The aim of the present in vitro study was to evaluate specific mechanical and physicochemical properties of two calcium silicate based sealers, (AH Plus Bioceramic “AHPB”; Well-Root ST “WRST”), and a conventional resin sealer (AH Plus “AHP”). These aims were accomplished by assessing the porosity, pH, compression strength, roughness, wettability and cell attachment of the tested materials. The results were compared statistically using the one-way ANOVA test. Higher pH values were obtained in both AHPB and WRST compared to AHP at 3, 24 and 72 h (p < 0.05). A greater level of porosity and wettability was detected for both AHPB and WRST compared to the resin sealer AHP (p < 0.05). Evident cell growth characterized by elongated morphology was observed on the surface of AHPB and WRST, while only a thin layer of cells was seen on the surface of AHP. A significant lower compression strength and modulus were obtained in the specimens created using AHPB compared to those made with AHP and WRST (p < 0.05). The removal of calcium silicates may be quite tricky during endodontic retreatment. In conclusion, considering the limitations of the present in vitro study, both calcium silicate sealers demonstrated good physicochemical properties. However, the lower compression strength and modulus of AHPB may facilitate its removal and make the retreatment procedures considerably easier.

This study investigated the antibacterial activity, bond strength to dentin (SBS), and ultra-morphology of the polymer–dentin interface of experimental adhesive systems doped with pyrogallol (PY), which is a ubiquitous phenolic moiety that is present in flavonoids and polyphenols. A universal adhesive containing 4-META and 10-MDP was used in this study. PY behaves as an antioxidant and anti-cancerogenic agent and it was incorporated into the adhesive at different concentrations (0.5 and 1 wt.%). The antibacterial activity and SBS were analyzed and the results were statistically analyzed. The ultra-morphology of the polymer–dentin interface was assessed using scanning electron microscopy (SEM). At 24 h, a lower antibacterial activity was observed for the control adhesive compared to those with 0.5% and 1% PY. No difference was seen in SBS between the three groups at 24 h. After 6 months, the SBS of the 0.5% PY adhesive was significantly lower than the other tested adhesives. The specimens created with 1% PY adhesive presented a higher bond strength at six months compared with that found at 24 h. No morphological differences were found at the polymer–dentin interfaces of the tested adhesives. Pyrogallol may be incorporated into modern universal adhesive systems to preserve the polymer–dentin bonding interface and confer a certain degree of antibacterial activity.

Flexible polyurethane foam is widely used in numerous comfort applications such as automotive seat cushions and mattresses. It would be interesting to design a mechanical model which describes the behavior of this material in a series of test conditions. This study is devoted to the modeling of the quasi-static behavior of polyurethane foam using a memory integer model. Polyurethane foam undergoing large compressive deformation exhibits highly nonlinear elasticity and a viscoelastic behavior. The memory integer model describes the nonlinearity in a polynomial function and the viscoelasticity through a convolution function. Uniaxial compression tests help to identify the mechanical parameters of the model. The difference between the force responses of foam in load and unload phases constitute the base element of the method used in this article. Numerous precautions are taken into account to obtain accurate results which verify the thermodynamic conditions. Finally, the reliability as well as the limits of the memory integer model are discussed.

The aim of the present in vitro study was to evaluate specific mechanical and physicochemical properties of three calcium silicate-based sealers, BioRoot™ Flow (BRF), CeraSeal (CRS) and TotalFill^® (TF). Samples were prepared to evaluate different physicochemical and mechanical properties of the tested sealers. These evaluations were accomplished by investigating the pH changes over time, porosity, roughness, flow properties, compressive strength and wettability. The results were statistically evaluated using one-way analysis of variance. All three sealers demonstrated an alkaline pH from 1 h of immersion in water to 168 h. A higher porosity and hydrophily were detected in BRF samples compared to CRS and TF. No significant difference was found between the tested materials in the flow properties. Lower compressive strength values were observed for BRF compared to TF and CRS. Differently shaped structures were detected on the three materials after 7 days of immersion in PBS. The three materials demonstrated a higher solubility than 3% after 24 h of immersion in water (CRS < BRF < TF). The novel premixed calcium silicate sealer (BRF) had comparable physicochemical properties to the existing sealers. The lower compressive strength values could facilitate the removal of these materials during retreatment procedures. Further studies should investigate the biological effects of the novel sealer.

The purpose of the present in vitro study was to investigate the bond strength of root canal dentin and the filling ability of a new multi-fiber-reinforced composite post (mFRC) compared to a conventional single fiber-reinforced-composite post (sFRC). Twenty-eight freshly maxillary first permanent single-rooted premolars were instrumented and divided into groups (n = 14). Group 1: single-fiber-reinforced composite (sFRC), group 2: multi-fiber-reinforced composite (mFRC). Bonding procedures were performed using a dual-cure universal adhesive system and resin cement. All specimens were sectioned so that seven discs of 1 mm of thickness were obtained from each root. An optical microscope was used before the push-out test to measure the total area of the voids and to determine the length of the smaller/bigger circumferences. The push-out bond strength (PBS) test was performed using an Instron universal testing machine. Data were then compared by one-way ANOVA on ranks (α = 0.05). The dentin–cement–post interface was observed using scanning electron microscopy (SEM). At the coronal third, a significantly higher bond strength (p < 0.05) was obtained in the sFRC group (44.7 ± 13.1 MPa) compared to the mFRC group (37.2 ± 9.2 MPa). No significant difference was detected between the groups at the middle third (sFRC group “33.7 ± 12.5 MPa” and mFRC group “32.6 ± 12.4 MPa”) (p > 0.05). Voids were significantly lower in the mFRC compared to those observed in the sFRC group (p < 0.05) at the coronal third. Whereas, no significant difference was found at the middle third (p > 0.05) between the tested groups. Filling ability was overall improved when employing mFRC, although such technique might have characteristic limitations concerning the bond strength to dentin.