Brookite TiO₂ is the most difficult TiO₂ polymorph to synthesize. The available methods in the literature to produce brookite nanostructures mostly use water-based techniques for the preparation of water-soluble Ti complexes first, followed by a hydrothermal growth of the brookite nanostructures. Besides its multi-step nature, achieving a single brookite phase and optimizing the aqueous growth environment are all issues to be hardly controlled. In this work, pure brookite TiO₂ nanorods are synthesized using tetrabutyl titanate Ti(OBu)₄ and Sodium Fluoride (NaF) as precursor materials in a simple non-aqueous one-pot solvothermal process. Alcoholysis of only Ti(OBu)₄ in ethanol resulted in pure anatase nanoparticles, while the addition of NaF was essential to promote the growth of highly pure brookite nanorods. The phase purity is confirmed by X-Ray Diffraction, Raman Spectroscopy, and High-Resolution Transmission Electron Microscopy. The growth mechanism is explained according to the Ostwald’s step rule, where Na⁺ ions are anticipated to have a potential role in driving the growth process towards the brookite phase.

Amplified spontaneous emission (ASE) threshold in ${\mathrm{CsPbBr}}_3$ quantum dot films is systematically reduced by introducing high quality ${\mathrm{TiO}}_2$ compact layer grown by atomic-layer deposition. Uniform and pinhole-free ${\mathrm{TiO}}_2$ films of thickness 10, 20 and 50 nm are used as a substrates for ${\mathrm{CsPbBr}}_3$ quantum dot films to enhance amplified spontaneous emission performance. The reduction is attributed indirectly to the improved morphology of ${\mathrm{TiO}}_2$ compact layer and subsequently ${\mathrm{CsPbBr}}_3$ active layer as grown on better quality substrates. This is quantified by the reduced roughness of the obtained films to less than 5 nm with 50 nm ${\mathrm{TiO}}_2$ substrate. Considering the used growth method for the quantum dot film, the improved substrate morphology maintains better the structure of the used quantum dots in the precursor solution. This results in better absorption and hence lower threshold of ASE. Besides that, the improved film quality results further in reducing light scattering and hence additional slight optical enhancement. The work demonstrates a potential venue to reduce the amplified spontaneous emission threshold of quantum dot films and therefore enhanced their optical performance.

2-hydroxyethyl methacrylate, methylmethacrylate, ethylene glycol dimethyl methacrylate, and lignocaine (drug) were mixed together and the monomers were copolymerized at 60 °C through a free radical polymerization in the presence of α,α′-Azoisobutyronitrile in tetrahydrofuran. A series of copolymer/drug composites with different monoacrylate monomer compositions were prepared by solvent evaporation and characterized by different methods such as nuclear magnetic resonance, differential scanning calorimetry, Fourier transform infrared, X-ray diffraction, and mechanical and optical testing. The water content in the copolymers and the cell viability test on the samples were also examined in this investigation. The results of the analyses of the properties of this drug-carrier system are promising, indicating that this material may be a potential candidate for contact lens applications. The release dynamic of this medication from the prepared drug-carrier systems was investigated in neutral pH media. The results obtained revealed that the diffusion of lignocaine through the copolymer matrix obeys the Fick model and the dynamic release can be easily controlled by the methyl methacrylate content in the copolymer.

A series of poly(vinyl acetate-co-2-hydroxyethylmethacrylate)/acyclovir drug carrier systems (HEMAVAC) containing different acyclovir contents was prepared through bulk free radical polymerization of 2-hydroxyethyl methacrylate with vinyl acetate (VAc) in presence of acyclovir (ACVR) as the drug using a LED lamp in presence of camphorquinone as the photoinitiator. The structure of the drug carrier system was confirmed by FTIR and ¹HNMR analysis, and the uniform dispersion of the drug particles in the carrier was proved by DSC and XRD analysis. The study of the physico-chemical properties of the prepared materials, such as the transparency, swelling capacity, wettability and optical refraction, was carried out by UV–visible analysis, a swelling test and measurement of the contact angle and the refractive index, respectively. The elastic modulus and the yield strength of the wet prepared materials were examined by dynamic mechanical analysis. The cytotoxicity of the prepared materials and cell adhesion on these systems were studied by LDH assay and the MTT test, respectively. The results obtained were comparable to those of standard lenses with a transparency of 76.90–89.51%, a swelling capacity of 42.23–81.80% by weight, a wettability of 75.95–89.04°, a refractive index of 1.4301–1.4526 and a modulus of elasticity of 0.67–1.50 MPa, depending on the ACVR content. It was also shown that these materials exhibit no significant cytotoxicity; on the other hand, they show significant cell adhesion. The in vitro dynamic release of ACVR in water revealed that the HEMAVAC drug carrier can consistently deliver uniformly adequate amounts of ACVR (5.04–36 wt%) over a long period (7 days) in two steps. It was also found that the solubility of ACVR obtained from the release process was improved by 1.4 times that obtained by direct solubility of the drug in powder form at the same temperature.

The purpose of the presented study is to examine the impact of zinc oxide nanoparticles (ZnO NPs) on the spectrum features of poly [2-methoxy-5-(3′,7′-dimethyloctyloxy)-1, 4-phenylenevinylene] (MDMO-PPV). The characteristics of the MDMO-PPV and doped ZnO NPS samples were assessed using several techniques. A set of solutions of MDMO-PPV in toluene that were doped with different ratio percentages of ZnO NPs was prepared to obtain thin films. Pristine and composite solutions were spin-coated on glass substrates. It was observed that MDMO-PPV had two distinct absorbance bands at $310$ and $500 \mathrm{nm}$ in its absorption spectrum. The UV-Vis spectrum was dramatically changed when $5\%$ of ZnO NPs were added. The result showed a significant reduction in absorption of the band $500 \mathrm{nm}$, while $310 \mathrm{nm}$ absorption increased rapidly and became more pronounced. Upon adding (10%) ZnONPs to the sample, no noticeable change was observed in the 500 nm band. However, the 310 nm band shifted towards the blue region. There is a dominant peak in the PL spectrum of MDMO-PPV in its pristine form around $575 \mathrm{nm}$ and a smaller hump around $600 \mathrm{nm}$ of the spectrum. The spectral profile at 600 nm and the intensity of both bands are improved by raising the ZnO NP concentration. These bands feature two vibronic transitions identified as (0-0) and (0-1). When the dopant concentration increased to the maximum dopant percentage ($10\%$), the energy band gap values increased by $0.21 \mathrm{eV}$ compared to the pristine MDMO-PPV. In addition, the refractive index (n) decreased to its lowest value of $2.30$ with the presence of concentrations of ZnO NPs.