Plasma electrolytic oxidation (PEO) coating was obtained on AZ31 Mg alloy using a direct current in a sodium silicate-based electrolyte with and without a carbon nanotube (CNT) additive. The surface morphology and phase composition of the PEO coatings were investigated through field emission scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The corrosion-resistance properties of the PEO coatings were evaluated using potentiodynamic polarization measurements and electrochemical impedance spectroscopy (EIS) in a 3.5 wt.% NaCl solution. Furthermore, the heat-dissipation property was evaluated by a heat-flux measurement setup using a modified steady-state method and Fourier transform infrared spectroscopy (FT-IR). The results demonstrate that, by increasing the concentration of CNT additive in the electrolyte, the micropores and cracks of the PEO coatings are greatly decreased. In addition, the anticorrosion performance of the PEO coatings that incorporated CNT for the protection of the Mg substrate was improved. Finally, the coating’s heat-dissipation property was improved by the incorporation of CNT with high thermal conductivity and high thermal emissivity.
7 January 2019 in Anti-Corrosion Methods and Materials
Purpose: The secondary phase decreased the corrosion resistance because of the segregation of Cr and Mo. Therefore, this paper aims to study the precipitation condition and the effect of secondary phase with volume fraction on corrosion behavior. Design/methodology/approach: Secondary phase precipitated approximately from 375°C to 975°C because of saturated Cr and Mo at grain boundary by growth of austenite. Therefore, heat treatment from 800°C to 1,300°C was applied to start the precipitation of the secondary phase. Findings: The secondary phase is precipitated at 1,020°C because of segregation by heterogeneous austenite. The growth of austenite at 1,000°C needs the time to saturate the Cr and Mo at grain boundary. When the volume fraction of austenite is 56 per cent (14 min at 1,000°C), the secondary phase is precipitated with grain boundary of austenite. The secondary phase increased the current density (corrosion rate) and decreased the passivation. That is checked to the critical pitting temperature (CPT) curves. The 1 per cent volume fraction of secondary phase decreased CPT to 60°C from 71°C. Research limitations/implications: The precipitation of secondary phase not wants anyone. Casted super-duplex stainless steel (SDSS) of big size precipitates the secondary phase. This study worked the precipitation condition and the suppression conditions of secondary phase. Social implications: Manufacturers need precipitation condition to make high-performance SDSS. Originality/value: The corrosion resistance of SDSS is hard the optimization because SDSS is dual-phase stainless steel. The precipitation of the secondary phase must be controlled to optimize of the corrosion resistance of SDSS. Anyone not studied the precipitation condition of secondary phase and the effect of secondary phase with volume fraction on corrosion behavior of SDSS.