Bamboo grid packing (BGP) is a new kind of cooling packing, used in some Chinese hyperbolic cooling towers, which has excellent potential to complement or replace cooling packing made of polyvinyl chloride (PVC), cement, and glass fiber-reinforced plastic. For bamboo applications, mechanical properties and service life are matters of concern; this is strongly associated with bamboo’s chemical composition and mass loss. To better understand the mechanics of mechanical property deterioration and service life reduction, this study investigated the effects of hygrothermal environments in cooling towers on the chemical and elemental composition, mass loss, Fourier-transform infrared (FTIR) spectrum, and color changes of BGP. The results showed that BGP that had been in service for nine years in cooling towers exhibited major decreases in content of hemicellulose and benzene-ethanol extractives, as well as a significant increases in the content of α-cellulose and lignin. Exposure to the hygrothermal environment led to a decrease of oxygen content and around 8% mass loss, as well as an increase in carbon content compared to control samples. The hot water flow in cooling towers not only hydrolyzed hemicellulose, but also degraded some functional groups in cellulose and lignin. The lightness (L*) and chromaticity (a* and b*) parameters of the used BGP all decreased, except for the a* value of the outer skin. The total color change (ΔE*) of the inner skin of used BGP exceeded that of the outer skin.

Chinese fir (Cunninghamia lanceolata (Lamb.) Hook.) has been an important afforestation species in northeast China. It has obvious defects of buckling and cracking easily, which are caused by its chemical components. Trametes versicolor (L.) Lloyd, a white-rot fungus, can decompose the cellulose, hemicellulose, and lignin in the wood. White-rot fungus was used to biologically degrade Chinese fir wood. The effects of different degradation time on the Chinese fir wood’s mechanical properties, micromorphology, chemical components, and crystallinity were studied. The results showed that the heartwood of Chinese fir was more durable than the sapwood and the durability class of Chinese fir was III. Trametes versicolor (L.) Lloyd had a greater influence on the mechanical properties (especially with respect to the modulus of elasticity (MOE)) for the sapwood. Trametes versicolor (L.) Lloyd degraded Chinese fir and colonized the lumen of various wood cell types in Chinese fir, penetrated cell walls via pits, caused erosion troughs and bore holes, and removed all cell layers. The ability of white-rot fungus to change the chemical composition mass fraction for Chinese fir was: hemicellulose > lignin > cellulose. The durability of the chemical compositions was: lignin > cellulose > hemicellulose. The crystallinity of the cellulose decreased and the mean size of the ordered (crystalline) domains increased after being treated by white-rot fungus.

Bamboo is a natural material widely used in buildings and bridges that has good mechanical properties. However, the longitudinal connection of bamboo culms is a major problem for the bamboo industry. In this study, sleeve-nailed bamboo specimens were produced, which contained three bamboo pieces. Two bamboo pieces with similar diameters were longitudinally joined by inserting a short bamboo culm with a smaller diameter, fixed with nails. The flexural performance of single beams and two-culm beams were studied. The load-displacement curves and fracture behavior of the specimens were investigated. The results show that the flexural bearing capacity of the single connected bamboo specimen was relatively smaller than that of an unconnected one, while the flexural bearing capacity of the two-culm beam was improved significantly. It can be seen that the lateral connection of bamboo specimens can improve the bearing capacity of the combined bamboo culms. This study provides a basis for promoting the application of sleeve-type nailed connections for bamboo.

Due to its advantages of good heat-resistance, environmental-friendliness, and low cost, bamboo grid packing (BGP) has become a promising new type of cooling packing. It is being increasingly used in Chinese industrial cooling towers to replace cooling packings made of polyvinyl chloride, cement, and glass fiber reinforced plastic. However, mechanical properties and fungal resistance are a concern for all bamboo applications. In this study, the modulus of rupture (MOR), modulus of elasticity (MOE), density, crystallinity, and environment scanning electron microscope (ESEM) properties were compared between fresh BGPs and those that had been in service for nine years in the cooling towers. The results showed that the MOR, MOE, density, crystallinity, and the crystal size of the used BGPs decreased to some extent, but still met the requirements for normal use in a cooling tower. The ESEM observation showed that the used BGPs were not infected by fungi. The decrease in mechanical properties could be caused by the decrease of density, crystallinity, and the decomposition of the chemical components of bamboo, but not by fungal infection.