Concrete production causes significant environmental damage during its entire life cycle due to the large consumption of natural aggregate. The aim of this research was to use the Life Cycle Assessment (LCA) methodology to conduct a comparative analysis of four different concrete mixtures, i.e., construction and demolition waste (CDW), incinerator ashes, marble sludge, and blast furnace slag. The LCA study was implemented in the Campania Region of Italy. The main contribution of the study was that it proposed the use of “green” recycled aggregates in concrete production in order to assess the reduction of potential adverse impacts, from both environmental and energy perspectives. SimaPro^© software was used to conduct the analysis. The main results of the research showed that the recycled aggregates that were analyzed were preferable to traditional concrete. In particular, the recycled aggregate that had the least adverse impact on the environment was blast furnace waste.

This paper highlights the multi-material additive manufacturing (AM) route for manufacturing of innovative materials and structures. Three different recycled thermoplastics, namely acrylonitrile butadiene styrene (ABS), polylactic acid (PLA), and high impact polystyrene (HIPS) (with different Young’s modulus, glass transition temperature, rheological properties), have been selected (as a case study) for multi-material AM. The functional prototypes have been printed on fused deposition modelling (FDM) setup as tensile specimens (as per ASTM D638 type-IV standard) with different combinations of top, middle, and bottom layers (of ABS/PLA/HIPS), at different printing speed and infill percentage density. The specimens were subjected to thermal (glass transition temperature and heat capacity) and mechanical testing (peak load, peak strength, peak elongation, percentage elongation at peak, and Young’s modulus) to ascertain their suitability in load-bearing structures, and the fabrication of functional prototypes of mechanical meta-materials. The results have been supported by photomicrographs to observe the microstructure of the analyzed multi-materials.