A novel resin-based bulk-fill restorative material (ST; Stela SDI, Bayswater, Victoria, Australia) has been recently introduced as a self-curing alternative to traditional light-cured composites. Promoted for its unlimited depth of cure, enhanced aesthetics, and unique primer composition, it aims to address challenges associated with amalgam and light-curing composites. Thus, the aim of this in vitro study was to investigate the performance of the new self-curing polymer-based restorative material, ST, compared to two conventional light-cured composites for direct restoration. The study evaluated compressive strength with and without aging, antibacterial activity, mineral deposition in contact with Phosphate-Buffered Saline (PBS) and artificial saliva, porosity, and wettability of ST (Tetric EvoCeram (TE; Ivoclar Vivadent, Schaan, Liechtenstein) and Clearfil Majesty ES-2 (CM; Kuraray Noritake Dental, Tokyo, Japan)). The data was statistically analyzed (α = 0.05) through one-way and two-way analysis of variance (ANOVA). ST demonstrated significantly higher compressive strength than TE and CM at baseline and after aging (p < 0.001), while aging significantly reduced compressive strength across all materials (p < 0.001). Fracture mode analysis revealed brittle fractures for TE and CM, whereas ST fractured in multiple smaller fragments. CM showed the highest void volume and diameter, significantly differing from ST and TE (p < 0.001). Scanning electron microscopy (SEM) analysis revealed cubical-like crystalline formations on ST’s surface after 28 days of immersion in PBS and saliva, indicating some level of bioactivity, whereas no changes were observed for TE and CM. Wettability testing showed ST had the lowest contact angle (12.24° ± 2.1°) compared to TE (62.78° ± 4.68°) and CM (64.64° ± 3.72°) (p < 0.001). Antibacterial activity testing displayed a significant decrease in bacterial growth for CM compared to ST (p = 0.001) and TE (p = 0.002); however, ST and TE showed no significant differences (p = 0.950). To conclude, ST Automix demonstrated promising results across several key parameters, making it a potential candidate for long-lasting restorative applications. Future studies should explore its long-term clinical performance and investigate formulations that enhance its antibacterial properties. Moreover, the bond strength of these materials to dentin and the cytotoxicity should be evaluated.

Objectives: This systematic review and meta-analysis aimed to evaluate microbial adhesion and biofilm formation on additively manufactured composite-based orthodontic clear aligners compared with thermoformed aligners and other conventional polymeric materials. The influence of material composition, surface roughness, post-processing parameters, and cleaning protocols on microbial colonization was also assessed. Methods: A comprehensive search of PubMed, EMBASE, Scopus, Web of Science, and the Cochrane Library was conducted up to September 2025. Only in vitro studies investigating microbial adhesion, biofilm biomass, or microbiome changes on three-dimensional (3D)-printed aligner composites were included. Primary outcomes consisted of colony-forming units (CFU), optical density (OD) from crystal violet assays, viable microbial counts, and surface roughness. Risk of bias was assessed using the RoBDEMAT tool. Data were narratively synthesized, and a random-effects meta-analysis was performed for comparable datasets. Results: Five studies fulfilled the inclusion criteria, of which two in vitro studies were eligible for meta-analysis. Microbial adhesion and biofilm accumulation were influenced by the manufacturing technique, composite resin formulation, and surface characteristics. Certain additively manufactured aligners exhibited smoother surfaces and reduced bacterial adhesion compared with thermoformed controls, whereas others with increased surface roughness showed higher biofilm accumulation. Incorporating bioactive additives such as chitosan nanoparticles reduced Streptococcus mutans biofilm formation without compromising material properties. The meta-analysis, based on two in vitro studies, demonstrated higher OD values for bacterial biofilm on 3D-printed aligners compared with thermoformed aligners, indicating increased biofilm biomass (p < 0.05), but not necessarily viable bacterial load. Conclusions: Microbial adhesion and biofilm formation on 3D-printed composite clear aligners are governed by resin composition, additive manufacturing parameters, post-curing processes, and surface finishing. Although certain 3D-printed materials display antibacterial potential, the limited number of studies restricts the generalizability of these findings. Clinical Significance: Optimizing composite formulations for 3D printing, alongside careful post-curing and surface finishing, may help reduce microbial colonization. Further research is required before translating these findings into definitive clinical recommendations for clear aligner therapy.

Background and Objectives: This study aims to investigate the impact of hemoglobin (Hb) level changes during radiochemotherapy (RCT) on the survival of patients with locally advanced head and neck squamous cell carcinoma (HNSCC). Materials and Methods: A retrospective analysis was conducted on 97 patients with HNSCC, treated with definitive RCT between January 2016 and October 2021. Hb levels were monitored weekly during RCT. Kaplan–Meier and Cox regression analysis were performed. Results: There was a significant association between Hb levels at the end of RCT and overall survival (p < 0.01). Initial Hb levels and Hb level changes were not significantly associated with survival. In multivariate analysis, a lower body mass index (BMI) and Hb levels at week six were identified as significant prognostic factors. Conclusions: At the end of RCT, rather than baseline levels or changes during treatment, Hb levels are a significant prognostic factor for overall survival in patients with HNSCC.