The present research is focused on the 3-Polker coins issued during 1619–1627 by Sigismund III Vasa, King of Poland. A major financial crisis took place at that time due to the 30-year War, which started in 1619. There are two theories among historians concerning the silver depreciation of these coins. The most common theory (generally accepted without proof) is that the later years of issue are depreciated below 60% Ag. The second theory is based on the medieval sources that indicate inflation during the years from 1621–1625, but the medieval source only refers to the inflation of the type of coins and does not mention the issuer. Therefore, in this study, we use modern investigation techniques and materials science methods to help historians elucidate the aforementioned aspects regarding the medieval period. The XRD investigation results are in good agreement with the SEM-EDX elemental analysis. The coins from 1619 and 1620 have high silver content, namely, 86.97% and 92.49%, which corresponds to good silver. The amount of Ag found in the coins from 1621–1625 issituated in the range of 63.2–74.6%. The silver titleis suddenly restored in 1626 at about 84.3% and is kept in a good range until the end of this decree under Sigismund III in 1627. In conclusion, the second theory was partly validated by our experimental results, certifying the currency depreciation during 1621–1625, but the silver title was not lower than 54.2%. Notably, even this depreciated silver title assures a good quality of the 3-Polker coins compared to similar coins issued in other countries that were copper–silver-plated. Therefore, the 3-Polker coins were preferably hoarded at that time.Small alterations in the mint mark’s design were observed in all the depreciated coins compared to the good ones. This might be a sign for an expert to identify the depreciated coins, a fact which requires supplementary investigations. The silver title’s restoration in 1626 also came with a complete change of the mintmark.

Several forged 3-Polker coins have been reported in historical sources on the financial crisis that occurred between 1619 and 1623 at the start of the 30-year-long war. Supposedly, belligerent countries forged other countries’ coins which were then used for external payments as a war strategy. Thus, a lot of 3-Polker coins (e.g., Sigismund-III-type) were forged, and the markets became flooded with poor currency. In the present day, these pre-modern forgeries are rare archeological findings. Only five forged 3-Polker coins randomly found in Transylvania were available for the current study. There are deeper implications of silver and tin in the forgery techniques that need to be considered. Thus, the forged 3-Polker coins were investigated via nondestructive methods: SEM microscopy coupled with EDS elemental spectroscopy for complex microstructural characterization and XRD for phase identification. Three distinct types of forgery methods were identified: the amalgam method is the first used for copper blank silvering (1620), and immersion in melted silver (1621) is the second one. Both methods were used to forge coins with proper legends and inscriptions. The third method is the tin plating of copper coins (with corrupted legend and altered design) (1622, 1623, and 1624). The EDS investigation revealed Hg traces inside the compact silver crusts for the first type and the elongated silver crystallites in the immersion direction, which are well-attached to the copper core for the second type. The third forgery type has a rich tin plating with the superficial formation of Cu₆Sn₅ compound that assures a good resistance of the coating layer. Therefore, this type should have been easily recognized as fake by traders, while the first two types require proper weighing and margin clipping to ensure their quality.

Methods for material investigation are powerful tools that allow specialists to elucidate important aspects regarding ancient artifacts such as the Roman amphorae deposits discovered at Potaissa Fortress in Turda, Romania. Archeological debate states that the deposit contained olive oil and wine amphorae, but no material evidence has been presented until now. The current research is focused on the most representative large amphora fragments found in the Potaissa deposit, with a significant amount of sediment on their walls, to give archeologists the material proof to elucidate their debate. Sediment was collected from each fragment and subjected to complex analysis. XRD investigation combined with cross-polarized light microscopy demonstrated mineral particles such as quartz, clay (muscovite and traces of biotite), and calcite. Quartz and calcite particles have a rounded shape and diameters in a range of 20–200 µm, and clay particles have a lamellar shape and dimensions from 1 to 20 µm, a fact confirmed by SEM microscopy. Sample 2 presented a large amount of amorphous phase followed by Samples 1 and 3, with a low amount of organic phase. FTIR investigation confirms organic phase presence owing to strong absorption bands regarding C-H, C=O, and O-H chemical bonds related to aliphatic compounds in Sample 2, and to some decayed wine residue in Samples 1 and 3. EDS elemental analysis was used for organic particle identification in the amphora sediments and to obtain a correlation with their microstructure. GC–MS investigation showed volatile compounds related to wine residue for Samples 1 and 3 and decomposed fats for Sample 2. Tartaric and malic acid were identified by HPLC in Samples 1 and 3, which are wine biomarkers. The correlation of all experimental results concludes with no doubt that Amphora 2 contained olive oil and Amphorae 1 and 3 contained wine in ancient times.

