Poly(vinyl chloride) (PVC) is an important synthetic plastic that is produced in large quantities (millions of tons) annually. Additives to PVC are necessary to allow its use in many applications, particularly in harsh conditions. In regard to this, investigation of the synthesis of trimethoprim–tin complexes and their use as PVC additives is reported. Trimethoprim–tin complexes were obtained from the reaction of trimethoprim and tin chlorides using simple procedures. Trimethoprim–tin complexes (0.5% by weight) were added to PVC to produce homogenous mixtures and thin films were made. The effect of ultraviolet irradiation on the surface and properties of the PVC films was investigated. The level of both photodecomposition and photo-oxidation of PVC films containing trimethoprim–tin complexes was observed to be lower than for the blank film. The effectiveness of tin complexes as PVC photostabilizers reflects the aromaticity of the additives. The complex containing three phenyl groups attached to the tin cation showed the most stabilizing effect on PVC. The complex containing two phenyl groups was next, with the one containing butyl substituents resulting in the least stabilization of PVC. A number of mechanisms have been proposed to explain the role of the synthesized complexes in PVC photostabilization.

Tetra Schiff bases were used as thermal stabilizers to enhance the properties of polyvinyl chloride (PVC) when operated at high temperatures. The thermal stability of PVC films doped with Schiff bases was tested by the weight-loss method, Fourier transform infrared (FTIR) spectroscopy, thermal aging test, optical microscope, and atomic force microscope (AFM). Results showed that embedding these additives increased the stability time of the polymer, which decreased the degradation reaction tendency. Furthermore, the primary color of PVC was improved by adding the Schiff bases using oven-aging. In addition, these Schiff bases resulted in a significant reduction in PVC’s conjugated double bonds and, hence, the weight loss.

Poly(vinyl chloride) (PVC) undergoes photodegradation induced by ultraviolet (UV) irradiation; therefore, for outdoor applications, its photostability should be enhanced through the use of additives. Several carvedilol tin complexes were synthesized, characterized and mixed with PVC to produce thin films. These films were irradiated at 25 °C with a UV light (λ = 313 nm) for up to 300 h. The reduction in weight and changes in chemical structure and surface morphology of the PVC films were monitored. The films containing synthesized complexes showed less undesirable changes than the pure PVC film. Organotin with a high content of aromatics was particularly efficient in inhibiting photodegradation of PVC. The carvedilol tin complexes both absorbed UV light and scavenged radicals, hydrochloride, and peroxides and, therefore, photostabilized PVC.

Poly(vinyl chloride), PVC, has many attractive properties, including low cost of manufacture, resistance to acid and alkali corrosion, and ease of molding. However, PVC suffers from aging in harsh conditions, leading to the shortening of its useful life. Stability to irradiation, for example, can be improved through the incorporation of additives to PVC. The design, synthesis, and application of new stabilizers continue to attract attention. The current work investigates the effect of three tin–cephalexin complexes on the stability of PVC on irradiation with ultraviolet (UV) light (λ = 313 nm) at 25 °C for a long duration. The PVC was blended with tin–cephalexin complexes at low concentrations (0.5% by weight), and thin films (around 40 µm) were made from the mixed materials. Various methods, including weight loss, infrared spectroscopy, and surface inspection of irradiated films were used to investigate the role played by these additives in the inhibition of PVC photodecomposition. The results confirmed that the additives led to a significant reduction in the rate of photodecomposition of the PVC blends. Tin–cephalexin complexes can absorb harmful radiation, deactivate hydrogen chloride, and scavenge high-energy species such as peroxides, therefore acting as stabilizers for PVC.

Three organosilanes were synthesized in good yields from the condensation of 4,4′,4″-((phenylsilanetriyl)tris(oxy))tribenzaldehyde and 4-substituted anilines under acidic conditions. The structure of the organosilanes was confirmed using a variety of techniques. Organosilanes were mixed with poly(vinyl chloride) (PVC) and homogenous films were produced. The effect of long-term irradiation on the films containing organosilanes was tested using various methods. Monitoring the infrared spectra of PVC films before, during and after irradiation processes showed the formation of side products comprising polyene, carbonyl and hydroxyl groups. The intensities of absorption bands due to these functional groups were much lower in the presence of organosilanes as compared to the blank film. Also, the decrease in the weight and molecular weight of PVC films after irradiation was lower in the presence of organosilanes. Additionally, there was a minimal surface change of irradiated PVC in the presence of organosilanes. Clearly, organosilanes act as inhibitors, particularly the one containing the hydroxyl group, for the photodegradation of PVC. Different mechanisms were proposed to speculate the role played by organosilanes in stabilizing PVC against long-term ultraviolet light exposure.