The high-temperature superplastic deformation behavior of rolled Mg-8Al-2Sn (AT82) and Mg-8Al-1Sn-1Zn (ATZ811) alloys were investigated in this study. During tensile deformation at 573 K, no obvious grain growth occurred in both alloys, because of the high-volume fraction of second phases located at grain boundaries. Meanwhile, texture weakening was observed, suggesting that grain boundary sliding (GBS) is the dominant superplastic deformation mechanism, which agreed well with the strain rate sensitivity (m) and the activation energy (Q) calculations. The microstructural evolution during tensile deformation manifested that there were more and larger cavities in AT82 than ATZ811 during high-temperature tensile deformation. Therefore, superior superplasticity was found in the ATZ811 alloy that presented a tensile elongation of ~510% under a strain rate of 10⁻³ s⁻¹ at 573 K, in contrast to the relatively inferior elongation of ~380% for the AT82 alloy. Meanwhile, good tensile properties at ambient temperature were also obtained in ATZ811 alloy, showing the ultimate tensile strength (UTS) of ~355 MPa, yield strength (YS) of ~250 MPa and elongation of ~18%. Excellent mechanical performance at both ambient and elevated temperatures can be realized by using economical elements and conventional rolling process, which is desirable for the industrial application of Mg alloy sheets.

In this work, the tensile deformation behavior of an as-extruded AZ80 magnesium alloy under pulsed current (PC) was investigated based on microstructure observations. We found that compared with the tensile tests at room temperature (RT) and given temperature (GT), the flow stress is reduced due to both thermal and athermal effects of pulsed current. A quasi-in-situ electron backscatter diffraction (EBSD) analysis reveals that at the same strain, the geometrically necessary dislocation (GND) density of the RT sample is the highest, followed by the GT sample and the PC sample. This proves that the athermal effect can promote the annihilation of dislocations and slow down dislocation pileup, which reduces the flow stress. In addition, the twinning behavior under different deformation conditions was studied; the twins are {10−12} tension twins, which are activated with the assistance of local stress. We found that the twin fraction in the PC sample is lower than that in the RT and GT samples, due to the least accumulation of GNDs at grain boundaries, which decreases the nucleation of {10−12} tension twins.

This study systematically investigates the microstructural characteristics and mechanical properties of resistance spot-welded joints in 3 mm thick non-heat-treatable die-cast AlSi₇MnMg alloy, with particular focus on the influence of element segregation and secondary phase behavior on fracture mechanisms and the process window. The results indicate that the weld nugget exhibits a typical dual structure consisting of columnar and equiaxed grain zones, with a corresponding “M”-shaped microhardness profile. Significant segregation of Si, Fe, and Mn elements at the nugget boundary was observed, leading to the formation of low-melting-point eutectic regions and secondary phase bands. These features induce microporosity along segregation trajectories, serving as crack initiation sites and resulting in a notably narrowed spot welding process window. From the perspective of microstructure and solute behavior during non-equilibrium solidification, this work elucidates the intrinsic mechanisms governing joint performance and process stability in non-heat-treatable die-cast aluminum alloys, providing a theoretical basis for their engineering applications.

In this study, laser oscillation welding was utilized to offer an effective solution for the joint welding of heat-treatment-free die-cast aluminum alloys, which expands the practical applications of automotive structural parts and heat sinks for electronic devices. The effects of oscillation amplitude on the macro-morphology, microstructure, and properties of the alloy weld were examined, and a molten pool flow model was developed to compare the behavior of the molten pool with and without oscillation. The results show that increasing the oscillation amplitude eliminates the coarse Al₁₅(Fe,Mn)₃Si₂ phase, resulting in a finer and more uniform distribution of the eutectic Si and Mg₂Si phases. At an oscillation amplitude of 7 mm, the maximum tensile shear load and displacement were 2761 N and 1.17 mm, respectively. Laser oscillation was found to enhance the fluidity of the molten pool, reduce porosity, improve weld quality, and effectively decrease cracks and inhomogeneous grain distribution. These findings provide a research basis for optimizing the laser oscillation welding process and for the practical welding of fabricated devices.