This study investigates the effectiveness of various beneficiation methods for recovering chromium from refined ferrochrome slag. Dry magnetic separation at different field intensities (0.45 T and 0.8 T) showed that selective extraction of metallic chromium (Cr_met) is more efficient at 0.45 T, achieving a recovery rate of up to 90.05%. Pneumatic separation using SEPAIR technology demonstrated promising results, especially for wide particle size fractions (0–20 mm), where chromium recovery reached 40.32% due to density differences between slag particles and metallic inclusions. Enrichment on a shaking table proved to be the most selective method, producing a concentrate with 29.9% Cr and 90.7% recovery, although the yield was low (3.8%). SEM-EDX and SEM-BSE analyses confirmed the heterogeneous phase composition of slag grains, revealing chromium–iron alloys embedded in oxide matrices. Based on laboratory experiments and material characterization, it is concluded that magnetic separation can be used for preliminary concentration, pneumatic classification is effective for processing bulk slag with economic potential, and gravity concentration on shaking tables is suitable for producing high-grade concentrates. The resulting tailings, low in chromium, are suitable for reuse in the production of building materials after carbonation treatment.

The processing of fine and technogenic chromite-bearing raw materials accumulated in tailings and sludge storage facilities is a key challenge for sustainable metallurgical development. This paper presents the results of laboratory and pilot-scale studies on the application of vibro-briquetting technology for flotation concentrates and waste materials from JSC “TNC Kazchrome” (ERG). For the first time in Kazakhstan, a pilot-scale validation of vibro-briquetting of flotation chromite concentrates was carried out, resulting in pilot confirmation of the vibro-briquetting technology. The optimal technological parameters of the process were established, and the effectiveness of various types of binders was evaluated. Pilot-scale trials demonstrated that the use of organic and mineral binders ensures the production of durable briquettes with a low yield of fines (around 2%). Comparison with conventional agglomeration technologies (pelletizing, sintering, roller-press briquetting, extrusion briquettes) highlighted the advantages of vibro-briquettes in terms of energy efficiency, environmental performance, and suitability for fine raw materials. It was shown that composite binders (lignosulfonate + cement) provide enhanced strength and water resistance in briquettes, as well as optimal conditions for strength development during thermal–moisture treatment. The findings confirm the high potential of vibro-briquetting technology in Kazakhstan as an energy-efficient and environmentally friendly solution for the integrated utilization of local chromite resources. The proposed vibro-briquetting technology makes it possible to process previously unused gravity and flotation tailings of chromite ores from the Kempirsai Massif, thereby improving the comprehensive utilization of mineral resources and reducing environmental impact. This development is of great importance for Kazakhstan’s industry, as it represents the first pilot-scale testing of cold vibro-briquetting technology for flotation concentrates.