The main differences in the transient zone extent between the individual strands for the former industrial six-strand tundish configuration is the basis for undertaking this study. The aim this study was to improve the casting conditions by proposing the optimal equipment of the tundish working space. For economic reasons, only the variants with different baffles configurations were considered. It was also dictated by the simplicity of construction and the possibility of its implementation by the base operating steel mill. In the current study, industrial plant measurements and mathematical modeling were used. Industrial experimental data were used to diagnose the current state of the industrial tundish and then validate the numerical simulations. After this, the influence of different baffle configurations installed in the tundish on the steel flow characteristic was modeled mathematically. Residence time distribution (RTD) curves are plotted, and individual flow shares for the investigated tundish were estimated based on the curves. Finally, the industrial plant was rebuilt according to the numerical results and additional plant measurements were performed. A result of the appearance of the baffles in the tundish working space was the reduction of the transient zone extent. The results indicate the increasing share of the dispersed plug flow and a decreasing share of the dead volume flow, with a practically unchanging share of well-mixed volume flow in the modified tundish.

The refining process is one of the essential stages of aluminum production. Its main aim is to remove hydrogen, that causes porosity and weakens the mechanical and physical properties of casting aluminum. The process is mainly conducted by purging inert gas through the liquid metal, using rotary impellers. The geometry of the impellers and the processing parameters, such as flow rate of gas and rotary impeller speed, influence the gas dispersion level, and therefore the efficiency of the process. Improving the process, and optimization of parameters, can be done by physical modelling. In this paper, the research was carried out with the use of a water model of batch reactor, testing three different rotary impellers. Varied methods were used: visualization, which can help to evaluate the level of dispersion of gas bubbles in liquid metal; determination of residence time distribution (RTD) curves, which was obtained by measuring the conductivity of NaCl tracer in the fluid; and indirect studies, completed by measuring the content of dissolved oxygen in water to simulate hydrogen desorption. The research was carried out for different processing parameters, such as flow rate of refining gas (5–25 L·min⁻¹) and rotary impeller speed (3.33–8.33 s⁻¹). The obtained results were presented graphically and discussed in detail.

This paper deals with the possibilities of using physical modelling to study the slag entrainment in the tundish. A level of steel in the tundish is changing during sequential continuous casting. The most significant decrease in the steel level occurs when replacing ladles. It is generally known that if the height of steel level in the tundish drops below a certain critical level, it may generate vortexes over the nozzles and as a consequence entrainment of tundish slag into individual casting strands can occur. Thus, it is necessary to identify the critical level of steel for specific operational conditions. In this paper, the development of physical modelling methodology is described as well as physical model corresponding to operational continuous casting machine No. 2 in Třinecké železárny, a.s. The obtained results are discussed.