Clean water is a vital need for all living creatures during their lifespan. However, contaminated stormwater is a major issue around the globe. A wide range of contaminants, including heavy metals, organic and inorganic impurities, has been discovered in stormwater. Some commonly utilized methods, such as biological, physical and chemical procedures, have been considered to overcome these issues. However, these current approaches result in moderate to low contaminant removal efficiencies for certain classes of contaminants. Of late, filtration and adsorption processes have become more featured in permeable concretes (PCs) for the treatment of stormwater. As nanoparticles have vast potential and unique characterizations, such as a higher surface area to cure polluted stormwater, employing them to improve permeable concretes’ capabilities in stormwater treatment systems is an effective way to increase filtration and adsorption mechanisms. The present study reviews the removal rate of different stormwater contaminants such as heavy metals, organic and other pollutants using nanoparticle-improved PC. The application of different kinds of nanomaterials in PC as porous media to investigate their influences on the properties of PC, including the permeability rate, compressive strength, adsorption capacity and mix design of such concrete, was also studied. The findings of this review show that different types of nanomaterials improve the removal efficiency, compressive strength and adsorption capacity and decrease the infiltration rate of PC during the stormwater treatment process. With regard to the lack of comprehensive investigation concerning the use of nanomaterials in PC to treat polluted stormwater runoff, this study reviews 242 published articles on the removal rate of different stormwater contaminants by using PC improved with nanoparticles.

Oil palm shell (OPS) is a biosolid waste in palm oil industry in the tropical countries which could be used as aggregate in concrete mixture. Since 1984, OPS has been experimented as natural lightweight aggregate in research studies to produce lightweight concrete (LWC). Medium and high‐strength LWCs using OPS as coarse aggregate were successfully produced. However, higher drying shrinkage and lower mechanical properties for concretes containing higher volume of OPS are reported in previous studies. Therefore, OPS is not fit to be used as full coarse aggregate in concrete mixture and therefore, there should be an optimum OPS content in concrete. In this study, in a normal‐weight concrete, normal coarse aggregate was replaced with OPS from zero to 100% with an interval of 20%. Tests such as slump, density, compressive strength in different curing conditions, splitting tensile strength, initial and final water absorptions, and drying shrinkage of cured and uncured specimens were conducted to find out optimum OPS content in concrete. From the test results, it could be summarized that OPS content should not exceed 60% of total volume of coarse aggregate.

The utilization of by-products and waste materials to substitute for the natural or manufactured resources is considered as a practical way to obtain green building materials. In concrete mixtures, amongst the many available options, Fly Ash (FA) as a by-product pozzolan has been used as a partial replacement of cement. As for the aggregates, lightweight agro-waste oil palm shell (OPS) can be used as a replacement to conventional aggregate for the production of lightweight aggregate concrete. The present communication aims to investigate the impact of FA on time-dependent development properties of OPS lightweight aggregate concrete, including density, water absorption, compressive strength up to 120-days, and drying shrinkage up to the age of 365-days under standard moist curing, partially early curing, and non-curing conditions. Additionally, drying shrinkage crack development was investigated. In this study, two series of concrete mixtures with different substitution levels of OPS (0%, 50%, and 100%) and FA were tested. From the obtained results, it was concluded that the incorporation of fly ash in OPS concrete reduces the density and compressive strength values. Dually, the initial and final water absorption values plus the rate of drying shrinkage at early and long-term ages increased. On top of that, a high potential of drying shrinkage crack, especially for mixtures with 100% OPS, was identified.

This study provides an overview of how phase change materials (PCMs) can improve the resistance of concrete pavement to freeze–thaw cycles and mitigate the urban heat island (UHI) effect. The investigation covers different types of PCMs and methods for integrating them into concrete pavement, as well as the mechanical properties and compressive strength of concrete pavement when employing various PCMs. Prior studies have identified porous aggregates, microencapsulation, and pipelines containing liquid PCM as common approaches for PCM integration. Researchers have observed that the utilization of PCMs in concrete pavement yields favorable thermal properties, suggesting the potential for anti-freezing and UHI mitigation applications. However, the choice of PCM materials should be informed by local climate conditions.