In this article, the effect of process parameters on the microstructure and mechanical properties of AW5083 aluminum alloy weld joints welded by a disk laser were studied. Butt welds were produced using 5087 (AlMg4.5MnZr) filler wire, with a diameter of 1.2 mm, and were protected from the ambient atmosphere by a mixture of argon and 30 vol.% of helium (Aluline He30). The widest weld joint (4.69 mm) and the highest tensile strength (309 MPa) were observed when a 30 L/min shielding gas flow rate was used. Conversely, the narrowest weld joint (4.15 mm) and the lowest tensile strength (160 MPa) were found when no shielding gas was used. The lowest average microhardness (55.4 HV0.1) was recorded when a 30 L/min shielding gas flow rate was used. The highest average microhardness (63.9 HV0.1) was observed when no shielding gas was used. In addition to the intermetallic compounds, β-Al₃Mg₂ and γ-Al₁₂Mg₁₇, in the inter-dendritic areas of the fusion zone (FZ), Al₄₉Mg₃₂, which has an irregular shape, was recorded. The application of the filler wire, which contains zirconium, resulted in grain refinement in the fusion zone. The protected weld joint was characterized by a ductile fracture in the base material (BM). A brittle fracture of the unshielded weld joint was caused by the presence of Al₂O₃ particles. The research results show that we achieved the optimal welding parameters, because no cracks and pores were present in the shielded weld metal (WM).

Sub-zero treatment of Vanadis 6 steel resulted in a considerable reduction of retained austenite amount, refinement of martensite, enhancement of population density of carbides, and modification of precipitation behaviour. Tempering of sub-zero-treated steel led to a decrease in population density of carbides, to a further reduction of retained austenite, and to precipitation of M₃C carbides, while M₇C₃ carbides precipitated only in the case of conventionally quenched steel. Complementary effects of these microstructural variations resulted in more noble behaviour of sub-zero-treated steel compared to the conventionally room-quenched one, and to clear inhibition of the corrosion rate at the same time.

Intergranular corrosion is one of the most important processes affecting the behaviour of austenitic stainless steels. Factors such as steel chemical composition, the degree of prior deformation and the exposure temperature affect the degree of sensitisation. AISI 316L (0% CW) steel was annealed at 650 °C for 5, 10, 30, 100, 300 and 1000 h to analyse the influence of isothermal annealing on the precipitation of secondary phases. AISI 316L steel after 40% cold working and subsequent annealing at 650 °C for 1, 1.5, 2, 5 and 10 h was investigated. Time–temperature sensitisation (TTS) diagrams were created based on corrosion test (ASTM A 262, practice A) results. In the case of AISI 316L (0% CW), M₂₃C₆, chi and sigma phases precipitated at grain boundaries, and the Laves phase was mainly inside of the grains. In the case of AISI 316L (40% CW), sigma, chi, Laves and M₂₃C₆ were identified and precipitated mainly along the grain boundaries as well as on the shear bands within different annealing times. It was confirmed that the increase in the annealing time caused an increase in the amounts of secondary phases. Secondary phases in the equilibrium state were calculated using Thermo-Calc software.