The synthesis of new composite nanomaterials based on graphene oxide (GO)modified with cellulose and its derivatives, as well as nanocellulose, is currently an important direction and contributes toward solving many problems in various fields such as nanotechnology, information technology, medicine, high-dielectric materials, and nanoelectronics. In this work, for the first time, for the production of GO and its membrane with carboxymethylcellulose (CMC), local Kazakhstan “Ognevsky” graphite was used as the initial raw material. In this regard, the preparation of nanocomposites of GO modified with cellulose derivatives, including CMC, attracts great interest from scientists and expands its field of practical application due to the significant changes in its physicochemical properties. In this work, the GO obtained using the Hummers method was modified by CMC, and its physicochemical, structural, and electrical characteristics were studied. The GO/CMC membrane was synthesized by mixing 1% GO with crushed solid mass of CMC (0.03 g; 0.06 g; 0.15 g) and then processing using ultrasound. The surface morphology of the GO/CMC membrane was studied using scanning electron microscopy (SEM). It has been established that by increasing the mass of CMC (0.03 g; 0.06 g; 0.15 g), the polymerization of CMC occurs on the surface of GO nanosheets. Cross-sectional micrographs of GO/CMC show the formation of sandwich-like layered structures. The synthesis efficiency (yield) of GO from synthetic graphite is 10.8%, and GO from Ognevsky graphite is 11.9%, almost 1.1% more than GO from synthetic graphite. The mechanical tensile strength increases from 2.3 MPa to 14.3 MPa and the Young’s modulus from 2.3 MPa to 143 MPa. The electrical parameters of the humidity sensor based on GO and GO/CMC membranes (0.03 g; 0.06 g; 0.15 g) were studied as a function of humidity to determine the performance of the device.

In recent years, interest in the liquid-phase exfoliation (LPE) of layered crystals has been growing due to the efficiency and scalability of the method, as well as the wide range of practical applications of the obtained dispersions based on two-dimensional flakes. In this paper, we present a comparative study of as-grown and liquid-phase exfoliated GaSe_1−xS_x flakes. Bulk GaSe_1−xS_x crystals with x ~ 0, 0.25, 0.5, 0.75, 1 were synthesized by melting stoichiometric amounts of gallium, selenium, and sulfur particles in evacuated ampoules. X-ray diffraction analysis showed that the crystal structure does not change considerably after LPE, while the analysis of the Raman spectra revealed that, after liquid-phase processing in IPA, an additional peak associated with amorphous selenium is observed in selenium-rich GaSeS compounds. Nevertheless, the direct and indirect transition energies determined from the Kubelka-Munk function for LPE crystals correlate with the band gap of the as-grown bulk GaSeS crystals. This finding is also confirmed by comparison with the data on the positions of the photoluminescence peak.

As nanotechnology continues to advance, the study of nanocomposites and their unique properties is at the forefront of research. There are still various blank spots in understanding the behavior of such composite materials, especially regarding plasmonic effects like localized surface plasmon resonance (LSPR) which is essential for developing advanced nanotechnologies. In this work, we explore the structural properties of composite thin films consisting of oxide matrices and gold nanoparticles (Au NPs), which were prepared by radio-frequency magnetron sputtering. Titanium dioxide (TiO₂) and tungsten trioxide (WO₃) were chosen as the host matrices of the composites. Such composite thin films owing to the presence of Au NPs demonstrate the LSPR phenomenon in the visible region. It is shown, that spectroscopic study, in particular, Raman spectroscopy can reveal peculiar features of structures of such composite systems due to LSPR and photoluminescence (PL) of Au NPs in the visible spectrum. In particular, defect peaks of TiO₂ (700–720 cm⁻¹) or WO₃ (935 cm⁻¹) in Raman spectra can be clearly observed when the samples are illuminated with a 633 nm excitation laser. Excitation with 532 nm leads to a decrease in the intensity of the defect peak, which totally disappears at 473 nm excitation. Such dependences of the defect peaks on excitation laser wavelength are probably related to the polarization of the matrix’s defective regions close to the interface with gold NPs.

Currently, one of the topical directions in the field of production and application of graphene-like nanostructures is the use of renewable natural raw materials, which have unlimited resources for an economically efficient large-scale yield of a product with environmental safety. In this regard, we present the production of graphene oxide (GO) from a renewable natural raw material of plant biomass, birch activated carbon (BAC), and a comparison of the obtained physicochemical, mechanical, and electrical properties of birch activated carbon–graphene oxide (BAC–GO) and graphite–graphene oxide (G–GO) synthesized from the initial materials, BAC and graphite (G). Results obtained from this study confirm the successful oxidation of BAC, which correlates well with the physical–chemical dates of the G–GO and BAC–GO samples. Change in data after the oxidation of graphite and BAC was facilitated by the structure of the starting materials and, presumably, the location and content of functional oxygen-containing groups in the G–GO and BAC–GO chains. Based on the results, the application of a cost-effective, eco-friendly colloidal solution of nanodispersed BAC–GO from a plant biomass-based high-quality resource for producing large-scale nanostructured graphene is validated which has potential applicability in nanoelectronics, medicine, and other fields.

In nowadays, the synthesis of new composite nanomaterials based on graphene oxide (GO) modified with cellulose and its derivatives, as well as nanocellulose, is an important direction and contributes to solve many problems in various fields such as: nanotechnology, information technology, medicine, high-dielectric materials and nanoelectronics. In this work, for the first time, for the production of GO and its membrane with carboxymethylcellulose (CMC), local Kazakhstan “Ognevsky” graphite was used as the initial raw material. In this regard, the preparation of nanocomposites of GO modified with cellulose derivatives, including CMC, attracts great interest from scientists and expands its field of practical application due to the amazing changes of physicochemical properties. In the work, the GO obtained by the Hummers method was modified by CMC, with following study of its physicochemical, structural and electrical characteristics. The GO/CMC membrane was synthesized by mixing 1% GO with crushed solid mass of CMC (0.03 g; 0.06 g; 0.15 g) and then was processed by ultrasound. The surface morphology of the GO/CMC membrane were studied using Scanning electron microscopy (SEM). It has been established that with an increasing in the mass of CMC (0.03 g; 0.06 g; 0.15 g), polymerization of CMC occurs on the surface of GO nanosheets. Cross-sectional micrographs of GO/CMC show the formation of sandwich-like layered structures.