The article provides a brief overview of technologies and methods for processing dispersed metallic waste generated during ferroalloy production, including high-carbon ferrochrome (HCFeCr). It is noted that the most cost-effective and rational method for reusing metallic dust is briquetting. Considering the development of briquetting technologies, as well as the latest equipment and binder materials involved in this process, aspiration dust from ferrochrome crushing can be fully utilized in metallurgical recycling. To verify this assumption, laboratory studies were conducted using polymer-based binders and liquid glass as a baseline option. The methodology of briquetting using both laboratory and industrial presses is described, along with an assessment of the mechanical properties of the briquettes. The studies indicate that the introduction of an inert filler (gas-cleaning dust) into the metallic dust composition improves the briquetting ability of the mixture by enhancing adhesion between metal particles and the binder. The obtained industrial briquette samples exhibit high mechanical strength, ensuring their further use in metallurgical processing. The study concludes that semi-dry briquetting using hydraulic vibropresses is a promising approach for the utilization of dispersed ferroalloy waste.

This study presents the results of laboratory experiments on the processing of lateritic nickel ores mixed with coal and CaO, followed by the use of the obtained product for the smelting of nickel-containing ferroalloy by the metallothermic method. The study analyzed the thermodynamic effects of complex reductant concentration (silicon- and aluminum-containing alloy) on the reduction degree of nickel and iron. An experimental process resulted in a product containing Ni_total (2.60%) and Fe_total (60.52%), obtained through reduction roasting of lateritic nickel ore mixed with coal and an addition of 20 g of CaO at a temperature of 1150 °C. Under laboratory conditions, a nickel-containing ferroalloy was successfully obtained using the product after reduction roasting and a complex alloy as the reducing agent. The following optimal process parameters were determined: reductant consumption of 20 g per 100 g of the reduction roasting product, smelting temperature of 1600 °C, and slag basicity (CaO/SiO₂) of 0.5. In this case, a nickel-containing ferroalloy with 72% iron, 15% nickel, and up to 5% chromium was successfully obtained through silicon and aluminum reduction using a complex alloy. A microstructural analysis of the nickel-containing alloy was conducted using an electron probe microanalyzer (JXA-8230) in combination with scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS). The results showed that silicon and iron were the dominant elements in all particles. Nickel was detected at concentrations of up to 15.02 wt. %, while chromium reached 3.47 wt. %. Depending on the silicon concentration, the nickel-containing ferroalloy is recommended for corrosion-resistant steel production (Si < 5%) and as a reducing agent for ferronickel production (Si > 5%).

This study investigates the effectiveness of various beneficiation methods for recovering chromium from refined ferrochrome slag. Dry magnetic separation at different field intensities (0.45 T and 0.8 T) showed that selective extraction of metallic chromium (Cr_met) is more efficient at 0.45 T, achieving a recovery rate of up to 90.05%. Pneumatic separation using SEPAIR technology demonstrated promising results, especially for wide particle size fractions (0–20 mm), where chromium recovery reached 40.32% due to density differences between slag particles and metallic inclusions. Enrichment on a shaking table proved to be the most selective method, producing a concentrate with 29.9% Cr and 90.7% recovery, although the yield was low (3.8%). SEM-EDX and SEM-BSE analyses confirmed the heterogeneous phase composition of slag grains, revealing chromium–iron alloys embedded in oxide matrices. Based on laboratory experiments and material characterization, it is concluded that magnetic separation can be used for preliminary concentration, pneumatic classification is effective for processing bulk slag with economic potential, and gravity concentration on shaking tables is suitable for producing high-grade concentrates. The resulting tailings, low in chromium, are suitable for reuse in the production of building materials after carbonation treatment.

This study investigates the behavior of phosphorus during high-temperature smelting of hydrogen-reduced high-phosphorus oolitic iron ore from the Lisakovsk deposit. The preliminary reduction was carried out at temperatures ranging from 600 to 900 °C using hydrogen, aiming to selectively reduce iron to the metallic phase while retaining phosphorus in the oxide form. The resulting reduced products were subjected to wet magnetic separation and liquid-phase separation. It was found that neither method provides effective separation of phosphorus from iron: phosphorus partially enters the magnetic fraction and, during smelting, transfers into the metallic phase. To confirm the mechanism of phosphate reduction by metallic iron, a control experiment was conducted, in which a mixture of reduced iron and raw ore was smelted at 1650 °C. Microstructural and elemental analyses confirmed the redistribution of phosphorus into the metallic phase. These findings indicate that effective separation of iron and phosphorus cannot be achieved by reduction roasting alone and highlight the need for further studies on slag formation conditions and phase separation kinetics.

This study addresses the problem of efficient utilization of aspiration dust (AD) generated during crushing of high-carbon ferrochrome (HCFeCr). To solve this issue, a briquetting technology was proposed, involving aspiration dust blended with dry gas-cleaning dust (20 wt.% as filler) and an organic polymer binder (3 wt.%). The produced briquettes demonstrated high mechanical strength (average 195 kg per briquette in splitting strength and 98% drop resistance), ensuring maximum integrity during transportation and handling. Pilot-industrial remelting of 35 tons of briquettes in a 1.8 MVA direct current electric arc furnace (DC EAF) confirmed the effectiveness of the proposed technology for HCFeCr production. Chromium recovery into the alloy reached 94%, which is 3–4% higher compared to remelting of loose dust. The specific electric energy consumption was 1600 kWh/t, representing a 29% reduction compared to loose dust processing. The produced metal met commercial grades FeCr800–FeCr900 specifications. Additional advantages included elimination of dust formation, reduction in fines generation during crushing of the final metal to 15%, and improved environmental performance. The developed technology represents an economically and environmentally viable solution for comprehensive recycling of ferroalloy dust waste.

Thermodynamic modeling combined with experimental reduction tests was conducted to investigate the selective reduction behavior of iron-manganese ore using hydrogen gas at 800–900 °C. The results reveal that hydrogen reduction at a flow rate of 0.5 L/min promotes the stepwise transformation of iron oxides (Fe₂O₃ → Fe₃O₄ → FeO → Fe), accompanied by the decomposition of the intermediate spinel phase Fe2MnO4, resulting in the formation of metallic iron. In contrast, the reduction of MnO to metallic manganese is thermodynamically unfavorable (ΔG > 0), limiting the extent of manganese reduction. Experimental findings confirm the formation of metallic iron inclusions enriched in Fe, while manganese predominantly remains in the form of MnO and silicate-associated oxides. X-ray diffraction analysis of reduced samples shows a decrease in Fe₃O₄ and Fe₂MnO₄ phases with increasing reduction degree and indicates the growth of metallic Fe particles with rising temperature. These results demonstrate that hydrogen enables controlled and selective reduction of iron with minimal manganese conversion, providing a promising route for subsequent efficient magnetic separation of metallic and oxide phases following reduction roasting.