Phase-specific damage tolerance was investigated for the AlCoCrFeNi_2.1 high entropy alloy with a lamellar microstructure of L1₂ and B2 phases. A microcantilever bending technique was utilized with notches milled in each of the two phases as well as at the phase boundary. The L1₂ phase exhibited superior bending strength, strain hardening, and plastic deformation, while the B2 phase showed limited damage tolerance during bending due to micro-crack formation. The dimensionalized stiffness (DS) of the L1₂ phase cantilevers were relatively constant, indicating strain hardening followed by increase in stiffness at the later stages and, therefore, indicating plastic failure. In contrast, the B2 phase cantilevers showed a continuous drop in stiffness, indicating crack propagation. Distinct differences in micro-scale deformation mechanisms were reflected in post-compression fractography, with L1₂-phase cantilevers showing typical characteristics of ductile failure, including the activation of multiple slip planes, shear lips at the notch edge, and tearing inside the notch versus quasi-cleavage fracture with cleavage facets and a river pattern on the fracture surface for the B2-phase cantilevers.

The combination of elevated temperature and tribo-corrosion leads to the accelerated degradation of structural components used in many extreme environments. Recently developed high-entropy alloys (HEAs) with multiple principal elements have the potential for superior degradation resistance compared with presently used structural alloys. Here, we demonstrate the microstructural stability, pitting resistance, and superior tribo-corrosion degradation resistance of the AlCoCrFeNi_2.1 eutectic HEA in comparison with duplex stainless steel 2205 in deionized water (controlled low-ionic-strength electrolyte) at 25 °C, 50 °C and 100 °C. The AlCoCrFeNi_2.1 HEA showed excellent microstructural stability and tribo-corrosion resistance at all three temperatures, an order-of-magnitude lower wear rate, and a lower coefficient of friction compared with duplex 2205 steel. The lowest wear volume loss and wear rate for both AlCoCrFeNi_2.1 and duplex steel were recorded at 50 °C, which was attributed to temperature-assisted passivation and formation of a comparatively stable tribological surface condition. These results suggest superior performance of eutectic HEAs in tribo-corrosion applications compared with currently used dual-phase steels and motivate future evaluation in ion-containing industrial water chemistries.

The effects of a small addition of Ag and Ti on the thermal stability, mechanical properties, and tribological behavior of Zr-Co-Al bulk metallic glass (BMG) were investigated. A 5 at.% addition of Ag and Ti to the Zr-Co-Al base alloy improved the thermal stability and had no significant effect on the mechanical properties but considerably improved the wear behavior. The coefficient of friction decreased while the wear rate increased with increasing normal loads for all three alloys. Zr-Co-Al-Ti showed the best tribological performance among the studied alloys, with coefficient of friction and wear rate lower by a factor of four compared to Zr-Co-Al BMG. Predominantly oxidative wear was seen for the quaternary Zr-Co-Al-Ag and Zr-Co-Al-Ti BMGs at higher loads in contrast to abrasive and adhesive wear for the ternary Zr-Co-Al base alloy. These results highlight the potential of Ag and Ti micro-alloying for improving the mechanical and tribological properties of Zr-based amorphous alloys.