Exceptional magnetic properties of magnetite, Fe₃O₄, nanoparticles make them one of the most intensively studied inorganic nanomaterials for biomedical applications. We report successful gram-scale syntheses, via hydrothermal route or controlled coprecipitation in an automated reactor, of colloidal Fe₃O₄ nanoparticles with sizes of 12.9 ± 5.9, 17.9 ± 4.4, and 19.8 ± 3.2 nm. To investigate structure–property relationships as a function of the synthetic procedure, we used multiple techniques to characterize the structure, phase composition, and magnetic behavior of these nanoparticles. For the iron oxide cores of these nanoparticles, powder X-ray diffraction and electron microscopy both confirm single-phase Fe₃O₄ composition. In addition to the core composition, the magnetic performance of nanoparticles in the 13–20 nm size range can be strongly influenced by the surface properties, which we analyzed by three complementary techniques. Raman scattering and X-ray photoelectron spectroscopy (XPS) measurements indicate overoxidation of nanoparticle surfaces, while transmission electron microscopy (TEM) shows no distinct core–shell structure. Considered together, Raman, XPS, and TEM observations suggest that our nanoparticles have a gradually varying nonstoichiometric Fe₃O_4+δ composition, which could be attributed to the formation of Fe₃O₄–γ-Fe₂O₃ solid solutions at their outermost surface. Detailed analyses by TEM reveal that the hydrothermally produced samples include single-domain nanocrystals coexisting with defective twinned and dimer nanoparticles, which form as a result of oriented-attachment crystal growth. All our nanoparticles exhibit superparamagnetic-like behavior with a characteristic blocking temperature above room temperature. We attribute the estimated saturation magnetization values up to 84.01 ± 0.25 emu/g at 300 K to the relatively large size of the nanoparticles (13–20 nm) coupled with the syntheses under elevated temperature; alternative explanations, such as surface-mediated effects, are not supported by our spectroscopy or microscopy measurements. For these colloids, the heating efficiency in magnetic hyperthermia correlates with their saturation magnetization, making them appealing for therapeutic and other biomedical applications that rely on high-performance nanoparticle-mediated hyperthermia.

Carbon dots have demonstrated great potential as luminescent nanoparticles in bioapplications. Although such nanoparticles appear to exhibit low toxicity compared to other metal luminescent nanomaterials, today we know that the toxicity of carbon dots (C-dots) strongly depends on the protocol of fabrication. In this work, aqueous fluorescent C-dots have been synthesized from cinnamon, red chilli, turmeric and black pepper, by a one-pot green hydrothermal method. The synthesized C-dots were firstly characterized by means of UV–vis, fluorescence, Fourier transform infrared and Raman spectroscopy, dynamic light scattering and transmission electron microscopy. The optical performance showed an outstanding ability for imaging purposes, with quantum yields up to 43.6%. Thus, the cytotoxicity of the above mentioned spice-derived C-dots was evaluated in vitro in human glioblastoma cells (LN-229 cancer cell line) and in human kidney cells (HK-2 non-cancerous cell line). Bioimaging and viability studies were performed with different C-dot concentrations from 0.1 to 2 mg·mL⁻¹, exhibiting a higher uptake of C-dots in the cancer cultures compared to the non-cancerous cells. Results showed that the spice-derived C-dots inhibited cell viability dose-dependently after a 24 h incubation period, displaying a higher toxicity in LN-229, than in HK-2 cells. As a control, C-dots synthesized from citric acid did not show any significant toxicity in either cancerous or non-cancerous cells, implying that the tumour cell growth inhibition properties observed in the spice-derived C-dots can be attributed to the starting material employed for their fabrication. These results evidence that functional groups in the surface of the C-dots might be responsible for the selective cytotoxicity, as suggested by the presence of piperine in the surface of black pepper C-dots analysed by ESI-QTOF-MS.

Electrochemical water splitting into hydrogen and oxygen is a promising technology for sustainable energy storage. The development of earth-abundant transition metal phosphides (TMPs) to catalyze the hydrogen evolution reaction (HER) and TMP-derived oxy-hydroxides to catalyze the oxygen evolution reaction (OER) has recently drawn considerable attention. However, most monolithically integrated metal phosphide electrodes are prepared by laborious multi-step methods and their operational stability at high current densities has been rarely studied. Herein, we report a novel vapor–solid synthesis of single-crystalline cobalt phosphide nanowires (CoP NWs) on a porous Co foam and demonstrate their use in overall water splitting. The CoP NWs grown on the entire surface of the porous Co foam ligaments have a large aspect ratio, and hence are able to provide a large catalytically accessible surface over a given geometrical area. Comprehensive investigation shows that under the OER conditions CoP NWs are progressively and conformally converted to CoOOH through electrochemical in situ oxidation/dephosphorization; the latter serving as an active species to catalyze the OER. The in situ oxidized electrode shows exceptional electrocatalytic performance for the OER in 1.0 M KOH, delivering 100 mA cm⁻² at an overpotential (η) of merely 300 mV and a small Tafel slope of 78 mV dec⁻¹ as well as excellent stability at various current densities. Meanwhile, the CoP NW electrode exhibits superior catalytic activity for the HER in the same electrolyte, affording −100 mA cm⁻² at η = 244 mV and showing outstanding stability. An alkaline electrolyzer composed of two symmetrical CoP NW electrodes can deliver 10 and 100 mA cm⁻² at low cell voltages of 1.56 and 1.78 V, respectively. The CoP NW electrolyzer demonstrates exceptional long-term stability for overall water splitting, capable of working at 20 and 100 mA cm⁻² for 1000 h without obvious degradation.