Through nanoscratch experiments with a spherical diamond indenter, a contrastive study of the nanotribological properties of Ga- and N-faced gallium nitride (GaN) samples was carried out. Nanoindentation results revealed that the elastic modulus of the Ga-faced GaN sample was slightly higher than that of N-faced GaN sample. Particularly, Ga- and N-faced GaN samples exhibited rather different nanotribological properties, and the Ga-faced sample showed a stronger wear resistance. The study indicated that the critical normal load required to cause material removal of N-faced GaN sample was almost two times that of Ga-faced GaN sample. Both Ga- and N-faces exhibited a rather low frictional coefficient at the elastic and elastoplastic stages of material, e.g., ~0.06 for Ga-face and ~0.075 for N-face when scratching under the progressive normal load. Combined with transmission electron microscopy and X-ray photoelectron spectroscopy, we speculated that, except for the intrinsic atomic arrangements attributed to the non-reverse crystallographic symmetry of c-plane wurtzite GaN, the difference of nanotribological properties between Ga- and N-faces may also be related to the preferential formation of a native oxide layer and a slight lattice damage layer on the N-faced GaN surface. This study can enrich the understanding of the nanotribological properties of Ga- and N-polar-faced bulk monocrystalline GaN materials fabricated by the conventional technique.

An Al₂O₃–TiO₂ amorphous composite coating with a thickness of 100–120 μm was fabricated on China low activation martensitic steel (CLAM steel) by oxygen acetylene flame spraying technology and the laser in-situ reaction method. We investigated the microstructures and mechanical properties of the coating after liquid lead-bismuth eutectic (LBE) alloy corrosion under different temperatures for 300 h and found that the corrosion temperature of the LBE had no observable effect on the microstructure and chemical phase of the Al₂O₃–TiO₂ amorphous composite coatings. However, the mechanical properties (micro-hardness and shear strength) of the Al₂O₃–TiO₂ multiphase coating deteriorated slightly with the increase in the immersion temperature of the LBE. As a result of oxygen acetylene flame spraying and laser in-situ reaction technology, it was found that the Al₂O₃–TiO₂ amorphous composite coating exhibits an excellent LBE corrosion resistance, which is a candidate structural material for the accelerator-driven subcritical system (ADS) to handle nuclear waste under extreme conditions.