions in formic acid (29 µmol/L). The results show that the CSS method produces films with improved molecular ordering, enhanced surface uniformity, superior optical and morphological properties compared to those obtained by drop casting. Moreover, CSS allows a precise and reproducible deposition, resulting in thinner, homogeneous layers with strong substrate adhesion and fewer defects. Optical characterization confirms that CSS films display high transparency (~90%), a sharp Q-band around 680 nm, and a fluorescence maximum at ~825 nm with the strongest emission intensity.In contrast, DC films show lower transparency (<70%), a slightly shifted Q-band (~675 nm), and similar emission around 825 nm. The fluorescence is strongly thickness-dependent: at ~100 nm, the emission band appears at 795 nm, while films thicker than 300 nm exhibit a red-shifted maximum at ~825 nm. AFM analysis further demonstrates the influence of deposition method: CSS yields smoother films with tunable morphology, while DC produces rougher, less controllable surfaces. Overall, CSS is shown to be the more effective approach for fabricating high-quality phthalocyanine films for optoelectronic applications such as photovoltaics and sensors.