Saxony was ruled by two cousins in 1544: John Frederick I (Elector of Saxony) and his cousin Maurice (Duke of Saxony). Both rulers’ names appear on each side of the quarter thalers produced in this year. They were enemies involved in religious wars, although they were both Protestants. Two types of quarter thalers from 1544 occur: a pierced random find from Transylvania (Romania) with four shields on the reverse, heavily worn, and another one with three shields on the obverse side, found in the Głogów Hoard (Poland), which is well preserved. Why did they issue two types in the same year? Was it a matter of silver title or other historical factors? Nondestructive investigation methods were used: XRD revealed the phases within the alloy and patina layer; SEM-EDS revealed the morphological aspects and their elemental compositions, which were correlated with XRF results. The results show that both coins have closer silver amounts, from 91 to 96 wt.%. The EDS results were in good agreement with the XRF results. Lead traces indicated a difference between them: the four-shielded coin is lead-free, while the three-shielded coin has a moderate amount of lead, about 0.5 wt.%. The archeological data evidence that the four-shielded coin issued in 1544 is rarer than the three-shielded one because it was issued during specific historical conditions. Black patina is formed by a mixture rich in copper oxides mixed with silver oxides and Ag₂S. The presence of silver sulfide in the patina layer confirms that the pierced coin was in prolonged contact with the skin surface. Also, the finest traces of minerals embedded in the patina layer (e.g., quartz, kaolinite, and calcite) suggest that they were embedded in the patina via prolonged exposure to particulate matter. The mineral inclusions in the patina would have been more numerous if they were formed underground. Thus, the pierced four-shielded coin was probably worn as jewelry by nomads, while the three-shielded coin was most likely treasured in a well-preserved hoard.

Nanomaterials are usually associated with modern technologies and advanced processing methods. Three silver Dacian bracelets within Cehei hoard (Salaj County, Romania) are tougher than they should be according to the apparently higher silver content. The microstructural investigation reveals that all three bracelets have silver content of about 90 wt.%. The metallographic inspection of a bracelet sample reveals a very refined microstructure of α grain while fewer eutectic grains are almost undetectable, indicating intensive plastic deformation. XRD patterns of the bracelets reveal relevant peaks for silver (without copper) having a much-broadened aspect indicating nanostructural level. The nano-grains were evidenced at high magnification of SEM imaging: 55 nm for bracelet 1, 95 nm for bracelet 2 and 75 nm for bracelet 3. Elemental maps reveal that the nanograins are basically formed by α phase; the finest eutectic traces are situated and uniformly dispersed within α phase, appearing as small red spots. Vickers µHV10 micro indentation was calibrated on a pure silver 999.9 ‰ in annealed state, resulting in 37 HV10. The nanostructured bracelets have about 56 µHV10 for bracelet 1; 50 µHV10 for bracelet 2 and 52 µHV10 for bracelet 3. Dyrrachium drachmas have Vickers microhardness of about 37 µHV10. The obtained results confirm the historian’s supposition that Dyrrachium drachmas could be the source for silver but also clearly indicate that the final steps of bracelets manufacturing were effectuated by cold deformation with intensive cold hardening. It results that cold deformation of the bracelets rods induces a nanostructural state that significantly increases their microhardness instead of their higher silver title.

At the beginning of the reign of Louis I of Anjou, King of Hungary (1342–1382), various types of currency were introduced, undergoing repeated devaluations until 1360. According to Lajos Huszár, denarii of the Saint Ladislas type were issued in 1358–1371, with a fineness of approximately 0.93, whereas Saracen Head denarii were assigned to 1373–1382 and described as being of lower fineness. Recently, Csaba Tóth claimed that the Saracen’s Head Denarii were issued in the middle of the reign of Louis I, and the last types of denarii were those with the representation of Saint Ladislas. A recent archeological find from Transylvania (Romania) contains 3 intact Saracen Head denarii and 12 fragments and only 3 fragments of Saint Ladislas denarii. The significant number of fragments facilitates advanced microstructural investigations of the bulk alloy, including XRD correlated with SEM microscopy and EDS elemental spectroscopy. It results in a silver content of about 89.15 ± 0.93 wt.% for Saracen Head denarii, while Saint Ladislas ones have a significantly decreased fineness of 81.75 ± 2.54 wt.%. These values support the newest chronology discussed in the literature, placing the Saracen Head denarii in the middle of Louis I of Anjou reign, while the Saint Ladislas type belongs to the latest part of the reign. Patina layers were investigated regarding the resting ground, which contains quartz, clays (kaolinite and muscovite mixture), and calcite. Thus, the oxidized layer formed directly on the metallic surface is dominated by copper oxides, which further interact with the calcium carbonate from the soil generating a green layer of malachite. This layered corrosion extracts copper from the outermost layers, causing significant silver enrichment of the coin’s surface of about 97 wt.%, which affect nondestructive investigations. The slight micro-incision of the fragment’s sides enabled accurate measurement of the silver fineness despite the presence of corrosion features. Such an approach could be applied for evaluation of other coins’ fineness performing the micro-abrasion on their edges, allowing for SEM-EDS measurements while preserving the visual integrity of coins.