Exceptional magnetic properties of magnetite, Fe₃O₄, nanoparticles make them one of the most intensively studied inorganic nanomaterials for biomedical applications. We report successful gram-scale syntheses, via hydrothermal route or controlled coprecipitation in an automated reactor, of colloidal Fe₃O₄ nanoparticles with sizes of 12.9 ± 5.9, 17.9 ± 4.4, and 19.8 ± 3.2 nm. To investigate structure–property relationships as a function of the synthetic procedure, we used multiple techniques to characterize the structure, phase composition, and magnetic behavior of these nanoparticles. For the iron oxide cores of these nanoparticles, powder X-ray diffraction and electron microscopy both confirm single-phase Fe₃O₄ composition. In addition to the core composition, the magnetic performance of nanoparticles in the 13–20 nm size range can be strongly influenced by the surface properties, which we analyzed by three complementary techniques. Raman scattering and X-ray photoelectron spectroscopy (XPS) measurements indicate overoxidation of nanoparticle surfaces, while transmission electron microscopy (TEM) shows no distinct core–shell structure. Considered together, Raman, XPS, and TEM observations suggest that our nanoparticles have a gradually varying nonstoichiometric Fe₃O_4+δ composition, which could be attributed to the formation of Fe₃O₄–γ-Fe₂O₃ solid solutions at their outermost surface. Detailed analyses by TEM reveal that the hydrothermally produced samples include single-domain nanocrystals coexisting with defective twinned and dimer nanoparticles, which form as a result of oriented-attachment crystal growth. All our nanoparticles exhibit superparamagnetic-like behavior with a characteristic blocking temperature above room temperature. We attribute the estimated saturation magnetization values up to 84.01 ± 0.25 emu/g at 300 K to the relatively large size of the nanoparticles (13–20 nm) coupled with the syntheses under elevated temperature; alternative explanations, such as surface-mediated effects, are not supported by our spectroscopy or microscopy measurements. For these colloids, the heating efficiency in magnetic hyperthermia correlates with their saturation magnetization, making them appealing for therapeutic and other biomedical applications that rely on high-performance nanoparticle-mediated hyperthermia.

In biomedicine, magnetic nanoparticles provide some attractive possibilities because they possess peculiar physical properties that permit their use in a wide range of applications. The concept of magnetic guidance basically spans from drug delivery and hyperthermia treatment of tumours, to tissue engineering, such as magneto-mechanical stimulation/activation of cell constructs and mechanosensitive ion channels, magnetic cell-seeding procedures, and controlled cell proliferation and differentiation. Accordingly, the aim of this study was to develop fully biodegradable and magnetic nanocomposite substrates for bone tissue engineering by embedding iron-doped hydroxyapatite (FeHA) nanoparticles in a poly(ε-caprolactone) (PCL) matrix. X-ray diffraction analyses enabled the demonstration that the phase composition and crystallinity of the magnetic FeHA were not affected by the process used to develop the nanocomposite substrates. The mechanical characterization performed through small punch tests has evidenced that inclusion of 10 per cent by weight of FeHA would represent an effective reinforcement. The inclusion of nanoparticles also improves the hydrophilicity of the substrates as evidenced by the lower values of water contact angle in comparison with those of neat PCL. The results from magnetic measurements confirmed the superparamagnetic character of the nanocomposite substrates, indicated by a very low coercive field, a saturation magnetization strictly proportional to the FeHA content and a strong history dependence in temperature sweeps. Regarding the biological performances, confocal laser scanning microscopy and AlamarBlue assay have provided qualitative and quantitative information on human mesenchymal stem cell adhesion and viability/proliferation, respectively, whereas the obtained ALP/DNA values have shown the ability of the nanocomposite substrates to support osteogenic differentiation.

The suitability of magnetic nanoparticles (MNPs) to act as heat nano-sources by application of an alternating magnetic field has recently been studied due to their promising applications in biomedicine. The understanding of the magnetic relaxation mechanism in biocompatible nanoparticle systems is crucial in order to optimize the magnetic properties and maximize the specific absorption rate (SAR). With this aim, the SAR of magnetic dispersions containing superparamagnetic magnetite nanoparticles bio-coated with polyacrylic acid of an average particle size of ≈10 nm has been evaluated separately by changing colloidal parameters such as the MNP concentration and the viscosity of the solvent. A remarkable decrease of the SAR values with increasing particle concentration and solvent viscosity was found. These behaviours have been discussed on the basis of the magnetic relaxation mechanisms involved. PACS: 80; 87; 87.85jf

Early diagnosis of disease and follow-up of therapy is of vital importance for appropriate patient management since it allows rapid treatment, thereby reducing mortality and improving health and quality of life with lower expenditure for health care systems. New approaches include nanomedicine-based diagnosis combined with therapy. Nanoparticles (NPs), as contrast agents for in vivo diagnosis, have the advantage of combining several imaging agents that are visible using different modalities, thereby achieving high spatial resolution, high sensitivity, high specificity, morphological, and functional information. In this work, we present the development of aluminum hydroxide nanostructures embedded with polyacrylic acid (PAA) coated iron oxide superparamagnetic nanoparticles, Fe₃O₄@Al(OH)₃, synthesized by a two-step co-precipitation and forced hydrolysis method, their physicochemical characterization and first biomedical studies as dual magnetic resonance imaging (MRI)/positron emission tomography (PET) contrast agents for cell imaging. The so-prepared NPs are size-controlled, with diameters below 250 nm, completely and homogeneously coated with an Al(OH)₃ phase over the magnetite cores, superparamagnetic with high saturation magnetization value (Ms = 63 emu/g-Fe₃O₄), and porous at the surface with a chemical affinity for fluoride ion adsorption. The suitability as MRI and PET contrast agents was tested showing high transversal relaxivity (r₂) (83.6 mM⁻¹ s⁻¹) and rapid uptake of ¹⁸F-labeled fluoride ions as a PET tracer. The loading stability with ¹⁸F-fluoride was tested in longitudinal experiments using water, buffer, and cell culture media. Even though the stability of the ¹⁸F-label varied, it remained stable under all conditions. A first in vivo experiment indicates the suitability of Fe₃O₄@Al(OH)₃ nanoparticles as a dual contrast agent for sensitive short-term (PET) and high-resolution long-term imaging (MRI).

Synthetic scaffolds for tissue engineering coupled to stem cells represent a promising approach aiming to promote the regeneration of large defects of damaged tissues or organs. Magnetic nanocomposites formed by a biodegradable poly(caprolactone) (PCL) matrix and superparamagnetic iron doped hydroxyapatite (FeHA) nanoparticles at different PCL/FeHA compositions have been successfully prototyped, layer on layer, through 3D bioplotting. Magnetic measurements, mechanical testing, and imaging were carried out to calibrate both model and technological processing in the magnetized scaffold prototyping. An amount of 10% w/w of magnetic FeHA nanoparticles represents a reinforcement for PCL matrix, however, a reduction of strain at failure is also observed. Energy loss (absorption) measurements under a radio-frequency applied magnetic field were performed in the resulting magnetic scaffolds and very promising heating properties were observed, making them very useful for potential biomedical applications.