The silicon wafers for solar cells on which the paste is deposited experience a bowing phenomenon. The thickness of commonly used c-Si wafers is 180 μm or more. When fabricating c-Si solar cells with this wafer thickness, the bowing value is 3 mm or less and the problem does not occur. However, for the thin c-Si solar cells which are being studied recently, the output reduction due to failure during manufacture and cracking are attributed to bowing. In generally, it is known that the bowing phenomenon arises mainly from the paste applied to the back side electrode of c-Si solar cells and the effects of SiNx (silicon nitride) and the paste on the front side are not considered significant. The bowing phenomenon is caused by a difference in the coefficient of expansion between heterogeneous materials, there is the effect of bowing on the front electrode and ARC. In this paper, a partially processed c-Si solar cell was fabricated and a bowing phenomenon variation according to the wafer thicknesses was confirmed. As a result of the experiment, the measured bow value after the firing process suggests that the paste on the front-side indicates a direction different from that of the back-side paste. The bow value increases when Al paste is deposited on SiNx. The fabricated c-Si solar cell was analyzed on basis of the correlation between the bowing phenomenon of the materials and the c-Si wafer using Stoney’s equation, which is capable of analyzing the relationship between bowing and stress. As a result, the bowing phenomenon of the c-Si solar cell estimated through the experiment that the back side electrode is the important element, but also the front electrode and ARC influence the bowing phenomenon when fabricating c-Si solar cells using thin c-Si wafers.

In PV (Photovoltaic) systems, the PV array is a structure in which many PV strings are connected in parallel. The voltage mismatch between PV strings, in which PV modules are connected in a series, occurs due to a voltage decrease in some modules. In this paper, research on the electrical characteristics of PV arrays due to a voltage mismatch was conducted. Considering the voltage mismatch, experiments on partial shading, the non-uniformity of irradiance, and the failure of bypass diodes were conducted on the PV module level. It was confirmed that the open-circuit voltage greatly decreased due to the failure of bypass diodes, which is among the causes of voltage mismatch. From the simulation results at the PV array level, it can be seen that a reverse current flowed into the low-potential string, which includes PV modules, causing the failure of the bypass diodes. Measuring the reverse current at one low-potential string, it was found that, in four parallel circuits, the reverse current was 12 A. For this reason, in large PV plants, an overcurrent can flow into the fuse due to the potential difference between strings, causing an output decrease of PV plants and the burnout of fuses.

In recent years, various types of installations such as floating photovoltaic (PV) and agri-voltaic systems, and BIPV (building integrated photovoltaic system) have been implemented in PV systems and, accordingly, there is a growing demand for new PV designs and materials. In particular, in order to install a PV module in a building, it is important to reduce the weight of the module. The PV module in which low-iron, tempered glass is applied to the front surface, which is generally used, has excellent electrical output and reliability characteristics; however, it is heavy. In order to reduce the weight of the PV module, it is necessary to use a film or plastic-based material, as opposed to low-iron, tempered glass, on the front surface. However, if a material other than glass is used on the front of the PV module, various problems such as reduced electrical output and reduced reliability may occur. Therefore, in this paper, a PV module using a film instead of glass as the front surface was fabricated, and a characteristic analysis and reliability test were conducted. First, the transmittance and UV characteristics of each material were tested, and one-cell and 24-cell PV modules were fabricated and tested for electrical output and reliability. From the results, it was found that the transmittance and UV characteristics of the front material were excellent. In addition, the electrical output and reliability test results confirmed that the front-surface film was appropriate for use in a PV module.

In Korea, there is a rule for Renewable Energy Certification with weighting 5.0, to expand grid linkage capacity and to improve the stability of the grid to accommodate photovoltaic (PV) systems in a distributed power system. Due to this rule, many power companies and operators are trying to install electrical energy storage systems that are able to operate in conjunction with PV system power. These systems operate in parallel at the same grid connection point. This paper presents the results of case studies on the failure to detect islanding operation. Test evaluation devices that could be bi-directionally charged and discharged were implemented for an islanding detection test. Testing was conducted under a variety of operating conditions. When a single inverter was operated under the islanding condition, it was stably stopped within 0.5 s using the Korean grid-code standard. However, when two inverters were operated at the same time under the islanding condition, islanding detection failed and the two inverters continued to feed the connected RLC (resistor, inductor, capacitor) loads in the isolated section known as an island. Different algorithms used by PCS (power conversion system) manufacturers to detect islanding might cause this phenomenon. Therefore, it is necessary for a new PCS test standard to detect islanding.

Cut solar cells have received considerable attention recently as they can reduce electrical output degradation when the c-Si solar cells (crystalline-silicon solar cells) are shaded. Cut c-Si solar cells have a lower short-circuit current than normal solar cells and the decrease in short-circuit currents is similar to the shading effect of c-Si solar cells. However, the results of this study’s experiment show that the shadow effect of a c-Si solar cell reduces the $V_{oc}$ (open circuit voltage) in the c-Si solar cell but the $V_{oc}$ does not change when the c-Si solar cell is cut because the amount of incident light does not change. In this paper, the limitations of the electrical power analysis of the cut solar cells were identified when only photo current was considered and the analysis of the electric output of the cut c-Si solar cells was interpreted with a method different from that used in previous analyses. Electrical output was measured when the shaded and cut rates of c-Si solar cells were increased from 0% to 25, 50 and 75%, and a new theoretical model was compared with the experimental results using MATLAB.