The formation of a columnar grain structure in high chromium nickel based alloy welds can be associated with cracking and poor resolution for ultrasonic non-destructive examination. The objective of this research was to characterise the effects of circular magnetic arc deflection (arc stirring) on grain structure of gas tungsten arc weld overlays made on Inconel 690 substrates with 52M filler wire. Welds and weld overlays were made at various arc stirring frequencies, and microstructures were analysed using optical and electron backscattered diffraction microscopy. Significant refinement of grain size occurred at a stirring frequency of 7 Hz. Ultrasonic non-destructive examination confirmed 100% improvement in signal/noise ratio in weld overlays made with magnetic stirring.

Traditional spot welds and magnetically assisted spot welds were made in 2.25 mm thick galvanised dual-phase steel, and the weld microstructures were compared. The magnetically assisted weld nugget had a ‘dog bone’ shape, and it had an increased diameter, which indicates a larger load-bearing area that will improve mechanical performance. The fusion zone of the magnetically assisted welds had a finer and less-directional grain structure than the conventional welds, which would improve weld strength, plastic strains, and ductility. Both types of welds contained an unusual soft zone very close to the fusion zone that is thought to be an integral part of the fusion zone. The soft zone of the magnetically assisted welds was wider than the conventional welds.