This article presents a comprehensive study on the physical, mechanical, thermal, and chemical properties of polypropylene (PP) composites reinforced with hemp fibers (HF) and compatibilized with maleic anhydride (MAPP). The composites were processed using a twin-screw extruder, followed by hot compression at 190 °C. Subsequently, the composites were analyzed using Izod impact and Shore D hardness tests to evaluate their mechanical properties. Thermal properties were investigated through differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA), while X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR) were employed to study their chemical properties. Additionally, a statistical analysis was conducted to compare the average results of the impact and hardness tests. XRD analysis revealed that the addition of HF and MAPP led to the disappearance of peaks corresponding to the beta phase in pure PP. Hemp fibers exhibited an impressive crystallinity of 82.10%, surpassing other natural fibers, and had a significant molecular orientation angle (MFA) of 6.06°, making them highly desirable for engineering applications. The crystallite size was observed to be relatively large, at 32.49 nm. FTIR analysis demonstrated strong interactions between the fiber, compatibilizing agent, and polymer matrix. TGA tests showed that the addition of 5 and 10 wt.% MAPP resulted in complete degradation of the composites, similar to pure PP. DSC analyses indicated a reduction in crystallinity (X_c) due to the incorporation of HF and MAPP. Shore D hardness tests revealed an increase in hardness with the addition of 5 wt.% MAPP, while a steep decline in this property was observed with 10 wt.% MAPP. In terms of impact resistance, fractions of 3 and 5 wt.% MAPP in the composites exhibited improved performance compared to the pure polymer. Analysis of variance (ANOVA) was employed to ensure the statistical reliability of the mechanical test results. This comprehensive study sheds light on the diverse properties of PP composites reinforced with hemp fibers and compatibilized with MAPP, emphasizing their potential as sustainable materials for engineering applications. The results contribute to the understanding of the structural and functional aspects of these composites, guiding future research and developments in the field.

A preocupação crescente acerca da sustentabilidade associa-se à produção de materiais que sejam mais sustentáveis, impulsionando o interesse por compósitos poliméricos que não degradem o meio ambiente. Deste modo, o objetivo deste trabalho foi realizar a preparação e caracterização de compósitos sustentáveis à base de polipropileno reciclado (PPr) e fibra de sisal em proporções de 10, 20 e 30%. Foram realizadas análises de densidade, dureza e absorção de água nas quais os compósitos formados foram processados por extrusão e moldados por compressão. Os resultados obtidos demonstraram que a adição da fibra natural promoveu uma redução nas propriedades de densidade e dureza dos materiais. A adição da carga fibrosa aumentou significativamente a absorção de água dos compósitos formados.

In this work, graphene oxide (GO) was first obtained by chemical exfoliation. Then it was melted by hot compression with polypropylene grafted with maleic anhydride (PP-g-MA). The PP-g-MA/GO (1% and 3% GO wt.%) were applied to prepare polypropylene/PP-g-MA/GO nanocomposites by extrusion. Pelletized samples obtained by extrusion were stamped from plates obtained by compression in a bench press and these materials were characterized through FTIR and tensile tests. The GO was also characterized by Raman spectroscopy, X-ray diffraction and FTIR. The results indicated that GO acted as a plasticizer, reducing the mechanical property values in comparison with pure polypropylene.

A crescente preocupação ambiental na sociedade impulsiona pesquisas para substituir materiais existentes por alternativas mais sustentáveis. Nesse contexto, as fibras naturais se destacam como excelentes opções para reforçar compósitos de matriz polimérica. Além disso, a argila é um material natural abundante e com granulometria interessante, tornando-a atraente para estudos. O objetivo deste trabalho foi de desenvolver compósitos de matriz polimérica reciclada reforçados com fibra de sisal e argila, avaliando suas propriedades mecânica, morfológica, térmica e estrutural. Foram produzidos compósitos de PP reciclado, fibra de sisal e bentonita organofílica pelo método de intercalação por fusão. O ter de fibra de sisal empregado nos compósitos foi de 20% e o de argila variou em 5, 10 e 15 % em massa. Verificou-se uma redução da resistência ao impacto dos materiais obtidos em relação a matriz pura. A análise de MEV demonstrou que ocorreu mudança na microestrutura do polipropileno reciclado com a adição da fibra natural e da argila. Os resultados de VICAT mostraram uma redução na estabilidade térmica dos materiais. A técnica de DRX revelou que a presença da fibra e da argila não modificou a estrutura cristalina da matriz polimérica.

O polietileno de alta densidade (PEAD) e o polipropileno (PP) estão entre os polímeros mais consumidos em escala mundial. Essas poliolefinas, são uns dos principais constituintes dos resíduos sólidos urbanos. O descarte intensivo desses materiais torna a reciclagem cada vez mais importante. No setor polimérico, as blendas surgiram como uma alternativa atraente para o desenvolvimento tecnológico, permitindo combinar propriedades de diferentes polímeros em um curto prazo de desenvolvimento. Além disso, a utilização do PEAD e PP reciclado em blendas é uma saída para a diminuição do descarte no meio ambiente. No presente trabalho foram preparadas blendas de PEAD e PP reciclados visando avaliar o efeito de dois compatibilizantes diferentes nas propriedades estrutural e térmicas do material. A análise de FTIR revelou a ausência de interação química entre os polímeros. As análises de DSC e TGA mostraram que a adição dos diferentes agentes de compatibilização não influenciou de forma significativa as propriedades térmicas das blendas.

Este artigo apresenta um estudo sobre as propriedades físico-mecânicas de blendas de Polietileno de alta densidade reciclado (PEADr) e Polipropileno reciclado (PPr) reforçados com argila bentonita (bento). As blendas foram processadas ​​em extrusora dupla-rosca, seguida de compressão a quente a 190°C. Posteriormente, as blendas foram analisadas ​​por meio de ensaios de densidade, MFI, Dureza Shore D, Impacto Izod e Temperatura de Deflexão Térmica (HDT) para avaliar suas propriedades físico-mecânicas. A adição de argila promoveu uma tendência de aumento na densidade e MFI das blendas, a temperatura de deflexão térmica das blendas se manteve similar a blenda sem argila e houve uma diminuição na resistência ao impacto das blendas avaliadas. Desse modo concluiu-se que a adição de argila pode resultar em interfaces fracas e aglomeração de partículas acarretando o declínio das propriedades.