Nowadays, luminescent materials attract wide attention due to their valuable characteristics and broad area of potential application. Luminescent silicone-based polymers possess unique properties, such as flexibility, hydrophobicity, thermal and chemical stabilities, etc., which allow them to be utilized in various fields, such as optoelectronics, solid-state lasers, luminescent solar concentrators, sensors, and others. In the present work, a metal-ligand interaction approach was applied to obtain new cross-linked luminescent polymers based on multiligand polysiloxanes with grafted β-diketone fragments and organoeuropiumsiloxanes containing various organic substituents. Organoeuropiumsiloxanes were utilized as a source of Eu³⁺ ions due to their compatibility with the silicon matrix. All synthesized polymers were fully characterized and their physicochemical, mechanical, self-healing, optical, and thermal properties were studied.

A series of aromatic polyimides based on the asymmetrical diamine 3,4ʹ-oxydianiline and various tetracarboxylic acid dianhydrides, both “rigid” and “flexible” structure, have been synthesized using the original method of one-pot high-temperature catalytic polycondensation in molten benzoic acid. The synthesized polyimides were investigated using fourier-transform infrared (FTIR) and ¹H NMR spectroscopy, gel permeation chromatography (GPC), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), thermomechanical analysis (TMA) and wide-angle X-ray scattering (WAXS). It was found that the synthesized polyimides, depending on the used dianhydride, are characterized by different solubility in organic solvent and molten benzoic acid, molecular weight, glass transition temperature (Tg) from 198 to 270 °C, an amorphous or semi crystalline structure with the degree of crystallinity from 41 to 52%. The influence of the method of synthesis on the formation of the crystalline phase of polyimides was studied, and the obtained results were compared with the literature data. The effect of dianhydride chemical structure on the performance of polyimide in pervaporation more specifically, dehydratation of azeotropic isopropanol solution was investigated and compared with the commercially available polyetherimide Ultem 1000™. Membrane structure was studied using scanning electron microscopy. It was found that polyimide PI-DA is the most effective for separation of 88 wt.% isopropanol/12 wt.% water mixture compared to the polyimide PI-6FDA and commercial polyetherimide Ultem 1000™ demonstrating normalized permeation flux of 2.77 kg µm m⁻² h⁻¹ and separation factor of 264 (water content in permeate 97 wt.%).

A method for the preparation of polydimethylsiloxanes with grafted methoxy-substituted dibenzoylmethanatoboron difluoride has been described. The structures of prepared polymers were confirmed using NMR, IR spectroscopy and gel permeation chromatography methods. Their thermal properties were investigated using thermal gravimetric analysis, differential scanning calorimetry and thermomechanical analysis. The prepared polymers had good thermal (T_d^5% up to 393 °C) and thermo-oxidative (T_d^5% = 413 °C) stability. The polymers started to transit in a viscous flow state at about 40 °C (for 3 a) and at about 20 °C (for 3 b). The viscoelastic characteristics of prepared polymers were determined in the sinusoidal oscillating vibrations mode. It was shown that the studied polymers at low frequencies at room temperature are viscoelastic fluids (G′ < G″). Increasing the frequency led to inversion (crossover) of dependences G′ and G″, which indicated the transition of polymers from viscous to elastomeric behavior characteristics, and the beginning of the formation of a physical network. Optical properties were studied using electron absorption, steady-state and time-resolved fluorescence spectroscopy. It was shown that intramolecular H-dimers exist in the ground state. The polymers studied had a bright fluorescence in the solution and in the solid state, consisting of bands of monomer and excimer emission. Thermally-activated delayed fluorescence was observed in the solution and the solid state. The prepared polymers possess intriguing properties that make them useful as optical materials, sensors or imaging agents.

The development of photocurable compositions is in high demand for the manufacture of functional materials for electronics, optics, medicine, energy, etc. The properties of the final photo-cured material are primarily determined by the initial mixture, which needs to be tuned for each application. In this study we propose to use simple systems based on di(meth)acrylate, polyimide and photoinitiator for the preparation of new photo-curable compositions. It was established that a fluorinated cardo copolyimide (FCPI) based on 2,2-bis-(3,4-dicarboxydiphenyl)hexafluoropropane dianhydride, 9,9-bis-(4-aminophenyl)fluorene and 2,2-bis-(4-aminophenyl)hexafluoropropane (1.00:0.75:0.25 mol) has excellent solubility in di(met)acrylates. This made it possible to prepare solutions of FCPI in such monomers, to study the effect of FCPI on the kinetics of their photopolymerization in situ and the properties of the resulting polymers. According to the obtained data, the solutions of FCPI (23 wt.%) in 1,4-butanediol diacrylate (BDDA) and FCPI (15 wt.%) in tetraethylene glycol diacrylate were tested for the formation of the primary protective coatings of the silica optical fibers. It was found that the new coating of poly(BDDA–FCPI_23%) can withstand prolonged annealing at 200 °C (72 h), which is comparable or superior to the known most thermally stable photo-curable coatings. The proposed approach can be applied to obtain other functional materials.

Owing to their outstanding thermal and mechanical properties, polyimides (PIs), polyamides (PAs), and poly(amide-imides) (PAIs) are essential for developing and manufacturing modern high-tech products, including electroactive ones. Despite their large-scale production for diverse applications, the synthesis of these polymers traditionally relies on highly toxic solvents such as N,N-dimethylacetamide, N,N-dimethylformamide, N-methyl-2-pyrrolidone (NMP), and m-cresol. This work investigates the possibility of replacing these hazardous solvents with a more sustainable and “green” alternative, N-butyl-2-pyrrolidone (NBP). We have thoroughly studied and analyzed the synthesis of various PIs, PAs, and PAIs via one- and two-step polycondensation of tetracarboxylic acid dianhydrides with diamines, low-temperature polycondensation of terephthaloyl chloride with diamines, and low-temperature polycondensation of tetracarboxylic acid dianhydrides and terephthaloyl chloride with diamines, respectively. Our results demonstrate that substituting NBP for NMP presents distinct characteristics and outcomes for each process. By optimizing the reaction conditions, we were able to obtain high-molecular-weight products (M_n = 37–346 kDa; M_w = 133–537 kDa) for all polymer classes studied. Thus, this work establishes NBP as a suitable and promising solvent for synthesizing PIs, PAs, and PAIs with diverse chemical structures and tunable molecular weight characteristics.

Development of new microporous organic polymers attracts significant attention due to a wide scope of promising applications. In addition, the synthesis of soluble, non-crosslinking polymers of high surface area and uniform microporosity is very challenging, and the methods for soluble microporous polymers formation are rather limited. In this work, we report a new approach to construct porous polyphenylenes which employs the Diels–Alder polycondensation of multifunctional ethynyl-containing monomers of different spatial architecture with bis(cyclopentadienone)s. The resulting polymers were soluble in common organic solvents, and their structure and properties were assessed by NMR, TGA, DSC, and SEC studies. The polymers demonstrated a specific surface area up to 751 m²·g⁻¹ and ultramicroporous (pore size ≤ 0.6 nm) structure. N₂ and CO₂ adsorption–desorption data revealed that porosity parameters, e.g., specific surface area and pore sizes, can be tuned selectively by varying the type of monomers and reaction conditions.