Coatings based on Cu–Mn doped with nickel show better electrical properties, corrosion resistance and lower reactivity towards Cr₂O₃ than those doped with iron.

Cu- and Mn-based spinel coatings are currently among the most promising materials for solid oxide electrolyzer cell (SOEC) interconnects due to their high electrical conductivity and ability to eliminate environmentally hazardous cobalt, which is included in the most widely used coatings. However, their properties are affected by the presence of the Cr₂O₃ scale and high-temperature corrosion, and to mitigate this they could be doped with elements such as Ni and Fe. In addition, the electrical properties of such steel/shell layered systems can be further improved using rare-earth element nanoparticles (Ce_0.9Y_0.1O₂). In this work, low-chromium steel was modified using nanoparticles and/or spinel coatings and oxidized in air atmosphere at 800 °C for 2000 hours. The oxidized systems were then characterized using diffraction studies, microstructural observations and electrical measurements. Electrical studies in particular showed a significant reduction in area-specific resistance for steels modified using a combination of both nanoparticles and spinel coatings.