This paper presents the possibility of using the Spark Plasma Sintering (SPS) method to obtain WCCo composite materials. Such materials are used as cutting blades for machining wood-based materials. Two series of composites, different in grain size and cobalt content, were analyzed in the paper. The produced materials were characterized using Scanning Electron Microscopy (SEM), X-ray diffraction (XRD), and tribological properties were determined. In addition, preliminary tests were carried out on the durability of the blades made of sintered WCCo composites while machining three-layer chipboard. The results of the microstructure analysis proved that the SPS method makes it possible to obtain solid composites. Phase analysis showed the occurrence of the following phases: WC, Co, and Co₃W₉C₄. The lowest friction coefficient value was found in samples sintered using powder with an average primary particle size of 400 nm (ultrafine).

A highly effective method of the processing of steelmaking dust in an arc-resistant furnace has been presented. The aim of the research was to investigate the possibility of processing steelmaking dust in terms of waste minimization and selective recovery of valuable components. For this purpose, an electric arc resistance furnace was used. Granulated steelmaking dust with reducer (coal dust) was the input material. The products of the process are zinc oxide, iron alloy and slag, with properties meeting high ecological requirements. The technology does not generate solid waste. Zinc recovery is over 99% and iron recovery over 98%. The content of heavy metals (Zn + Pb + Cu) in glassy slag is below 0.2%, which ensures very low leachability.

Metal products for the metallurgical and machinery industries must meet high requirements in terms of their performance, including reliability, accuracy, durability and fatigue strength. It is also important that materials commonly used to manufacture such products must meet specific requirements. Therefore, various techniques and technologies for modifying the surface layer are becoming more and more widely used. These include burnishing, which may be dynamic or static. This article studies the process of slide burnishing of surfaces of cylindrical objects. The burnishing was performed using a slide burnisher with a rigid diamond-tipped clamp on a general-purpose lathe. The tests were performed for corrosion-resistant steel X2CrNiMo17-12-2. The aim of the research was to determine the impact of changes in burnishing conditions and parameters—feed rate, burnisher depth and burnishing force at a constant burnishing speed—on the surface roughness and hardness. Additionally, the microstructure was assessed in the critical areas: the surface and the core. Another phenomenon observed was surface cracking, which would be destructive due to the occurrence of indentation. In the paper, it was stated that the microstructure, or rather the grains, in the area of the surface layer was oriented in the direction of deformation. It was also observed that in the area of the surface layer, no cracks or other flaws were revealed. Therefore, slide burnishing not only reduces the surface roughness but hardens the surface layer of the burnished material.

This work aimed to assess the impact of acellularization and sterilization methods on the mechanical properties of biocomposites used as a skin substitute. On the basis of the statistical analysis, it was ascertained that the values of the Young modulus for the samples before the sterilization process—only in the cases of substances such as: trypsin, 15% glycerol and dispase—changed in a statistically significant way. In the case of dispase, the Young modulus value before the sterilization process amounted to 66.6 MPa, for trypsin this value equalled 33.9 MPa, whereas for 15% glycerol it was 11 MPa. In the case of samples after the completion of the sterilization process, the analysis did not show any statistically significant differences between the obtained results of Young’s modulus depending on the respective reagents applied. It was confirmed that different methods of acellularization and the process of sterilization effect the alteration of mechanical properties of allogeneic skins. In the case of the decellularization method using SDS (Sodium Dodecyl Sulfate), liquid nitrogen and 85% glycerol the highest values of strain were observed. In the authors’ opinion, it is the above-mentioned methods that should be recommended in the process of preparation of skin substitutes.