Poly(vinyl chloride) (PVC), a polymer widely used in common household and industrial materials, undergoes photodegradation upon ultraviolet irradiation, leading to undesirable physicochemical properties and a reduced lifetime. In this study, four telmisartan organotin(IV) compounds were tested as photostabilizers against photodegradation. PVC films (40-µm thickness) containing these compounds (0.5 wt%) were irradiated with ultraviolet light at room temperature for up to 300 h. Changes in various polymeric parameters, including the growth of hydroxyl, carbonyl, and alkene functional groups, weight loss, reduction in molecular weight, and appearance of surface irregularities, were investigated to test the efficiency of the photostabilizers. The changes were more noticeable in the blank PVC film than in the films containing the telmisartan organotin(IV) compounds. These results reflect that these compounds effectively inhibit the photodegradation of PVC, possibly by acting as hydrogen chloride and radical scavengers, peroxide decomposers, and primary photostabilizers. The synthesized organotin(IV) complexes could be used as PVC additives to enhance photostability.

As poly(vinyl chloride) (PVC) photodegrades with long-term exposure to ultraviolet radiation, it is desirable to develop methods that enhance the photostability of PVC. In this study, new aromatic-rich diorganotin(IV) complexes were tested as photostabilizers in PVC films. The diorganotin(IV) complexes were synthesized in 79–86% yields by reacting excess naproxen with tin(IV) chlorides. PVC films containing 0.5 wt % diorganotin(IV) complexes were irradiated with ultraviolet light for up to 300 h, and changes within the films were monitored using the weight loss and the formation of specific functional groups (hydroxyl, carbonyl, and polyene). In addition, changes in the surface morphologies of the films were investigated. The diorganotin(IV) complexes enhanced the photostability of PVC, as the weight loss and surface roughness were much lower in the films with additives than in the blank film. Notably, the dimethyltin(IV) complex was the most efficient photostabilizer. The polymeric film containing this complex exhibited a morphology of regularly distributed hexagonal pores, with a honeycomb-like structure—possibly due to cross-linking and interactions between the additive and the polymeric chains. Various mechanisms, including direct absorption of ultraviolet irradiation, radical or hydrogen chloride scavenging, and polymer chain coordination, could explain how the diorganotin(IV) complexes stabilize PVC against photodegradation.

Novel, porous, highly aromatic organotin(IV) frameworks were successfully synthesized by the condensation of telmisartan and an appropriate tin(IV) chloride. The structures of the synthesized organotin(IV) complexes were elucidated by elemental analysis, ¹H-, ¹³C-, and ¹¹⁹Sn-NMR, and FTIR spectroscopy. The surface morphologies of the complexes were inspected by field emission scanning electron microscopy. The synthesized mesoporous organotin(IV) complexes have a Brunauer–Emmett–Teller (BET) surface area of 32.3–130.4 m²·g⁻¹, pore volume of 0.046–0.162 cm³·g⁻¹, and pore size of around 2.4 nm. The tin complexes containing a butyl substituent were more efficient as carbon dioxide storage media than the complexes containing a phenyl substituent. The dibutyltin(IV) complex had the highest BET surface area (S_BET = 130.357 m²·g⁻¹), the largest volume (0.162 cm³·g⁻¹), and was the most efficient for carbon dioxide storage (7.1 wt%) at a controlled temperature (323 K) and pressure (50 bars).

Tetra Schiff bases were used as thermal stabilizers to enhance the properties of polyvinyl chloride (PVC) when operated at high temperatures. The thermal stability of PVC films doped with Schiff bases was tested by the weight-loss method, Fourier transform infrared (FTIR) spectroscopy, thermal aging test, optical microscope, and atomic force microscope (AFM). Results showed that embedding these additives increased the stability time of the polymer, which decreased the degradation reaction tendency. Furthermore, the primary color of PVC was improved by adding the Schiff bases using oven-aging. In addition, these Schiff bases resulted in a significant reduction in PVC’s conjugated double bonds and, hence, the weight loss.

Poly(vinyl chloride), PVC, has many attractive properties, including low cost of manufacture, resistance to acid and alkali corrosion, and ease of molding. However, PVC suffers from aging in harsh conditions, leading to the shortening of its useful life. Stability to irradiation, for example, can be improved through the incorporation of additives to PVC. The design, synthesis, and application of new stabilizers continue to attract attention. The current work investigates the effect of three tin–cephalexin complexes on the stability of PVC on irradiation with ultraviolet (UV) light (λ = 313 nm) at 25 °C for a long duration. The PVC was blended with tin–cephalexin complexes at low concentrations (0.5% by weight), and thin films (around 40 µm) were made from the mixed materials. Various methods, including weight loss, infrared spectroscopy, and surface inspection of irradiated films were used to investigate the role played by these additives in the inhibition of PVC photodecomposition. The results confirmed that the additives led to a significant reduction in the rate of photodecomposition of the PVC blends. Tin–cephalexin complexes can absorb harmful radiation, deactivate hydrogen chloride, and scavenge high-energy species such as peroxides, therefore acting as stabilizers for PVC.